多钨酸盐修饰ZrO2气凝胶催化四氢呋喃开环聚合

doi:10.3866/PKU.WHXB20110212

物理化学学报 >> 2011, Vol. 27 >> Issue (02): 491-498.doi: 10.3866/PKU.WHXB20110212

多钨酸盐修饰ZrO₂气凝胶催化四氢呋喃开环聚合

朱晴¹, 梁丽萍^1,2, 贾志奇¹, 高春光¹, 赵永祥¹

1. 山西大学化学化工学院, 精细化学品教育部工程研究中心, 太原 030006;
2. 太原科技大学材料科学与工程学院, 太原 030024

收稿日期:2010-08-10 修回日期:2010-11-23 发布日期:2011-01-25
通讯作者: 梁丽萍, 赵永祥 E-mail:yxzhao@sxu.edu.cn, liangliping@sxu.edu.cn
基金资助:
山西省科技攻关计划项目(20090321059)和山西省发改委产业技术开发项目(2009164)资助

Polyoxotungstate-Modified Zirconia Aerogel as a Solid Catalyst for Tetrahydrofuran Polymerization

ZHU Qing¹, LIANG Li-Ping^1,2, JIA Zhi-Qi¹, GAO Chun-Guang¹, ZHAO Yong-Xiang¹

1. School of Chemistry and Chemical Engineering, Engineering Research Center for Fine Chemicals of Ministry of Education, Shanxi University, Taiyuan 030006, P. R. China;
2. School of Materials Science and Engineering, Taiyuan University of Science and Technology, Taiyuan 030024, P. R. China

Received:2010-08-10 Revised:2010-11-23 Published:2011-01-25
Contact: LIANG Li-Ping, ZHAO Yong-Xiang E-mail:yxzhao@sxu.edu.cn, liangliping@sxu.edu.cn
Supported by:
The project was supported by the Scientific and Technological Project of Shanxi Province, China (20090321059) and Industrial Technology Development Project of Development and Reform Commission of Shanxi Province, China (2009164).

摘要/Abstract

摘要：

采用过量浸渍结合溶剂蒸发将磷钨杂多酸(TPA)分散于ZrO₂气凝胶表面(TPA的质量分数为5%-45%), 再经750 °C空气气氛焙烧得到多钨酸盐修饰ZrO₂固体酸催化剂. 借助N₂吸附、X射线衍射(XRD)、傅里叶变换红外(FTIR)光谱、氨程序升温脱附(NH₃-TPD)和吡啶吸附红外(Py-IR)光谱对催化剂的结构及酸性质进行表征, 针对四氢呋喃(THF)开环聚合反应考察其酸催化性能. 研究发现, TPA与ZrO₂之间较强的相互作用抑制了ZrO₂的晶化, 同时也在一定程度上稳定了TPA的Keggin(凯金)-阴离子结构. 高温焙烧的催化剂中, 活性组分以ZrO₂锚定的表面相(包括含有畸变或缺陷型Keggin单元的杂多酸盐及以Zr为杂原子的类杂多酸物种等)和TPA完全分解形成的氧化物体相存在, 各物种的相对量取决于TPA的负载量. 催化剂表面同时具有中等强度的布朗斯特德(Brönsted)酸与路易斯(Lewis)酸中心, 且初始TPA负载量为20%的催化剂实现了活性组分在载体表面的单层覆盖, 因而显示最大的总酸量, 对THF聚合反应也表现出最高的催化活性. 在反应温度为40 °C、时间为20 h条件下, 聚合物收率达30.9%±2%, 数均相对分子质量为2698±100; 在催化剂重复使用6次过程中, 活性未见明显降低.

关键词: 二氧化锆气凝胶, 磷钨杂多酸, 多钨酸盐, 四氢呋喃, 聚合

Abstract:

Catalysts with different loadings (mass fractions from 5% to 45%) of tungstophosphoric acid (TPA) on zirconia were prepared by suspending zirconia aerogel in an ethanol solution of TPA, removing the solvent via evaporation, drying and then calcining the powder at 750 °C. These catalysts were characterized by N₂ adsorption, X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy, FTIR spectroscopy of adsorbed Pyridine (Py-IR), and temperature programmed desorption of NH₃ (NH₃-TPD). The catalytic performances of these materials were examined for the polymerization of tetrahydrofuran (THF). The experimental results indicated that the strong interaction between TPA and zirconia retarded both the crystallization of zirconia and the destruction of the Keggin-unit of TPA. In these materials, the major tungsten species were found to be zirconia-anchored heteropolytungstates (with distorted intact and/or partially fragmented Keggin-units) and Zr-containing pseudo-heteropolyanions produced by the chemical bonding of Zr⁴⁺ with the WO_x fragments from TPA decomposition as well as some amount of WO₃. The catalysts showed both Brönsted and Lewis acidity, and the catalyst with 20% TPA loading had the highest total acidity and catalytic activity because of the monolayer coverage of the active species. Under the reaction conditions of 40 °C for 20 h, the most active catalyst, 20TPZ-750, gave a high polymer yield of 30.9%±2%. During recycling for 6 times, no obvious activity loss was observed.

Key words: Zirconia aerogel, Tungstophosphoric acid, Polyoxotungstate, Tetrahydrofuran, Polymerization

MSC2000:

O643.3

朱晴, 梁丽萍, 贾志奇, 高春光, 赵永祥. 多钨酸盐修饰ZrO₂气凝胶催化四氢呋喃开环聚合[J]. 物理化学学报, 2011, 27(02): 491-498.

ZHU Qing, LIANG Li-Ping, JIA Zhi-Qi, GAO Chun-Guang, ZHAO Yong-Xiang. Polyoxotungstate-Modified Zirconia Aerogel as a Solid Catalyst for Tetrahydrofuran Polymerization[J]. Acta Phys. -Chim. Sin., 2011, 27(02): 491-498.

参考文献

(1) Setoyama, T.; Kobayashi, M.; Kabata, Y.; Kawai, T.; Nakanishi, A. Catal. Today 2002, 73, 29.
(2) Okuhara, T.; Mizuno, N.; Misono, M. Appl. Catal. A: Gen. 2001, 222, 63.
(3) Rafiee, E.; Joshaghani, M.; Tork, F.; Fakhri, A.; Eavani, S. J. Mol. Catal. A: Chem. 2008, 283, 1.
(4) Bhatt, N.; Patel, A. J. Mol. Catal. A: Chem. 2007, 264, 214.
(5) Bhatt, N.; Sharma, P.; Patel, A.; Selvam, P. Catal. Commun. 2008, 9, 1545.
(6) Sharma, P.; Patel, A. Appl. Surf. Sci. 2009, 255, 7635.
(7) Mallick, S.; Parida, K. M. Catal. Commun. 2007, 8, 889.
(8) Parida, K. M.; Mallick, S. J. Mol. Catal. A: Chem. 2007, 275, 7.
(9) Parida, K. M.; Mallick, S.; Pradhan, G. C. J. Mol. Catal. A: Chem. 2009, 297, 93.
(10) Rajkumar, T.; Rao, G. R. J. Mol. Catal. A: Chem. 2008, 295, 1.
(11) Oliveira, C. F.; Dezaneti, L. M.; Garcia, F. A. C.; de Macedo, J. L.; Dias, J. A.; Dias, S. C. L.; Alvim, Kayne S. P. Appl. Catal. A: Gen. 2010, 372, 153.
(12) Devassy, B. M.; Lefebvre, F.; Halligudi, S. B. J. Catal. 2005, 31, 1.
(13) Devassy, B. M.; Halligudi, S. B. J. Catal. 2005, 236, 313.
(14) Devassy, B. M.; Halligudi, S. B. J. Mol. Catal. A: Chem. 2006, 253, 8.
(15) Sunita, G.; Devassy, B. M.; Vinu, A.; Sawant, D. P.; alasubramanian, V. V.; Halligudi, S. B. Catal. Commun. 2008, 9, 696.
(16) Lucas, N.; Bordoloi, A.; Amrute, A. P.; Kasinathan, P.; Vinu, A.; ohringer,W.; Fletcher, J. C. Q.; Halligudi, S. B. Appl. Catal. A: Gen. 2009, 352, 74.
(17) Sawant, D. P.; Vinu, A.; Lefebvre, F.; Halligudi, S. B. J. Mol. Catal. A: Chem. 2007, 262, 98.
(18) Sawant, D. P.; Vinu, A.; Mirajkar, S. P.; Lefebvre, F.; Ariga, K.; Anandan, S.; Mori, T.; Nishimura, C.; Halligudi, S. B. J. Mol. atal. A: Chem. 2007, 271, 46.
(19) Sawant, D. P.; Hartmann, M.; Halligudi, S. B. Microporous Mesoporous Mat. 2007, 102, 223.
(20) Satam, . R.; Parghi, K. D.; Jayaram, R. V. Catal. Commun. 2008, 9, 1071.
(21) Chai, S. H.;Wang, H. P.; Liang, Y.; Xu, B. Q. Appl. Catal. A: Gen., 2009, 353, 213.
(22) Liang, L. P.; Dang, S.;Wu, D.; Sun, Y. H. J. Mater. Sci. Technol. 2004, 20, 435.
(23) Zhao, M.; Jia, Z. Q.; Zhao, L. L.; Sun, Z. J.; Liu, X.W.;Wang, P. F.; Gao, C. G. J. Mol. Catal. (China) 2010, 24, 117.
[赵敏, 志奇, 赵丽丽, 孙自瑾, 刘新文, 王鹏飞, 高春光, 赵永祥. 分子催化, 2010, 24, 117.]
(24) Damyanova, S.; Fierro, J. L. G.; Sobrados, I.; Sanz, J. Langmuir 1999, 15, 469.
(25) López-Salinas, E.; Hernández-Cortéz, J. G.; Schifter, I.; Torres- arcía, E.; Navarrete, J.; Gutiérrez-Carrillo, A.; López, T.; ottici, P. P.; Bersani, D. Appl. Catal. A: Gen. 2000, 193, 215.
(26) Vu, T. N.; Van Gestel, J.; Gilson, J. P.; Collet, C.; Dath, J. P.; uchet, J. C. J. Catal. 2005, 231, 453.
(27) Martínez, A.; Prieto, G.; Arribas, M. A.; Concepción, P.; ánchez-Royo, J. F. J. Catal. 2007, 248, 288.
(28) Lebarbier, V.; Clet, G.; Houalla, M. J. Phys. Chem. B 2006, 110, 3905.
(29) Chen, S. C.; Lin, F. S.; Chou, J. Y.; Hsu, L. A.; Chu, M. H.; Huang, C. C.; Shao, M. H. Method for preparing polyether olyol and copolymer thereof. US Patent 6313262, 2001-11-06.
(30) Liao, X. M.; Chu,W.; Li, Y.; Zhou, F. D.; Luo, S. Z. Chinese hem. Lett. 2009, 20, 344.
(31) Huang, M.; Chu,W.; Liao, X. M.; Dai, X. Y. Chinese Sci. Bull. 2010, 55, 2652.

[1]	王义洲,刘晔宏,徐首红,刘洪来. 用于药物载体的多重响应型聚合物分子的设计与合成[J]. 物理化学学报, 2019, 35(8): 876 -884 .
[2]	GUPTA Monika,闫东,沈福刚,徐建中,詹传郎. 苝二酰亚胺:有机膦盐基双组份共混电子传输层及其开路电压接近1.0 V的非富勒烯聚合物太阳电池[J]. 物理化学学报, 2019, 35(5): 496 -502 .
[3]	冯诗语, 路皓, 刘泽坤, 刘亚辉, 李翠红, 薄志山. 通过非共价构象锁定和端基工程策略设计高效率的A-D-A型稠环电子受体[J]. 物理化学学报, 2019, 35(4): 355 -360 .
[4]	吕康杰,彭燕秋,肖丽,陆君涛,庄林. 醇/水混合溶剂中碱性聚合物电解质独特的溶解行为[J]. 物理化学学报, 2019, 35(4): 378 -384 .
[5]	章中强, 张书华, 刘志玺, 张志国, 李永舫, 李昌治, 陈红征. 骨架非稠合的电子受体在聚合物太阳能电池中的应用[J]. 物理化学学报, 2019, 35(4): 394 -400 .
[6]	刘恒昌,冯玉军. CO₂诱导的五嵌段非离子共聚物与阴离子氟碳表面活性剂的相互作用[J]. 物理化学学报, 2019, 35(4): 408 -414 .
[7]	许青青,常春梅,李万宾,郭冰,国霞,张茂杰. 基于一种新型聚噻吩衍生物为给体的非富勒烯聚合物太阳能电池[J]. 物理化学学报, 2019, 35(3): 268 -274 .
[8]	何妍,李豪,周莉,徐婷,彭昌军,刘洪来. 新型芳香三嗪超交联多孔聚合物去除水溶液中甲基橙[J]. 物理化学学报, 2019, 35(3): 299 -306 .
[9]	吴仪, 孔静宜, 秦云朋, 姚惠峰, 张少青, 侯剑辉. 通过调节共轭聚合物侧链实现可绿色溶剂加工的非富勒烯太阳能电池[J]. 物理化学学报, 2019, 35(12): 1391 -1398 .
[10]	薛智敏,严传玉,赵新辉,于东琨,牟天成. Hofmeister离子对水溶液中热响应聚合物的局域环境的影响[J]. 物理化学学报, 2019, 35(1): 49 -57 .
[11]	周劲媛,张锦,刘忠范. 石墨双炔的合成方法[J]. 物理化学学报, 2018, 34(9): 977 -991 .
[12]	韩雪,杨进,刘莹莹,马建方. 三氮唑取代杯[4]芳烃配位聚合物的合成与荧光性能[J]. 物理化学学报, 2018, 34(5): 476 -482 .
[13]	马强,胡勇胜,李泓,陈立泉,黄学杰,周志彬. 双(三氟甲基磺酰)亚胺钠基聚合物电解质在固态钠电池中的性能[J]. 物理化学学报, 2018, 34(2): 213 -218 .
[14]	袁俊,刘晔,朱灿,沈平,万梅秀,冯柳柳,邹应萍. 基于侧链不对称喹喔啉聚合物的高效非富勒烯太阳电池[J]. 物理化学学报, 2018, 34(11): 1272 -1278 .
[15]	国霞,凡群平,崔超华,张志国,张茂杰. 基于无规三元共聚物的非卤溶液加工型高效聚合物太阳能电池[J]. 物理化学学报, 2018, 34(11): 1279 -1285 .

多钨酸盐修饰ZrO₂气凝胶催化四氢呋喃开环聚合

Polyoxotungstate-Modified Zirconia Aerogel as a Solid Catalyst for Tetrahydrofuran Polymerization

PDF (PC)

赞

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

Metrics

本文评价

推荐阅读 10