物理化学学报 >> 2003, Vol. 19 >> Issue (01): 82-84.doi: 10.3866/PKU.WHXB20030119

研究简报 上一篇    下一篇

新钽酸盐Ba2LnTi2Ta3O15(Ln=Y、La)的结构与介电性能

方亮;张辉;鄢俊兵;杨卫明   

  1. 武汉理工大学,材料复合新技术国家重点实验室,武汉 430070
  • 收稿日期:2002-05-27 修回日期:2002-06-17 发布日期:2003-01-15
  • 通讯作者: 方亮 E-mail:fangliang001@263.net

Structure and Dielectric Properties of New Tantalates Ba2LaTi2Ta3O15 (Ln=Y, La)

Fang Liang;Zhang Hui;Yan Jun-Bing;Yang Wei-Ming   

  1. State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology,
  • Received:2002-05-27 Revised:2002-06-17 Published:2003-01-15
  • Contact: Fang Liang E-mail:fangliang001@263.net

摘要: 通过固相反应法合成了四方钨青铜结构新钽酸盐Ba2LaTi2Ta3O15与Ba2YTi2Ta3O15,分别进行了X射线衍射分析与介电性能测试.结果表明, Ba2LaTi2Ta3O15室温时晶胞参数为a=1.242 64(5) nm, c=0.391 57(2) nm,为四方钨青铜结构顺电相;Ba2YTi2Ta3O15室温时晶胞参数为a=1.236 46(4) nm, c=0.388 60(2) nm,为四方钨青铜结构铁电相,铁电相与顺电相转变温度为180 ℃.频率为1 MHz时, Ba2LaTi2Ta3O15陶瓷的室温相对介电常数为194,介电损耗也降低至8×10-4. Ba2YTi2Ta3O15陶瓷的室温相对介电常数为107.

关键词: 钽酸盐, 钨青铜结构, X射线衍射, 介电性能

Abstract: New tantalates Ba2LnTi2Ta3O15 (Ln=Y, La) were synthesized by Ln partial substitution for Ba in the crystal structure of Ba3TiTa4O15.The crystal structure and dielectric properties were determined by X-ray powder diffraction and dielectric measurements. The results show that Ba2YTi2Ta3O15 belongs to ferroelectric phase of tetragonal tungsten bronze structure at room temperature with unit cell parameters: a=1.236 46(4) nm, c=0.388 60(2) nm. The phase transition of Ba2YTi2Ta3O15 from ferroelectric to paraelectric occurred at 180 ℃. Ba2LaTi2Ta3O15 belongs to paraelectric phase of tetragonal tungsten bronze structure at room temperature with unit cell parameters: a=1.242 64(5) nm, c=0.391 57(2) nm. At room temperature, the dielectric constant (εr) of Ba2YTi2Ta3O15 approached 107, while Ba2LaTi2Ta3O15 ceramic approached 194,combined with a low dielectric loss of 8×10-4 at 1 MHz. Ba2LaTi2Ta3O15 might be a suitable candidate of high εr microwave dielectric ceramics.

Key words: Tantalate, Tungsten bronze structure, XRD, Dielectric property