(Sr1-x,Eux)B4O7的结构及其发光性能研究

刘德文; 莫述诚; 陈朝宗   

  1. 北京轻工业学院化工系，北京 100037；北京大学化学系，北京 100871
  • 收稿日期:1991-05-27 修回日期:1992-01-27 发布日期:1992-10-15
  • 通讯作者: 刘德文

A Study on the Structure and Luminescent Properties of (Sr1-x,Eux)B4O7

Liu De-Wen; Mo Shu-Cheng; Chen Zhao-Zong   

  1. Department of Chemical Engineering, Beijing Institute of Light Industry, Beijing 100037; Department of Chemistry, Peking University, Peking University, Beijing 100871
  • Received:1991-05-27 Revised:1992-01-27 Published:1992-10-15
  • Contact: Liu De-Wen

PDF (PC)

2721

赞

关键词: 紫外发射, X射线衍射, 激活剂Eu2+

Abstract: A sample was produced by heating the mixture of boric acid, strontium carbonate added europium oxide at 800—1000 ℃ in reductive atmosphere for 4 hours. According to the pattern of X-ray diffraction of the sample, Its phase and mechanism of emission under the ultraviolet excitation of sample are discussed. It was shown that the emission was relative with the content of Sr_(1-x)Eu_xB_4O_7 as well as the impurity of the sample.

Key words: UV-emission, X-ray diffraction, Luminous center Eu2+