超细二氧化锆的制备和表征

刘源,钟炳,彭少逸,吴东,范文浩   

  1. 中国科学院山西煤炭化学研究所,太原 030001
  • 收稿日期:1994-08-14 修回日期:1900-01-01 发布日期:1995-09-15
  • 通讯作者: 刘源

The Preparation and Characterization of Ultrafine ZrO2

Liu Yuan,Zhong Bing,Peng Shao-Yi,Wu Dong,Fan Wen-Hao   

  1. Institute of Coal Chemistry,Academia Sinica,Taiyuan 030001
  • Received:1994-08-14 Revised:1900-01-01 Published:1995-09-15
  • Contact: Liu Yuan

摘要:

通过研究不同干燥条件下制得的二氧化锆的织构和结构,发现在超临界干燥过程中附加一定的惰性气体压力能够防止或大大减小凝胶在干燥过程中的收缩,从而可提高BET表面积,和普通空气中干燥得到的二氧化锆相比,超临界干燥得到的二氧化锆的孔结构大为改善,同时BET表面积也增大.

关键词: 超临界干燥, 超细粒子, 二氧化锆

Abstract:

Ultrafine ZrO2 with high BET surface area and large pore size, as compared with that dried in air, was prepared by Super Critical Drying. In Super Critical Drying process, application of inert gas pressure could eliminate or reduce the gel shrinkage, so that the surface area and pore volume of ZrO2 could be increased and its particle size and pore size could be decreased.

Key words: Super critical drying, Ultrafine particle, Zireonia