自组装半导体碳纳米管薄膜的光电特性

doi:10.3866/PKU.WHXB201405093

物理化学学报 >> 2014, Vol. 30 >> Issue (7): 1377-1383.doi: 10.3866/PKU.WHXB201405093

自组装半导体碳纳米管薄膜的光电特性

赵青靓¹, 刘旸^1,2, 魏楠¹, 王胜¹

1. 北京大学电子学系, 纳米器件物理与化学教育部重点实验室, 北京 100871;
2. 北京大学前沿交叉学科研究院, 北京 100871

收稿日期:2014-02-26 修回日期:2014-05-06 发布日期:2014-06-30
通讯作者: 王胜 E-mail:shengwang@pku.edu.cn
基金资助:
国家重点基础研究发展规划项目（973）（2011CB933002，2011CB933001）和国家自然科学基金（61370009，61271051，61321001）资助

Photoelectric Characteristics of Self-Assembled Semiconducting Carbon Nanotube Thin Films

ZHAO Qing-Liang¹, LIU Yang^1,2, WEI Nan¹, WANG Sheng¹

1. Key Laboratory for the Physics and Chemistry of Nanodevices, Department of Electronics, Peking University, Beijing 100871, P. R. China;
2. Academy for Advanced Interdisciplinary Studies, Peking University, Beijing 100871, P. R. China

Received:2014-02-26 Revised:2014-05-06 Published:2014-06-30
Contact: WANG Sheng E-mail:shengwang@pku.edu.cn
Supported by:
The project was supported by the National Key Basic Research Program of China (973) (2011CB933002, 2011CB933001) and National Natural Science Foundation of China (61370009, 61271051, 61321001).

摘要/Abstract

摘要：

采用自组装的方法制备99%高纯度半导体碳纳米管平行阵列条带，以金属钯和钪为非对称接触电极制备碳纳米管（CNT）薄膜晶体管（TFTs）器件. 主要研究不同沟道长度碳纳米管薄膜晶体管器件的电输运特性和红外光电响应特性，分析了其中的载流子输运和光生载流子分离的物理机制. 我们发现薄膜晶体管器件的电学性能和光电性能依赖于器件沟道长度（L）和碳纳米管的平均长度（L_CNT）. 当沟道长度小于碳纳米管的平均长度时，器件开关比最低；当沟道长度超过碳纳米管平均长度时，随着沟道长度的增加，器件开关比增加，光电流减小.相关研究结果为高纯碳纳米管薄膜晶体管器件在红外光探测器方面的进一步应用提供参考依据.

关键词: 碳纳米管, 自组装, 非对称接触, 光电响应, 红外, 沟道长度, 薄膜晶体管

Abstract:

We used the self-assembly method to formhigh purity (99%) semiconducting carbon nanotube (CNT) aligned arrays. Thin-film transistors (TFTs) were fabricated with asymmetric Pd and Sc electrodes. We studied the electronic transport characteristics and infrared photoelectronic properties of the TFTs with different channel lengths. The physical mechanism of carrier transport and the dissociation of photoexcited carries are also discussed. We found that the electronic and photoelectronic properties of the TFTs were dependent on the channel length and the average length of the CNTs. The on/off ratio of the device was the lowest when the channel length of the device (L) was less than the average length of the CNTs (L_CNT), and it increased with increasing L when L was larger than L_CNT. In addition, the short circuit current of the device also decreased. These results provide an effective reference for further infrared detector applications based on high-purity semiconducting carbon nanotube TFTs.

Key words: Carbon nanotube, Self-assembly, Asymmetric contact, Photoelectric response, Infrared, Channel length, Thin filmtransistor

MSC2000:

O649

赵青靓, 刘旸, 魏楠, 王胜. 自组装半导体碳纳米管薄膜的光电特性[J]. 物理化学学报, 2014, 30(7): 1377-1383.

ZHAO Qing-Liang, LIU Yang, WEI Nan, WANG Sheng. Photoelectric Characteristics of Self-Assembled Semiconducting Carbon Nanotube Thin Films[J]. Acta Phys. -Chim. Sin., 2014, 30(7): 1377-1383.

参考文献

(1) Iijima, S. Nature 1991, 354, 56. doi: 10.1038/354056a0
(2) Perebeinos, V.; Tersoff, J.; Avouris, P. Nano Lett. 2006, 6, 205. doi: 10.1021/nl052044h
(3) Purewal, M. S.; Hong, B. H.; Ravi, A.; Chandra, B.; Hone, J.; Kim, P. Phys. Rev. Lett. 2007, 98, 186808. doi: 10.1103/PhysRevLett.98.186808
(4) Cao, Q.; Kim, H. S.; Pimparkar, N.; Kulkarni, J. P.; Wang, C.; Shim, M.; Roy, K.; Alam, M. A.; Rogers, J. A. Nature 2008, 454, 495. doi: 10.1038/nature07110
(5) Liang, X. L.; Wang, S.; Wei, X. L.; Ding, L.; Zhu, Y. Z.; Zhang, Z. Y.; Chen, Q.; Li, Y.; Zhang, J.; Peng, L. M. Adv. Mater. 2009, 21, 1339. doi: 10.1002/adma.v21:13
(6) Zhu, Y. Z.; Wang, S.; Wei, X. L.; Ding, L.; Zhang, Z. Y.; Liang, X. L.; Chen, Q.; Peng, L. M. Acta Phys. -Chim. Sin. 2008, 24, 2122. [朱玉振,王胜,魏贤龙, 丁力, 张志勇, 梁学磊, 陈清,彭练矛, 物理化学学报, 2008, 24, 2122]
(7) Bachilo, S. M.; Strano, M. S.; Kittrell, C.; Hauge, R. H.; Smalley, R. E.; Weisman, R. B. Science 2002, 298, 2361. doi: 10.1126/science.1078727
(8) Itkis, M. E.; Borondics, F.; Yu, A.; Haddon, R. C. Science 2006, 312, 413. doi: 10.1126/science.1125695
(9) Yang, L. J.; Wang, S.; Zeng, Q. S.; Zhang, Z. Y.; Li, Y.; Zhou, W. W.; Liu, J.; Peng, L. M. ACS Appl. Mater. Inter. 2012, 4, 1154. doi: 10.1021/am201778x
(10) Tans, S. J.; Verschueren, A. R. M.; Dekker, C. Nature 1998, 393, 49. doi: 10.1038/29954
(11) Javey, A.; Guo, J.; Wang, Q.; Lundstrom, M.; Dai, H. J. Nature 2003, 424, 654. doi: 10.1038/nature01797
(12) Zhang, Z.; Liang, X.; Wang, S.; Yao, K.; Hu, Y.; Zhu, Y.; Chen, Q.; Zhou, W.; Li, Y.; Yao, Y.; Zhang, J.; Peng, L. M. Nano Lett. 2007, 7, 3603. doi: 10.1021/nl0717107
(13) Ding, L.; Wang, S.; Zhang, Z. Y.; Zeng, Q. S.; Wang, Z. X.; Pei, T.; Yang, L. J.; Liang, X. L.; Shen, J.; Chen, Q.; Cui, R. L.; Li, Y.; Peng, L. M. Nano Lett. 2009, 9, 4209. doi: 10.1021/nl9024243
(14) Wang, S.; Zhang, Z. Y.; Ding, L.; Liang, X. L.; Sun, J.; Xu, H. L.; Chen, Q.; Cui, R. L.; Li, Y.; Peng, L. M. Adv. Mater. 2008, 20, 3258. doi: 10.1002/adma.v20:17
(15) Yang, L.; Wang, S.; Zeng, Q. S.; Zhang, Z. Y.; Pei, T.; Li, Y.; Peng, L. M. Nature Photon. 2011, 5, 672. doi: 10.1038/nphoton.2011.250
(16) Yang, L.; Wang, S.; Zeng, Q. S.; Zhang, Z. Y.; Peng, L. M. Small 2013, 9, 1225. doi: 10.1002/smll.201203151
(17) Snow, E. S.; Novak, J. P.; Campbell, P. M.; Park, D. Appl. Phys. Lett. 2003, 82, 2145. doi: 10.1063/1.1564291
(18) Zhang, J.; Wang, C.; Fu, Y.; Che, Y.; Zhou, C. W. ACS Nano 2011, 5, 3284. doi: 10.1021/nn2004298
(19) Wang, C.; Zhang, J.; Zhou, C. W. ACS Nano 2010, 4, 7123. doi: 10.1021/nn1021378
(20) Wei, J. Q.; Jia, Y.; Shu, Q. K.; Gu, Z. Y.; Wang, K. L.; Zhuang, D. M.; Zhang, G.; Wang, Z. C.; Luo, J. B.; Cao, A. Y.; Wu, D. H. Nano Lett. 2007, 7, 2317. doi: 10.1021/nl070961c
(21) Wang, C.; Zhang, J.; Ryu, K.; Badmaev, A.; Arco, L. G.; Zhou, C. W. Nano Lett. 2009, 9, 4285. doi: 10.1021/nl902522f
(22) Shastry, T, A.; Seo, J.; Lopez, J.; Arnold, H.; Kelter J.; Sangwan, V.; Lauhon, L.; Marks, T.; Hersam, M. C. Small 2013, 9, 45. doi: 10.1002/smll.v9.1
(23) Engel, M.; Small, J. P.; Steiner, M.; Freitag, M.; Green, A. A.; Hersam, M. C.; Avouris, P. ACS Nano 2008, 2, 2445. doi: 10.1021/nn800708w
(24) Kinoshita, M.; Steiner, M.; Engel, M.; Small, J. P.; Green, A. A.; Hersam, M. C.; Krupke, R.; Mendez, E. E.; Avouris, P. Opt. Express 2010, 18, 25738. doi: 10.1364/OE.18.025738
(25) Dresselhaus, M. S.; Dresselhaus, G.; Saito, R.; Jorio, A. Phys. Rep. 2005, 409, 47. doi: 10.1016/j.physrep.2004.10.006
(26) Cao, Q.; Han, S.; Tulevski, G. S.; Zhu, Y.; Lu, D. D.; Haensch, W. Nature Nanotech. 2013, 8, 180. doi: 10.1038/nnano.2012.257

[1]	方佳丽, 陈新, 李唱, 吴玉莲. 原位液体室透射电镜观察金纳米棒/石墨烯复合物的形成和运动过程[J]. 物理化学学报, 2019, 35(8): 808 -815 .
[2]	焦建梅,徐桂英,辛霞. 胆酸盐参与的自组装及微纳米材料制备[J]. 物理化学学报, 2019, 35(7): 684 -696 .
[3]	李路路,姚路,段力. 基于共价有机框架复合材料的锂硒电池应用[J]. 物理化学学报, 2019, 35(7): 734 -739 .
[4]	赵喆, 卢岳, 张振华, 隋曼龄. 原位透射电子显微镜观察电荷驱动的氧化物纳米颗粒水中自组装[J]. 物理化学学报, 2019, 35(5): 539 -545 .
[5]	刘恒昌,冯玉军. CO₂诱导的五嵌段非离子共聚物与阴离子氟碳表面活性剂的相互作用[J]. 物理化学学报, 2019, 35(4): 408 -414 .
[6]	王灏珉,何茂帅,张莹莹. 碳纳米管薄膜的制备及其在柔性电子器件中的应用[J]. 物理化学学报, 2019, 35(11): 1207 -1223 .
[7]	程晓蒙,焦东霞,梁志豪,魏金金,李宏平,杨俊佼. 聚苯乙烯-聚4-乙烯基吡啶两亲嵌段共聚物在CO₂膨胀液体中的组装行为[J]. 物理化学学报, 2018, 34(8): 945 -951 .
[8]	周士超,冯贵涛,夏冬冬,李诚,武永刚,李韦伟. 萘酰亚胺-卟啉星型电子受体分子的构筑及其在非富勒烯太阳能电池中的应用[J]. 物理化学学报, 2018, 34(4): 344 -347 .
[9]	尹玥琪,蒋梦绪,刘春光. Keggin型多酸负载的单原子催化剂(M₁/POM, M = Ni, Pd, Pt, Cu, Ag, Au, POM = [PW₁₂O₄₀]^3-)活化氮气分子的密度泛函理论计算研究[J]. 物理化学学报, 2018, 34(3): 270 -277 .
[10]	黄丽丽,邵翔. CO与蜜勒胺自组装膜协同作用制备Au单原子及多原子物种[J]. 物理化学学报, 2018, 34(12): 1390 -1396 .
[11]	相欣然,万晓梅,索红波,胡燚. 功能化离子液体修饰多壁碳纳米管固定化Candida antarctic lipase B[J]. 物理化学学报, 2018, 34(1): 99 -107 .
[12]	于景华,李文文,朱红. 管径对碳纳米管负载铂催化剂氧还原的影响[J]. 物理化学学报, 2017, 33(9): 1838 -1845 .
[13]	张洪芝,张志庆,王芳,周亭,王秀凤,张国栋,刘婷婷,刘淑贞. 结构DNA纳米技术应用新进展[J]. 物理化学学报, 2017, 33(8): 1520 -1532 .
[14]	王琳,肖立志,郭龙,廖广志,张岩,戈革. 纳米自组装γ-Al₂O₃孔隙结构的核磁共振表征[J]. 物理化学学报, 2017, 33(8): 1589 -1598 .
[15]	鞠广凯,陶占良,陈军. α-MnO₂纳米管自组装微球的可控制备及电化学性能[J]. 物理化学学报, 2017, 33(7): 1421 -1428 .

自组装半导体碳纳米管薄膜的光电特性

Photoelectric Characteristics of Self-Assembled Semiconducting Carbon Nanotube Thin Films

PDF (PC)

赞

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

Metrics

本文评价

推荐阅读 10