Thin Film Light-emitting Diodes with Organic/Inorganic Heterostructure

Tan Hai-Shu,Chen Li-Chun,Yang Xiao-Hui,Wang Xiang-Jun,Xie Hong-Quan,Gao Guang-Hua,Yao Jian-Quan   

  1. College of Precision Instrument and Opto-electronics Engineering,Tianjin University,Tianjin 300072|Institute of Material Physics,Tianjin Institute of Technology,Tianjin 300191|Department of Chemistry,Huazhong University of Science Technology,Wuhan 430074
  • Received:1997-01-06 Revised:1997-04-18 Published:1997-10-15
  • Contact: Tan Hai-Shu

关键词: ZnO:Zn, 有机/无机异质, 聚合物, 薄膜, 发光二极管

Abstract:

Thin film light-emitting diodes with organic/inorganic heterostructure in which ZnO:Zn layer was used as electron transporting and hole blocking layer, PDDOPV, Poly(2,5- Didodecyloxy-1,4 Phenylenevinylene ) was used as hole transport and emission layer have been successfully prepared. Comparing to single layer device, the luminescent efficiency of bilayer device is improved about twenty-six times, the emission spectrum's peak wavelength shifts to short wavelength, the half width at full maximum (HWFM) widens. The improvement of luminescent efficiency is due to the insertion of ZnO:Zn layer.

Key words: ZnO:Zn, Organic/inorganic heterostructure, Polymer, Thin film, Light-emitting diode