Probing the Controlled Oxidative Etching of Palladium Nanorods by Liquid Cell Transmission Electron Microscopy

Ganxing DONG,Chuanhong JIN*()   

  • Received:2017-10-30 Published:2018-06-13
  • Contact: Chuanhong JIN E-mail:chhjin@zju.edu.cn
  • Supported by:
    the National Natural Science Foundation of China(51772265);the National Natural Science Foundation of China(61721005)

摘要:

借助原位液体透射电镜,我们观察并研究了钯纳米棒溶液环境下的氧化刻蚀的微观行为及机理。通过改变钯纳米棒所处的液体环境,有效地控制了钯纳米棒的氧化刻蚀行为。由于端部具有较高的反应活性,钯纳米棒在氯化铁溶液中的氧化刻蚀会选择沿着轴向进行,具有明显的各向异性。当反应在超薄液层进行时,钯纳米棒的氧化刻蚀会变为准各向同性。这种行为是由于超薄溶液中溶解产物以及氧化物的扩散被抑制,在纳米棒端部选择性发生的氧化刻蚀会受到阻碍。最后,我们发现在钯纳米棒端部选择性沉积金,可以保护纳米棒的端部不受氧化,从而能控制刻蚀沿着钯纳米棒的径向进行。本文的研究结果对贵金属纳米晶的结构参数的精确调控以利于实际应用具有重要的意义。

关键词: 钯纳米棒, 氧化刻蚀, 原位液体电镜, 各向异性, 扩散抑制, 端部保护

Abstract:

Herein, we report an in situ study of a microscopic process of oxidative etching of palladium nanorods using liquid cell transmission electron microscopy. Oxidative etching is a universal corrosion phenomenon in the natural environment, and has become an effective tool in the fields of materials and nano-science to precisely tailor product sizes. For some noble metal nanocrystals with shape and chemical anisotropy, oxidative etching selectively occurs on specific sites or facets of the nanoparticles and could change the anisotropy. To study the behavior of anisotropic noble metal nanocrystals, it is easier to directly observe the dynamic etching of nanocrystals in solution. Liquid cell electron microscopy is a rapidly developing and powerful technique, and it allows the study of dynamic events occurring in the liquid phase with sub-nanometer resolution and can be used to track the dynamics of reactions in real-time. By recording the changes in morphology and quantitatively analyzing variations in dimensions could allow us to clarify the mechanism involved in the oxidative etching of palladium nanorods. By changing the solution properties, the oxidative etching behaviors of the palladium nanorods could be effectively controlled. Because of the higher chemical reactivity of the apex of the palladium nanorods, oxidative etching preferentially proceeded along the longitudinal direction, showing strong anisotropic behavior. The decrease in the length of the nanorods was more rapid than the decrease in their diameter, and the aspect ratio decreased continuously throughout the etching process. An isotropic-like etching was observed when the reaction was performed in an ultrathin solution, where the diffusion of reactants and dissolved agents were inhibited due to the confinement effect. In this case, the palladium nanorods kept their rod shape and aspect ratio before being completely dissolved during the etching process. Furthermore, we demonstrate that the tip-deposition of gold can effectively protect the tips of the palladium nanorods from oxidative etching. Contrary to the previous experiment without gold deposition, oxidative etching selectively took place on the lateral sides. The palladium nanorods became progressively thinner and the aspect ratio continuously increased during the etching process. Previous studies on the oxidative etching of nanocrystals by liquid cell electron microscopy focused on the dissolution kinetics of metal nanocrystals with symmetrical structure. The results presented here show successful in situ monitoring of the controlled oxidative etching process of anisotropic noble metal nanocrystals. The presented results should be important for the precise structural tuning of noble metal nanocrystals for various practical applications.

Key words: Palladium nanorod, Oxidative etching, In situ liquid cell electron microscopy, Anisotropy, Limited-diffusion, Tip protection