Anodic Electrocrystallization of BaKPbO and BaKPbBiO from Molten Salt

Zhang Lin, Zhao Liang-Zhong, Zhang Jin-Biao, Xu Cui-Ying, Liu Shi-Hong   

  1. Institute of Chemistry,Chinese Academy of Science,Beijing 100080
  • Received:1999-01-25 Revised:1999-05-03 Published:1999-11-15
  • Contact: Zhang Lin

关键词: 复杂氧化物, 阳极电结晶, 超导性, 电子结构

Abstract:

BaKPbO and BaKPbBiO single crystals were electrodeposited on anode by the molten salt electrochemical method using KOH/KNO3 as flux. It is found that the K content decreases when the KNO3 concentration in the flux increases. On the other hand, when the KNO3 concentration in the flux is constant, the K content increases as the Bi content in the BaKPbBiO crystals increases. The magnetic susecptibility measurements show that Ba-K-Pb-Bi-O crystals are superconducting while BaKPbO crystals are not. XPS analyses reveal that the M(M=Pb, Bi)6s-O2p valence band moves toward the Fermi level when the Bi content in BaKPbBiO decreases.