物理化学学报 >> 1990, Vol. 6 >> Issue (03): 259-262.doi: 10.3866/PKU.WHXB19900302
张玉芬; 周鼎元; 郑香苗; 林炳雄; 唐有祺
Zhang Yu-Fen; Zhou Ding-Yuan; Zheng Xiang-Miao; Lin Bing-Xiong; Tang You-Qi
Abstract: Subramanian et al. found superconductivity at 80 K in Tl_(0.5)Pb_(0.5)Sr_2CaCu_2O_y sample with YBa_2 Cu_3 O_(7-δ)-like structure. However, there is unstable factor in the structure of the superconductor. Total plus valence is 12.5, and total minus valence is 14. The structure was further stabilized by partial substitution of Y, La, Nd orPr for Ca and Sn~(4+) or Sb~(5+) for (Tl, Pb), so that T_c was achieved above 100 K. For example, T_c is about 103 K in a sample with nominal composition (Tl_(0.4) Pb_(0.5)Sn_(0.2))Sr_2(Ca_(0.8)Y_(0.2))Cu_2O_(7-δ). During the preparation of superconductors, the temperature of samples was very slowly down after sintering, or samples were annealed at 500—700 ℃. The samples absorbed the oxygen during cooling, but no phase change occured. Appropriate amount of the oxygen made T_e higher.
张玉芬;周鼎元;郑香苗;林炳雄;唐有祺. 掺杂对超导体(Tl1-x-yPbxMy)Sr2(Ca0.8Ln0.2)Cu2O7-δ(M=Sn4+或Sb5+, Ln=Y, La, Nd或Pr)性能的影响[J]. 物理化学学报, 1990, 6(03): 259-262.
Zhang Yu-Fen; Zhou Ding-Yuan; Zheng Xiang-Miao; Lin Bing-Xiong; Tang You-Qi. Influence of Doping on Properties of Superconductor (Tl1-x-yPbxMy)Sr2(Ca0.8Ln0.2)Cu2O7-δ(M=Sn4+ or Sb5+, Ln=Y, La, Nd or Pr)[J]. Acta Phys. -Chim. Sin., 1990, 6(03): 259-262.
导出引用管理器 EndNote (中文内容)|EndNote (英文内容)|