大面积全柔性染料敏化太阳能电池光电性能优化

doi:10.3866/PKU.WHXB20111112

物理化学学报 >> 2011, Vol. 27 >> Issue (11): 2577-2582.doi: 10.3866/PKU.WHXB20111112

大面积全柔性染料敏化太阳能电池光电性能优化

林逍, 武明星, 安江, 苗青青, 覃达, 马廷丽

大连理工大学化工学院精细化工国家重点实验室, 辽宁大连 116024

收稿日期:2011-07-04 修回日期:2011-08-26 发布日期:2011-10-27
通讯作者: 马廷丽 E-mail:tinglima@dlut.edu.cn
基金资助:
国家自然科学基金(50773008)及国家高技术研究发展计划(863) (2009AA03Z220)资助项目

Optimization of the Photoelectric Performance of Large-Scale All-Flexible Dye-Sensitized Solar Cells

LIN Xiao, WU Ming-Xing, AN Jiang, MIAO Qing-Qing, QIN Da, MA Ting-Li

State Key Laboratory of Fine Chemicals, School of Chemical Engineering, Dalian University of Technology, Dalian 116024, Liaoning Province, P. R. China

Received:2011-07-04 Revised:2011-08-26 Published:2011-10-27
Contact: MA Ting-Li E-mail:tinglima@dlut.edu.cn
Supported by:
The project was supported by the National Natural Science Foundation of China (50773008) and National High Technology Research and Development Program of China (863) (2009AA03Z220).

摘要/Abstract

摘要： 设计并制作了大面积高效全柔性染料敏化太阳能电池(DSCs). 通过引入光散射层或施加机械压力,DSCs 的光电转化效率有了大幅度提高. 实验室小面积(0.4 cm×0.4 cm)柔性DSCs 的光电转化效率达到5.50%. 大面积(2 cm×3 cm, 活性面积为2.7 cm²) DSCs的光电转化效率从未进行处理的1.52%上升到1.81%和2.50%, 分别提高了20.0%和66.7%. 5 cm×7 cm面积的DSCs (活性面积为16.2 cm²)的光电转化效率在未做任何优化处理的条件下达到了1.60% (光强40 mW·cm^-2). 同时, 本文对提高光电转化效率的机理进行了深入研究. 电化学阻抗测试结果表明, 加压法能明显减小电池的内部串联电阻(R_s)及TiO₂/染料/电解液界面间的传荷电阻(R_ct). 扫描电镜结果也显示加压后TiO₂粒子之间粘结更加紧密, 更利于电子在TiO₂薄膜中的传输及染料的吸附. 另外, 900 h 的长期稳定性实验结果表明, 制作的柔性DSCs的各项光电性能参数均无明显下降. 该实验结果为柔性染料敏化太阳能电池的基础研究和大面积产业化技术研究奠定了基础.

关键词: 全柔性, 太阳能电池, 散射层, 加压法, 稳定性

Abstract: Highly efficient large scale flexible dye-sensitized solar cells (DSCs) were successfully designed and fabricated. By the introduction of a light scattering layer or pressure, the DSC efficiency was greatly improved. The flexible DSCs with a small surface area (0.4 cm × 0.4 cm) gave a high energy conversion efficiency of 5.50%. The energy conversion efficiencies of large area DSCs (2 cm×3 cm, active area of 2.7 cm²) improved from 1.52% to 1.81% and 2.50%, which is an increase of 20.0% and 66.7% compared with the DSCs prepared without any treatment. The 5 cm×7 cm DSCs (active area of 16.2 cm²) without any optimization showed an energy conversion efficiency of 1.60% under a sunlight intensity of 40 mW·cm^-2. The mechanism for the improvement in efficiency was also studied. The results of electrochemical impedance spectroscopy (EIS) demonstrated that the pressure method can significantly reduce the series resistance (R_s) and the charge transfer resistance (R_ct) in the TiO₂/dye/electrolyte interface. Scanning electron microscopy (SEM) showed that the TiO₂ particles were far more closely connected after pressing, which was helpful for electron transport in the TiO₂ network as well as for dye adsorption. In addition, the photovoltaic parameters of these flexible DSCs were found to be stable after the 900 h stability tests. The experimental results obtained for these flexible DSCs can be used as a foundation for further basic research and for industrialization technical research.

Key words: All-flexibility, Solar cell, Scattering layer, Pressure method, Stability

MSC2000:

O644

林逍, 武明星, 安江, 苗青青, 覃达, 马廷丽. 大面积全柔性染料敏化太阳能电池光电性能优化[J]. 物理化学学报, 2011, 27(11): 2577-2582.

LIN Xiao, WU Ming-Xing, AN Jiang, MIAO Qing-Qing, QIN Da, MA Ting-Li. Optimization of the Photoelectric Performance of Large-Scale All-Flexible Dye-Sensitized Solar Cells[J]. Acta Phys. -Chim. Sin., 2011, 27(11): 2577-2582.

参考文献

(1) O'Regan, B.; Grätzel, M. Nature 1991, 353, 737.

(2) Grätzel, M. Nature 2001, 414, 338.

(3) Tao, L.; Yang, Y. Z.; Shi, C.W.;Wu, Y. C.;Wu, X. Y. Acta Phys. -Chim. Sin. 2010, 26, 578. [桃李, 杨燕珍, 史成武, 吴玉程, 吴小燕. 物理化学学报, 2010, 26, 578.]
(4) Li, B.; Cheng, P.; Deng, C. S. Chin. J. Chem. 2007, 20, 816.

(5) Hagfeldt, A.; Boschloo, G.; Sun, L. C.; Kloo, L.; Pettersson, H. Chem. Rev. 2010, 110, 6595.

(6) Pichot, F.; Pitts, J. R.; Gregg, B. A. Langmuir 2000, 16, 5626.

(7) Chen, D. H.; Huang, F. Z.; Cheng, Y. B.; Caruso, R. A. Adv. Mater. 2009, 21, 2206.

(8) Wang, Y.;Wu, J. H.; Fan, L. Q.; Lan, Z.; Xiao, Y. M.; Li, Q. H.; Huang, M. L. Mater. Rev. 2010, 24, 131. [王岳, 吴季怀, 范乐庆, 兰章, 肖尧明, 李清华, 黄妙良. 材料导报, 2010, 24, 131.]
(9) Wang, M. K.; Anghel, A. M.; Marsan, B.; Ha, N. C.; Pootrakulchote, N.; Zakeeruddin, S. M.; Grätzel, M. J. Am. Chem. Soc. 2009, 131, 15976.

(10) Yang, L.; Xin, G.;Wu, L. Q.; Ma, T. L. Prog. Chem. 2009, 21, 2242. [杨丽, 辛刚, 吴丽琼, 马廷丽. 化学进展, 2009, 21, 2242.]
(11) Iwasaki, M.; Lee, C.W.; Kim, T. H.; Park,W. K. J. Ceram. Soc. Jpn. 2008, 116, 153.

(12) Lindström, H.; Holmberg, A.; Magnusson, E.; Lindquist, S. E.; Malmqvist, L.; Hagfeldt, A. Nano Lett. 2001, 1, 97.

(13) Lin, H.; Li, X.; Liu, Y. Z.; Li, J. B. Mater. Sci. Eng. B 2009, 161, 2.

(14) Ma, T. L.; Fang, X. M.; Akiyama, M.; Inoue, K.; Nomam, H.; Abe, E. J. Electroanal. Chem. 2004, 574, 77.

(15) Yang, L.;Wu, L. Q.;Wu, M. X.; Xin, G.; Lin, H.; Ma, T. L. Electrochem. Commun. 2010, 12, 1000.

(16) Papageorgiou, N.; Maier,W. F.; Grätzel, M. J. Electrochem. Soc. 1997, 144, 876.

(17) Han, L.; Koide, N.; Chiba, Y.; Islam, A.; Komiya, R.; Fuke, N.; Fukui, A.; Yamanaka, R. Appl. Phys. Lett. 2005, 86, 21350.
(18) Usami, A. Sol. Energy Mater. Sol. Cells 2000, 64, 73.

(19) Huang, F. Z.; Chen, D. H.; Zhang, X. L.; Caruso, R. A.; Cheng, Y. B. Adv. Funct. Mater. 2010, 20, 1301.

(20) Liu, J.; Yang, H. T.; Zhang, J. B.; Zhou, X.W.; Lin Y. Acta Phys. -Chim. Sin. 2011, 27, 408. [刘佳, 杨浩田, 张敬波, 周晓文, 林原. 物理化学学报, 2011, 27, 408.]
(21) Koide, N.; Islam, A.; Chiba, Y.; Han, L. Y. J. Photochem. Photobiol. A: Chem. 2006, 182, 296.

(22) Kern, R.; Sastrawan, R.; Ferber, J.; Stangl, R.; Luther, J. Electrochim. Acta 2002, 47, 4213.

(23) Wang, Q.; Moser, J. E.; Grätzel, M. J. Phys. Chem. B 2005, 109, 14945.

(24) Green, A. N. M.; Palomares, E.; Haque, S. A.; Kroon, J. M.; Durrant, J. R. J. Phys. Chem. B 2005, 109, 12525.

(25) Ikegami, M.; Suzuki, J.; Teshima, K.; Kawaraya, M.; Miyasaka, T. Sol. Energy Mater. Sol. Cells 2009, 93, 836.

(26) Trupke, T.;Würfel, P.; Uhlendorf, I. J. Phys. Chem. B 2000, 104, 11484.

[1]	连孟水,王雅莉,赵明全,李倩倩,翁维正,夏文生,万惠霖. Ni/SiO₂在甲烷部分氧化反应中的稳定性：W修饰的影响[J]. 物理化学学报, 2019, 35(6): 607-615.
[2]	张美琪, 马云龙, 郑庆东. 含萘并二噻吩小分子受体材料的带隙调控及其在非富勒烯太阳能电池中的应用[J]. 物理化学学报, 2019, 35(5): 503-508.
[3]	邓祎华, 彭爱东, 吴筱曦, 陈华杰, 黄辉. 有机太阳能电池中基于苝二酰亚胺结构小分子受体进展[J]. 物理化学学报, 2019, 35(5): 461-471.
[4]	章中强, 张书华, 刘志玺, 张志国, 李永舫, 李昌治, 陈红征. 骨架非稠合的电子受体在聚合物太阳能电池中的应用[J]. 物理化学学报, 2019, 35(4): 394-400.
[5]	冯诗语, 路皓, 刘泽坤, 刘亚辉, 李翠红, 薄志山. 通过非共价构象锁定和端基工程策略设计高效率的A-D-A型稠环电子受体[J]. 物理化学学报, 2019, 35(4): 355-360.
[6]	陈瑞,王维,卜童乐,库治良,钟杰,彭勇,肖生强,尤为,黄福志,程一兵,傅正义. 低成本富勒烯衍生物电子传输层在钙钛矿太阳能电池的应用[J]. 物理化学学报, 2019, 35(4): 401-407.
[7]	雷群,张玉荣,罗健辉,韩荣成,耿向飞,吕晓东,刘岩,王远. 高浓度乳液稳定性评价方法及其应用[J]. 物理化学学报, 2019, 35(4): 415-421.
[8]	刘方彬,刘俊,王利祥. 带有噻吩侧基的有机硼小分子电子受体光伏材料[J]. 物理化学学报, 2019, 35(3): 251-256.
[9]	杨阳,蒋秀,占肖卫,陈兴国. 以绕丹宁和噻唑烷-2, 4-二酮为端基的不对称结构有机受体分子的设计合成与构性关系探讨[J]. 物理化学学报, 2019, 35(3): 257-267.
[10]	许青青,常春梅,李万宾,郭冰,国霞,张茂杰. 基于一种新型聚噻吩衍生物为给体的非富勒烯聚合物太阳能电池[J]. 物理化学学报, 2019, 35(3): 268-274.
[11]	薛佩瑶,张俊祥,辛景明,RECHJeromy,李腾飞,孟凯鑫,王嘉宇,马伟,尤为,MARDER Seth R.,韩平畴,占肖卫. 第三组份端基对有机太阳能电池性能的影响[J]. 物理化学学报, 2019, 35(3): 275-283.
[12]	贾国骁,张少青,杨丽燕,何畅,范慧俐,侯剑辉. A-D-A型小分子电子给体光伏材料的端基修饰及其光伏性能[J]. 物理化学学报, 2019, 35(1): 76-83.
[13]	陈文君,薛智敏,王晋芳,蒋静云,赵新辉,牟天成. 低共熔溶剂的热稳定性研究[J]. 物理化学学报, 2018, 34(8): 904-911.
[14]	周士超,冯贵涛,夏冬冬,李诚,武永刚,李韦伟. 萘酰亚胺-卟啉星型电子受体分子的构筑及其在非富勒烯太阳能电池中的应用[J]. 物理化学学报, 2018, 34(4): 344-347.
[15]	韩杰,梁秋菊,曲轶,刘剑刚,韩艳春. 基于苝二酰亚胺类非富勒烯受体共混体系凝聚态结构调控[J]. 物理化学学报, 2018, 34(4): 391-406.

大面积全柔性染料敏化太阳能电池光电性能优化

Optimization of the Photoelectric Performance of Large-Scale All-Flexible Dye-Sensitized Solar Cells

PDF (PC)

赞

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

Metrics

本文评价

推荐阅读 10