Abstract: Chemical experiments and XPS analysis indicate that YBCO superconductor is a relatively strong base, and Ba-O components in YBCO is primarily responsible for its hasicity. Based on the basic property of YBCO, it is suggested that the chemical interactions between YBCO and oxide substrate materials is primarily solid acid-base reactions. The acid-base parameters for substrate materials (MgO, ZrO_2, Al_2O_3 and SiO_2) are calculated and used as a scale for measuring the acidity or basicity of the oxide substrates and for evaluating the YBCO-substrates chemical reactivity. It is found that the chemical reactivity increases with increasing acid-base parameter (or increases with increasing acidity) of the substrate materials. Therefore the chemical reactivity with YBCO increases in the order of MgOThe above rule is also suitable for chemical reaction of BSCCO superconductor with oxide substrate materials.
Key words: YBa2Cu3O7 high-Tc superconductor, Oxide substrate materials, Solid acid-base reaction, Acid-base parameter
赵良仲. YBCO高温超导体与氧化物衬底的化学反应性[J]. 物理化学学报, 1991, 7(06): 648-650.
Zhao Liang-Zhong. The Chemical Interaction of YBCO High-Tc Superconductor with Oxide Substrate Materials[J]. Acta Phys. -Chim. Sin., 1991, 7(06): 648-650.
0 /
导出引用管理器 EndNote (中文内容)|EndNote (英文内容)| Reference Manager|ProCite|BibTeX|RefWorks
链接本文: http://www.whxb.pku.edu.cn/CN/10.3866/PKU.WHXB19910603
http://www.whxb.pku.edu.cn/CN/Y1991/V7/I06/648
Cited