网状多级孔结构氧化铁的制备、合成机理及其光催化性质

doi:10.3866/PKU.WHXB201206122

摘要/Abstract

摘要：

以九水合硝酸铁为原料, 利用改进的聚合诱导胶体聚集(PICA)的方法制备出三维网络状多级孔结构氧化铁(HPH). 此结构的制备关键是在合成过程中尿素和甲醛聚合生成脲醛树脂(UF). 脲醛树脂一方面在铁的羟基氧化物生长过程中与之杂化形成杂化产物Fe-UF, 另一方面则进一步聚合, 形成脲醛树脂微球(UFM). 脲醛树脂微球作为模板诱导杂化产物Fe-UF在其表面的聚集. 微球与微球之间则由于表面存在的脲醛树脂间的聚合会相互交联形成网络状结构. 经过煅烧处理后, 脲醛树脂及脲醛树脂微球的分解导致不同尺寸孔结构的生成. 光催化研究结果表明, 产物对罗丹明B的降解效率是商用纳米氧化铁的4倍.

关键词: α-Fe₂O₃, 多级孔结构, 聚合诱导胶体聚集法, 光催化降解

Abstract:

Hierarchical porous hematite (HPH) network structures were successfully constructed using an improved polymerization induced colloid aggregation process with Fe(NO₃)₃·9H₂O as the raw material. The polymerization between urea and formaldehyde into urea-formaldehyde (UF) resin is the key factor for this construction. The UF resins appear to be advantageous in two respects: the UF oligomer hybrids with ferric hydroxide (Fe-UF) and UF polymer formed microcapsules (UFM) acted as templates to induce the aggregation of Fe-UF hybrids into mesoporous spheres. The further crosslink reactions among the hybrid spheres generate the network structure. After calcination, the decomposition of the UF resin and the UFM produces nanopores in the nanorod subunits and macropores in the network structure, respectively. The photodegradation activity of the unique structured HPH is four times that of the commercial hematite nanoparticles with rhodamine B (RhB) as pollutant.

Key words: α-Fe₂O₃, Hierarchical porous structure, Polymerization induced colloid aggregation method, Photodegradation

MSC2000:

O648

点击下载补充材料PDF格式文件

范海滨, 张东凤, 郭林. 网状多级孔结构氧化铁的制备、合成机理及其光催化性质[J]. 物理化学学报, 2012, 28(09): 2214-2220.

FAN Hai-Bin, ZHANG Dong-Feng, GUO Lin. Fabrication, Formation Mechanism and the Photocatalytic Properties of Hierarchical Porous Hematite Networks[J]. Acta Phys. -Chim. Sin., 2012, 28(09): 2214-2220.

参考文献

(1) Im, S. H.; Jeong, U. Y.; Xia, Y. N. Nat. Mater. 2005, 4 (9), 671.doi: 10.1038/nmat1448
(2) Yuan, Z. Y.; Su, B. L. J. Mater. Chem. 2006, 16 (7), 663. doi: 10.1039/b512304f
(3) Toberer, E. S.; Seshadri, R. Adv. Mater. 2005, 17 (18), 2244. doi: 10.1002/adma.200500668
(4) Ishizuka, N.; Minakuchi, H.; Nakanishi, K.; Hirao, K.; Tanaka,N. Colloid Surf. A-Physicochem. Eng. Asp. 2001, 187, 273. doi: 10.1016/S0927-7757(01)00642-2
(5) Du, J.; Lai, X. Y.; Yang, N. L.; Zhai, J.; Kisailus, D.; Su, F. B.;Wang, D.; Jiang, L. ACS Nano 2011, 5 (1), 590. doi: 10.1021/nn102767d
(6) Toberer, E. S.; Schladt, T. D.; Seshadri, R. J. Am. Chem. Soc.2006, 128 (5), 1462. doi: 10.1021/ja0579412
(7) Gao, G. D.; Li, J.; Zhang, A. Y.; An, X. H.; Zhou, L. Acta Phys. -Chim. Sin. 2010, 26, 2437. [高冠道, 李婧, 张爱勇,安晓红, 周蕾. 物理化学学报, 2010, 26, 2437.]
(8) Li, H. N.; Zhang, L.; Dai, H. X.; He, H. Inorg. Chem. 2009, 48 (10), 4421. doi: 10.1021/ic900132k
(9) Amutha, R.; Muruganandham, M.; Sathish, M.; Akilandeswari,S.; Suri, R. P. S.; Repo, E.; Sillanpää, M. J. Phys. Chem. C2011, 115 (14), 6367. doi: 10.1021/jp200301g
(10) Jiang, Z. T.; Zuo, Y. M. Anal. Chem. 2001, 73 (3), 686. doi: 10.1021/ac001008u
(11) Peng, X.; Zhang, Q. X.; Cheng, X.; Cao, D. P. Acta Phys. -Chim. Sin. 2011, 27, 2065. [彭璇, 张勤学, 成璇, 曹达鹏. 物理化学学报, 2011, 27, 2065.] doi: 10.3866/PKU.WHXB20110919
(12) Cho, C. Y.; Moon, J. H. Adv. Mater. 2011, 23 (26), 2971.doi: 10.1002/adma.201101042
(13) Barakat, T.; Rooke, J. C.; Tidahy, H. L.; Hosseini, M.; Cousin,R.; Lamonier, J. F.; Giraudon, J. M.; DeWeireld, G.; Su, B. L.;Siffert, S. ChemSusChem 2011, 4 (10), 1420. doi: 10.1002/cssc.201100282
(14) Lee, J.; Kim, J.; Jia, H. F.; Kim, M. I.; Kwak, J. H.; Jin, S. M.;Dohnalkova, A.; Park, H. G.; Chang, H. N.;Wang, P.; Grate, J.W.; Hyeon, T. Small 2005, 1 (7), 744. doi: 10.1002/smll.200500035
(15) Ma, G. X.; Zhong, Q. D.; Lu, X. G.; Lu, T. H. Acta Phys. -Chim. Sin. 2009, 25, 2061. [马国仙, 钟庆东, 鲁雄刚, 陆天虹. 物理化学学报, 2009, 25, 2061.] doi: 10.3866/PKU.WHXB20091037
(16) Croce, F.; Epifanio, A. D.; Hassoun, J.; Deptula, A.; Olczac, T.;Scrosati, B. Electrochem. Solid State Lett. 2002, 5 (3), A47.
(17) Wang, J. H.; Li, B.;Wu, H. Y.; Guo, Y. Z. Acta Phys. -Chim. Sin.2008, 24, 681. [王剑华, 李斌, 吴海燕, 郭玉忠. 物理化学学报, 2008, 24, 681.] doi: 10.3866/PKU.WHXB20080423
(18) Cheng, F.; Tao, Z.; Liang, J.; Chen, J. Chem. Mater. 2008, 20 (3), 667. doi: 10.1021/cm702091q
(19) Li, J. S.; Gu, J.; Ling, X. F.; Sun, X. Y.; Shen, J. Y.; Han,W. Q.;Wang, L. J. Acta Phys. -Chim. Sin. 2011, 27, 1772. [李健生,顾娟, 凌晓凤, 孙秀云, 沈锦优, 韩卫清, 王连军. 物理化学学报, 2011, 27, 1772.] doi: 10.3866/PKU.WHXB20110613
(20) Tsung, C. K.; Fan, J.; Zheng, N. F.; Shi, Q. H.; Forman, A. J.;Wang, J. F.; Stucky, G. D. Angew. Chem. Int. Edit. 2008, 47 (45), 8682. doi: 10.1002/anie.200802487
(21) Li, L. L.; Xu, J.; Yuan, Q.; Li, Z. X.; Song,W. G.; Yan, C. H.Small 2009, 5 (23), 2730. doi: 10.1002/smll.200900901
(22) Yuan, Q.; Duan, H. H.; Li, L. L.; Li, Z. X.; Duan,W. T.; Zhang,L. S.; Song,W. G.; Yan, C. H. Adv. Mater. 2010, 22 (13), 1475.doi: 10.1002/adma.200904223
(23) Meng, Y.; Gu, D.; Zhang, F. Q.; Shi, Y. F.; Yang, H. F.; Li, Z.;Yu, C. Z.; Tu, B.; Zhao, D. Y. Angew. Chem. Int. Edit. 2005, 44 (43), 7053. doi: 10.1002/anie.200501561
(24) Lee, J.; Orilall, M. C.;Warren, S. C.; Kamperman, M.; Disalvo,F. J.;Wiesner, U. Nat. Mater. 2008, 7 (3), 222. doi: 10.1038/nmat2111
(25) Niu, D. C.; Ma, Z.; Li, Y. S.; Shi, J. L. J. Am. Chem. Soc. 2010,132 (43), 15144. doi: 10.1021/ja1070653
(26) Gao, C. B.; Qiu, H. B.; Zeng,W.; Sakamoto, Y.; Terasaki, O.;Sakamoto, K.; Chen, Q.; Che, S. A. Chem. Mater. 2006, 18 (16),3904. doi: 10.1021/cm061107+
(27) Li, G. X.;Wang, T.; He, J. P.; Zhou, J. H.; Xue, H. R.; Ma, Y.O.; Hu, Y. Y. Acta Phys. -Chim. Sin. 2011, 27, 248. [李国显,王涛, 何建平, 周建华, 薛海荣, 马一鸥, 胡园园. 物理化学学报, 2011, 27, 248.] doi: 10.3866/PKU.WHXB20110131
(28) Dong, A. G.; Ren, N.; Tang, Y.;Wang, Y. J.; Zhang, Y. H.; Hua,W. M.; Gao, Z. J. Am. Chem. Soc. 2003, 125 (17), 4976. doi: 10.1021/ja029964b
(29) Brezesinski, K.; Haetge, J.;Wang, J.; Mascotto, S.; Reitz, C.;Rein, A.; Tolbert, S. H.; Perlich, J.; Dunn, B.; Brezesinski, T.Small 2011, 7 (3), 407. doi: 10.1002/smll.201001333
(30) Sadakane, M.; Sasaki, K.; Kunioku, H.; Ohtani, B.; Abe, R.;Ueda,W. J. Mater. Chem. 2010, 20 (9), 1811. doi: 10.1039/b922416e
(31) Hu, J.; Abdelsalam, M.; Bartlett, P.; Cole, R.; Sugawara, Y.;Baumberg, J.; Mahajan, S.; Denuault, G. J. Mater. Chem. 2009,19 (23), 3855. doi: 10.1039/b900279k
(32) Chen, X. Q.; Li, Z. S.; Ye, J. H.; Zou, Z. G. Chem. Mater. 2010,22 (12), 3583. doi: 10.1021/cm100751w
(33) Wu, Q. Z.; Shen, Y.; Li, Y. G. Acta Phys. -Chim. Sin. 2003, 19,737. [邬泉周, 沈勇, 李玉光. 物理化学学报, 2003, 19,737.] doi: 10.3866/PKU.WHXB20030813
(34) Davis, S. A.; Burkett, S. L.; Mendelson, N. H.; Mann, S. Nature1997, 385, 420. doi: 10.1038/385420a0
(35) Liu, Z. T.; Fan, T. X.; Zhang,W.; Zhang, D. Microporous Mesoporous Mat. 2005, 85 (1-2), 82. doi: 10.1016/j.micromeso.2005.06.021
(36) Biette, L.; Carn, F.; Maugey, M.; Achard, M. F.; Maquet, T.;Steunou, N.; Livage, T.; Serier, H.; Backov, R. Adv. Mater.2005, 17 (24), 2970. doi: 10.1002/adma.200501368
(37) Sen, T.; Tiddy, G. J. T.; Casci, J. L.; Anderson, M.W. Angew. Chem. Int. Edit. 2003, 42 (38), 4649. doi: 10.1002/anie.200351479
(38) Shi, Y. F.; Zhang, F.; Hu, Y. S.; Sun, X. H.; Zhang, Y. C.; Lee, H.I.; Chen, L. Q.; Stucky, G. D. J. Am. Chem. Soc. 2010, 132 (16),5552. doi: 10.1021/ja1001136
(39) Ke, X. F.; Cao, J. M.; Zheng, M. B.; Chen, Y. P.; Liu, J. S. Acta Phys. -Chim. Sin. 2007, 23, 757. [柯行飞, 曹洁明, 郑明波, 陈勇平, 刘劲松. 物理化学学报, 2007, 23, 757.] doi: 10.3866/PKU.WHXB20070526
(40) Dacquin, J. P.; Dhainaut, J.; Duprez, D.; Royer, S.; Lee, A. F.;Wilson, K. J. Am. Chem. Soc. 2009, 131 (36), 12896. doi: 10.1021/ja9056486
(41) Yan, H.W.; Blanford, C. F.; Holland, B. T.; Smyrl,W. H.; Stein,A. Chem. Mater. 2000, 12 (4), 1134. doi: 10.1021/cm9907763
(42) Sadakane, M.; Asanuma, T.; Kubo, J.; Ueda,W. Chem. Mater.2005, 17 (13), 3546. doi: 10.1021/cm050551u
(43) Zhang, R.; Dai, H.; Du, Y.; Zhang, L.; Deng, J.; Xia, Y.; Zhao,Z.; Meng, X.; Liu, Y. Inorg. Chem. 2011, 50 (6), 2534. doi: 10.1021/ic1023604
(44) Zhu, G.; Xu, H.; Xiao, Y.; Liu, Y.; Yuan, A.; Shen, X. ACS Appl. Mater. Interfaces 2012, 4 (2), 744. doi: 10.1021/am2013882
(45) Shi, Y.; Li, X.; Hu, J. K.; Lu, J. H.; Ma, Y. C.; Zhang, Y. H.;Tang, Y. J. Mater. Chem. 2011, 21 (40), 16223. doi: 10.1039/c1jm11669j
(46) Mao, D.; Yao, J. X.; Lai, X. Y.; Yang, M.; Du, J. A.;Wang, D.Small 2011, 7 (5), 578. doi: 10.1002/smll.201001728
(47) Pattanayak, A.; Subramanian, A. Int. J. Appl. Ceram. Technol.2011, 8 (1), 94. doi: 10.1111/j.1744-7402.2009.02410.x
(48) Pattanayak, A.; Subramanian, A. Powder Technol. 2009, 192 (3), 359. doi: 10.1016/j.powtec.2009.01.023
(49) Blin, J. L.; Leonard, A.; Yuan, Z. Y.; Gigot, L.; Vantomme, A.;Cheetham, A. K.; Su, B. L. Angew. Chem. Int. Edit. 2003, 42 (25), 2872. doi: 10.1002/anie.200250816
(50) Kang, Y. J.; Shan,W.;Wu, J. Y.; Zhang, Y. H.;Wang, X. Y.;Yang,W. L.; Tang, Y. Chem. Mater. 2006, 18 (7), 1861. doi: 10.1021/cm060084w
(51) Han, L.; Shan, Z.; Chen, D. H.; Yu, X. J.; Yang, P. Y.; Tu, B.;Zhao, D. Y. J. Colloid Interface Sci. 2008, 318 (2), 315. doi: 10.1016/j.jcis.2007.10.026

[1]	何科林, 沈荣晨, 郝磊, 李佑稷, 张鹏, 江吉周, 李鑫. 纳米SiC基光催化剂研究进展[J]. 物理化学学报, 2022, 38(11): 2201021 - .
[2]	杨晓庆, 杨华琳, 卢欢, 丁皓璇, 童妍心, 饶斐, 张鑫, 申茜, 高健智, 朱刚强. 高催化活性2D/2D Ti₃C₂/Bi₄O₅Br₂纳米片异质结的构建及其可见光催化去除NO[J]. 物理化学学报, 2021, 37(10): 2005008 - .
[3]	王艺蒙, 张申平, 葛宇, 王臣辉, 胡军, 刘洪来. 多孔双金属氧化物/碳复合光催化剂对四环素的高效光催化降解[J]. 物理化学学报, 2020, 36(8): 1905083 - .
[4]	张云龙,章俞之,宋力昕,郭云峰,吴岭南,张涛. 砚状ZnO/石墨烯复合物的制备及其光催化性能[J]. 物理化学学报, 2017, 33(11): 2284 -2292 .
[5]	佟拉嘎,刘金艳,王岑晨,荣华,李巍. 微/纳米ZnO绒球的制备及其在自然光下催化降解有机染料性能[J]. 物理化学学报, 2015, 31(8): 1615 -1620 .
[6]	邢伟男, 倪良, 颜学升, 刘馨琳, 罗莹莹, 逯子扬, 闫永胜, 霍鹏伟. C@CdS/埃洛石纳米管复合光催化剂一步热解法的制备及光降解性能[J]. 物理化学学报, 2014, 30(1): 141 -149 .
[7]	林雪, 于丽丽, 闫丽娜, 关庆丰, 闫永胜, 赵晗. 球形、花形和线状钒酸铋的可控合成及光催化性能[J]. 物理化学学报, 2013, 29(08): 1771 -1777 .
[8]	杨汉培, 张颖超, 傅小飞, 宋双双, 吴俊明. CNTs表面改性与TiO₂-CNTs异质结光催化性能[J]. 物理化学学报, 2013, 29(06): 1327 -1335 .
[9]	黄海凤, 贾建明, 卢晗锋, 张宏华, 潘烈群. Zr/Ti摩尔比对锶锆钛复合氧化物在可见光下光催化性能的影响[J]. 物理化学学报, 2013, 29(06): 1319 -1326 .
[10]	陈红丽, 丁键, 王一萌. 具有多级孔道结构、高水热稳定性的含氧化镁Silicalite-1分子筛的合成[J]. 物理化学学报, 2013, 29(05): 1035 -1040 .
[11]	林雪, 关庆丰, 刘婷婷, 张瑶, 邹春杰. 不同形貌Bi₄Ti₃O₁₂粒子的可控合成及光催化性能[J]. 物理化学学报, 2013, 29(02): 411 -417 .
[12]	岳明波, 杨娜, 王一萌. 晶种导向干凝胶法制备成型ZSM-5分子筛[J]. 物理化学学报, 2012, 28(09): 2115 -2121 .
[13]	林雪, 吕鹏, 关庆丰, 李海波, 李洪吉, 蔡杰, 邹阳. Bi_3.25La_0.75Ti₃O₁₂纳米线的可见光催化性能[J]. 物理化学学报, 2012, 28(08): 1978 -1984 .
[14]	林雪, 关庆丰, 李海波, 李洪吉, 巴春华, 邓海德. Bi_3.25Nd_0.75Ti₃O₁₂纳米结构: 可控合成及其可见光催化活性[J]. 物理化学学报, 2012, 28(06): 1481 -1488 .
[15]	詹拥共, 陈启元, 尹周澜, 李莉莉, 蔡炳新. 一种新型纺锤状α-Fe₂O₃纳米晶的合成、表征及其表面性能[J]. 物理化学学报, 2010, 26(11): 3113 -3119 .