摘要: 用电沉积法得到的CdSe薄膜, 在450 ℃热处理后, 其光电转换效率达到5.9%。 表面光伏谱测定结果表明, 电沉积CdSe薄膜经热处理后, 其光伏效应显著提高。推算出其少子扩散长度Lp等于0.42 μm。
Abstract: CdSe semiconductor thin-film electrodes have been prepared by means of electrodeposition. They are capable of achieving 5.9% solar energy conversion efficiency in PEC performance after being annealed at 450 ℃ in air. Surface photovoltage (SPV) has been used to study their photoelectrochemical properties. SPV spectra of the CdSe thin-films with and without annealing show that surface recombination of minority carriers is significantly reduced after annealing. The minority carriers diffusion length L_P has been determined by extrapolating the plots ofreciprocal surface photovoltage as a function of the absorption length to zero ΔV~(-1)_(ph). It is found that L_p=0.42 μm.
陈子云;王子琦;周绍民. 电沉积CdSe薄膜的表面光伏研究[J]. 物理化学学报, 1987, 3(04): 407-411.
Chen Zhiyun; Wang Zhiqi; Zhou Shaomin. INVESTIGATION OF ELECTRODEPOSITED CdSe THIN-FILM BY SURFACE PHOTOVOLTAGE SPECTROSCOPY[J]. Acta Phys. -Chim. Sin., 1987, 3(04): 407-411.
0 /
导出引用管理器 EndNote (中文内容)|EndNote (英文内容)| Reference Manager|ProCite|BibTeX|RefWorks
链接本文: http://www.whxb.pku.edu.cn/CN/10.3866/PKU.WHXB19870414
http://www.whxb.pku.edu.cn/CN/Y1987/V3/I04/407
Cited