物理化学学报 >> 1996, Vol. 12 >> Issue (01): 63-66.doi: 10.3866/PKU.WHXB19960114

研究简报 上一篇    下一篇

溶胶-凝胶法制备高取向Bi4Ti3O12/SrTiO3(100)薄膜

顾豪爽,王世敏,吴新民,邝安祥,马世安,汪连山,赵建洪,李兴教   

  1. 湖北大学压电陶瓷技术研究所，武汉 430062|华中理工大学固体电子学系，武汉 430074
  • 收稿日期:1995-01-11 修回日期:1995-06-01 发布日期:1996-01-15
  • 通讯作者: 顾豪爽

Highly Oriented Bi4Ti3O12/SrTiO3(100) Thin Films Prepared by Sol-Gel Technique

Gu Hao-Shuang,Wang Shi-Min,Wu Xin-Min,Kuang An-Xiang,Ma Shi-An,Wang Lian-Shan,Zhao Jian-Hong,Li Xing-Jiao   

  1. Institute of Piezoelectric Ceramic Technology,Hubei University,Wuhan 430062|Department of Solid State Electronics,Huazhong University Science and Technology,Wuhan 430074
  • Received:1995-01-11 Revised:1995-06-01 Published:1996-01-15
  • Contact: Gu Hao-Shuang

PDF (PC)

2482

赞

关键词: Sol-Gel方法, Bi4Ti3O12高取向薄膜, SrTiO3基片

Abstract:

Highly oriented Bi4Ti3O12 thin films were prepared by Sol-Gel technique on SrTiO3(100) single crystal, using Bi(NO3)3.5H2O, Ti(OC4H9)4 and CH3COOH as raw materials. The c-axis orientation was about 96%. The effect of pH value of solution on quality of the thin films was studied.

Key words: Sol-Gel method, Bi4Ti3O12 oriented thin films, SrTiO3substrate