物理化学学报 >> 2003, Vol. 19 >> Issue (05): 398-402.doi: 10.3866/PKU.WHXB20030504

研究论文 上一篇    下一篇

Tb掺杂SiO2-B2O3-NaF玻璃的制备及发光性质

王喜贵;吴红英;翁诗甫;吴瑾光   

  1. 内蒙古师范大学化学系,呼和浩特 010022;北京大学化学与分子工程学院,稀土材料化学及应用国家重点实验室,北京 100871
  • 收稿日期:2002-08-29 修回日期:2002-10-28 发布日期:2003-05-15
  • 通讯作者: 王喜贵 E-mail:wangxigui@21cn.com

Synthesis and Luminescent Properties of Tb-doped SiO2-B2O3-NaF Glass

Wang Xi-Gui;Wu Hong-Ying;Weng Shi-Fu;Wu Jin-Guang   

  1. Department of Chemistry, Inner Mongolia Normal University, Huhhot 010022;State Key Laboratory of Rare Earth Materials Chemistry and Application, College of Chemistry and Molecular Engineering, Peking University, Beijing 100871
  • Received:2002-08-29 Revised:2002-10-28 Published:2003-05-15
  • Contact: Wang Xi-Gui E-mail:wangxigui@21cn.com

摘要: 使用正硅酸乙酯、硼酸和氟化钠为前驱体,0.10 mol•L-1TbCl3溶液为掺杂剂,通过溶胶-凝胶方法制备了Tb3+掺杂的SiO2-B2O3-NaF玻璃,研究了Tb3+在SiO2-B2O3-NaF体系中的发光性质,结果显示发光体能产生强的绿色发光(544 nm),归属于Tb3+的5D4—7F5电子跃迁.Tb3+含量不同时,除发光强度不同外,其发射光谱基本相同,并且在低掺杂Tb3+样品和低退火温度样品中检测到了来自5D3跃迁产生的峰,其跃迁随Tb3+掺杂浓度的增加和退火温度的升高而发生猝灭,这种现象归因于5D3-5D47F6—7F0和/或5D3—7F07F6—5D4跃迁中发生了交叉弛豫现象.Tb3+在SiO2-B2O3-NaF玻璃中的激发光谱由一个宽峰和一系列窄峰组成,宽峰最大波长位于230 nm,对应于Tb3+的4f 8—4f 75d 1跃迁,一系列窄峰位于300~380 nm处,归属于4f 8跃迁,所有发光材料的XRD和TEM测试显示材料是非晶态的.

关键词: Tb3+, 发光性质, SiO2-B2O3-NaF玻璃

Abstract: Tb-doped SiO2-B2O3-NaF glass was prepared by sol-gel process,using tetraethoxy silcane, boric acid and sodium fluoride as precursors,0.10 mol•L-1 TbCl3 solution as the dopant. The luminescent properties of Tb3+ doped SiO2-B2O3-NaF phosphors were investigated. The phosphors showed prominent luminescence in green, due to the electronic transition of 5D4—7F5 (Tb3+).For all Tb3+ concentrations used the emission spectrum was essentially the same with the exception of intensity and weak peak belonging to transition from 5D3 was detected in lower Tb3+ doped samples and lower annealing temperature samples. The intensity of emission from 5D3 quenches with increasing of the Tb3+ concentration and annealing temperature. The observation showed that cross-relaxation obviously took place in the transition 5D3-5D47F6—7F0 and/or 5D3—7F07F6—5D4.The excitation spectra of Tb3+ emission in SiO2-B2O3-NaF glass consist of broad bands with a maximum at about 230 nm, corresponding to 4f 8—4f 75d 1 transition of Tb3+ ion, and a series of sharp lines in the range of 300 to 380 nm which belong to transitions between the energy levels of the 4f 8 configuration. The structural characterization of these luminescent materials were carried by using XRD and TEM. The results showed that the phosphor was in amorphous phase.

Key words: Tb3+, Luminescent property, SiO2-B2O3-NaF glass