物理化学学报 >> 1997, Vol. 13 >> Issue (05): 407-412.doi: 10.3866/PKU.WHXB19970505

研究论文 上一篇    下一篇

PMMA-ZrO2等有机无机杂化材料的制备与表征

蒋葵阳,张隽,桂琳琳   

  1. 北京大学物理化学研究所，北京 100871
  • 收稿日期:1996-09-03 修回日期:1996-11-11 发布日期:1997-05-15
  • 通讯作者: 桂琳琳

Synthesis and Characterization of PMMA-ZrO2(SiO2,TiO2,Al2O3) Organic-Inorganic Hybrid Materials

Jiang Kui-Yang,Zhang Jun,Gui Lin-Lin   

  1. Institute of Physical Chemistry,Peking University,Beijing 100871
  • Received:1996-09-03 Revised:1996-11-11 Published:1997-05-15
  • Contact: Gui Lin-Lin

PDF (PC)

2612

赞

摘要：

以烯丙基乙酸丙酮作为偶联剂应用溶胶凝胶法制备了一系列均匀透明的PMMA－ZrO2等有机无机杂化材料. 利用UV，IR对其制备过程进行了研究. 并测定了所得杂化玻璃的TGA性质.

关键词: 有机无机杂化材料, 甲基丙烯酸甲酯, 醇盐前体, 烯丙基乙酰丙酮, 溶胶凝胶方法

Abstract:

Poly(methyl methacrylate)-ZrO2(SiO2, TiO2, Al2O3) hybrid glasses have been synthesized through Sol-Gel process by using allyl acetylacetone as coupling agent. Alkoxide precursor modified with allyl acetylacetone was hydrolyzed to produce an inorganic network, and then poly(methacrylate) (PMMA) chains formed in situ through a radical polymerization were chemically bound to the forming inorganic network to synthesize a hybrid glass. Several transparent hybrid glasses have been obtained. The synthesis process was investigated by FTIR and UV spectroscopies, and the results demonstrated that acetylacetonate groups were bound to titanium(aluminium, zirconium) in the process of preparation and the final hybrid glasses, but they didn't to silicon. The results of TGA showed that the thermal stabilities of these hybrid materials were considerably improved compared with pure PMMA. Among them, the hybrid glass containing zirconia had the best thermal stability.

Key words: Organic-inorganic hybrid materials, Poly(methyl methacrylate)(PMMA), Alkoxide precursor, Allylacetylacetone(AAA), Sol-gel method