Study of Passivation and Pitting Corrosion for Ni Electrode in Borax-Borate Solution

Zhou Guo-Ding; Zhang Guo-Qing; Tong Ru-Ting; Jin Shi-Xun; Cai Sheng-Min   

  1. Shanghai Institute of Electric Power, Shanghai 200090; Department of Chemistry, Hebei Normal University; Department of Chemistry, Peking University
  • Received:1990-12-04 Revised:1991-07-18 Published:1992-06-15
  • Contact: Zhou Guo-Ding

关键词: 镍电极, 钝化, 点蚀, 交流阻抗技术, 硼砂-硼酸溶液

Abstract: The passivation behavior and the pitting process at the fixed potentials for Ni electrode in Na_2SO_4-borax-borate buffer solution have been studied with alternating current(AC) impedance technique. For the passivation in the Cl~--free buffer solution the maximum of impedance moduli |Z| and the minimum of capacitances C_(dl) appeared at the potential of -0.2 V (vs. Hg/HgO), because both the thickness of passive film and the rate of anodic dissolution increased with rising potential. As the pitting went on in the Cl~--containing buffer solutions at the fixed potentials, |Z| at low fretrations of 0.1, 0.05, 0.01 mol·L~(-1) and the fixed potentials of 0.2, 0.7, 0.7 V, respectively, are discussed.

Key words: Ni electrode, Passivation, Pitting corrosion, Alternating Current impedance techniques, Borax-borate solution