物理化学学报 >> 1998, Vol. 14 >> Issue (04): 365-368.doi: 10.3866/PKU.WHXB19980416

研究简报 上一篇    下一篇

AMT在铜表面形成保护膜的STM研究

李瑛, 曹楚南, 林海潮, 朱一帆, 李大钢, 施兵兵, 万俐, 徐飞, 陶保成   

  1. 中国科学院金属腐蚀与防护研究所 腐蚀与防护国家重点实验室,沈阳 110015|南京化工大学,南京 210037|南京博物馆,南京 210000
  • 收稿日期:1997-08-04 修回日期:1997-10-20 发布日期:1998-04-15
  • 通讯作者: 李瑛

Study on the Protection Film of AMT Formed on Bronze by Scanning Tunneling Microsecopy

Li Ying, Cao Chu-Nan, Lin Hai-Chao, Zhu Yi-Fan, Li Da-Gang, Shi Bing-Bing, Wan Li, Xu Fei, Tao bao-Cheng   

  1. Institute of Corrosion and Protection of Metal,Key Laboratory of Corrosion and Protection of Metal,SIC,Shenyang,110015|Naning Chemical Industry University,Nanjing 210037|Nanjing Museum,Nanjing 210000
  • Received:1997-08-04 Revised:1997-10-20 Published:1998-04-15
  • Contact: Li Ying

关键词: 保护膜, 缓腐蚀, 青铜, STM

Abstract:

The morphology of the protection film of AMT formed on bronze has been observed by scanning tunneling microscopy in angstrom scale. Three to five ellipse units join together to forma linear structure. Many such linear structures make up the protection film to prevent corrosion process of bronze. After analysis the reactivity of AMT with Cu (Ⅱ ) by XPS,XAES and IR, the conclusion has been obtained as follow: corrosion product Cu(Ⅱ ) combined with AMT forming a complex compound which deposits on the bronze from the protection film. The structure has been describe in the letter.

Key words: Protection film, Inhibitor, Bronze, STM