Tm3+掺杂的NaYF4微米颗粒中强烈的单带下转换荧光发射

doi:10.3866/PKU.WHXB201509142

摘要/Abstract

摘要：

采用柠檬酸钠辅助的水热方法合成了一系列具有不同长径比的Tm³⁺掺杂的β-NaYF₄ (NaYF:Tm³⁺)微米棒(盘).通过X射线衍射(XRD),扫描电子显微镜(SEM),能量色散X射线荧光光谱(EDX),傅里叶变换红外(FTIR)光谱和激光光谱学等手段对所制备的系列β-NaYF₄微米棒(盘)进行了表征. XRD和SEM分析表明β-NaYF₄微米棒(盘)的长径比依赖于前驱液的pH值,随着前驱液的pH值的增加,从长棒逐渐过渡到六角盘.光谱测量结果表明:一系列NaYF₄:Tm³⁺微米晶体在656 nm脉冲激光选择激发下,均获得了强烈的单带近红外下转换荧光发射.系统研究了激发波长、环境温度和颗粒长径比对NaYF₄:Tm³⁺微米晶体中单带近红外荧光强度的调控.结果表明:颗粒长径比越大,荧光强度越强.进一步探索了颗粒长径比调控的荧光增强机理,并提出了基于长径比控制的缺陷空位机理.

关键词: NaYF₄:Tm³⁺, 选择激发, 下转换荧光, 颗粒长径比, 单带荧光发射

Abstract:

We synthesized Tm³⁺-doped NaYF₄ microcrystals with various length-to-diameter ratios by using a facile hydrothermal method assisted with sodium citrate from precursor solutions with various pH values. The β-NaYF₄:Tm³⁺ samples were characterized by using X-ray diffraction (XRD), scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), Fourier-transform infrared (FT-IR) spectroscopy, and photoluminescence spectroscopy. XRD and SEM show that as the pH of the precursor solutions increased, the morphology of the microcrystals changed from long rods to short microprisms to microplates. We also investigated the luminescence properties of the β-NaYF₄:Tm³⁺ hexagonal microdisks and microrods. By selectively exciting the NaYF₄:Tm³⁺ microcrystals with a 656-nm pulsed laser at a pulse duration of 10 ns, they exhibited a strong single-band down-conversion emission at 800 nm. We systematically studied how the excitation wavelength, temperature, and length-to-diameter ratio of the particles affected the luminescence intensity of their near-infrared (NIR) single-band emission. As the length-to-diameter ratio of the NaYF₄:Tm³⁺ microcrystals increased, their luminescence intensity strengthened. Exploring the reason for this luminescence enhancement, we propose a mechanism based on vacancy defects.

Key words: NaYF₄:Tm³⁺, Selective excitation, Down-conversion luminescence, Length to diameter ratio of particles, Single-band luminescence emission

MSC2000:

O644

徐春龙,王晋国,张翔宇. Tm³⁺掺杂的NaYF₄微米颗粒中强烈的单带下转换荧光发射[J]. 物理化学学报, 2015, 31(11): 2183-2190.

Chun-Long. XU,Jin-Guo. WANG,Xiang-Yu. ZHANG. Strong Single-Band Down-Conversion Emission in Tm³⁺-Doped NaYF₄ Microparticles[J]. Acta Phys. -Chim. Sin., 2015, 31(11): 2183-2190.

参考文献

1	1 Chen, X. Y.; Liu, Y. S.; Tu, D. T. Lanthanide-doped Luminescent Nanomaterials: from Fundamentals to Bioapplications; Springer-Verlag Press: Heidelberg, 2014; pp 125-187.
2	MacDougall S. K. W. ; Ivaturi A. ; Marques-Hueso J. ; Krä mer K. W. ; Richards B. S. Sol. Energy Mater. Sol. Cells 2014, 128, 18.
3	Chen G. Y. ; Qiu H. L. ; Prasad P. N. ; Chen X. Y. Chem. Rev 2014, 114 (10), 5161.
4	Zheng W. ; Tu D. T. ; Liu Y. S. ; Luo W. Q. ; Ma E. ; Zhu H. M. ; Chen X. Y. Scientia Sinica Chimica 2014, 44 (2), 168.
4	郑伟; 涂大涛; 刘永升; 罗文钦; 马恩; 朱浩淼; 陈学元. 中国科学:化学, 2014, 44 (2), 168.
5	Wang F. ; Banerjee D. ; Liu Y. S. ; Chen X. Y. ; Liu X. G. Analyst 2010, 135 (8), 1839.
6	Ge X. Y. ; Yuan Q. J. Wuhan Univ. (Nat. Sci. Ed.) 2015, 61, 10.
6	葛雪莹; 袁荃. 武汉大学学报:理学版, 2015, 61, 10.
7	Hampl J. ; Hall M. ; Mufti N. A. ; Yao Y. M. ; MacQueen D. B. ; Wright W. H. ; Cooper D. E. Anal. Biochem 2001, 288 (2), 176.
8	Zou W. Q. ; Visser C. ; Maduro J. A. ; Pshenichnikov M. S. ; Hummelen J. C. Nat. Photonics 2012, 6 (8), 560.
9	Xie X. J. ; Liu X. G. Nat. Mater 2012, 11 (10), 842.
10	Kumar R. A. ; Arivanandhan M. ; Hayakawa Y. Progress in Crystal Growth and Characterization of Materials 2013, 59 (3), 113.
11	Karaveli S. ; Zia R. Phys. Rev. Lett 2011, 106 (19), 193004.
12	Wang F. ; Liu X. Accounts Chem. Res 2014, 47 (4), 1378.
13	Lu Q. ; Hou Y. ; Tang A. ; Wu H. ; Teng F. Appl. Phys. Lett 2013, 102 (23), 233103.
14	Gao D. ; Zhang X. ; Gao W. J. Appl. Phys 2012, 111 (3), 033505.
15	Tian D. P. ; Gao D. L. ; Chong B. ; Liu X. Z. Dalton Trans 2015, 44 (9), 4133.
16	Deng T. L. ; Yan S. R. ; Hu J. G. Acta Phys. -Chim. Sin 2014, 30 (4), 773.
16	邓陶丽; 闫世润; 胡建国. 物理化学学报, 2014, 30 (4), 773.
17	Zhang X. Y. ; Li L. ; Gao D. L. ; Zheng H. R. Spectrosc. Spect. Anal 2009, 29, 2738.
17	张翔宇; 李林; 高当丽; 郑海荣. 光谱学与光谱分析, 2009, 29, 2738.
18	Nasim H. ; Jamil Y. Optics & Laser Technology 2014, 56, 211.
19	Wu J. ; Yao Z. ; Zong J. ; Jiang S. Opt. Lett 2007, 32 (6), 638.
20	Zheng L. J. ; Li Y. X. ; Liu H. L. ; Xu W. ; Zhang Z. G. Acta Phys. Sin 2013, 62 (24), 240701.
20	郑龙江; 李雅新; 刘海龙; 徐伟; 张治国. 物理学报, 2013, 62 (24), 240701.
21	Zhang X. Y. ; Gao D. L. ; Zheng H. R. Chin. Phys. B 2008, 17 (11), 4328.
22	Gao D. L. ; Tian D. P. ; Xiao G. Q. ; Chong B. ; Yu G. H. ; Pang Q. Opt. Lett 2015, 40 (15), 3580.
23	Krämer K. W. ; Biner D. ; Frei G. ; Güdel H. U. ; Hehlen M. P. ; Lüthi S. R. Chem. Mater 2004, 16 (7), 1244.
24	Gao D. L. ; Gao W. ; Shi P. ; Li L. RSC Adv 2013, 3 (34), 14757.
25	Gao D. L. ; Zhang X. Y. ; Zheng H. R. ; Shi P. ; Li L. ; Ling Y. W. Dalton Trans 2013, 42 (5), 1834.
26	Yi G. ; Lu H. ; Zhao S. ; Ge Y. ; Yang W. ; Chen D. ; Guo L. H. Nano Lett 2004, 4 (11), 2191.
27	Gao D. ; Zhang X. ; Gao W. ACS Appl. Mater. Interfaces 2013, 5 (19), 9732.
28	Zhang X. Y. ; Gao D. L. ; Li L. J. Appl. Phys 2010, 107 (12), 123528.
29	Gao D. L. ; Zhang X. Y. ; Zhang Z. L. ; Xu L. M. ; Lei Y. ; Zheng H. R. Acta Phys. Sin 2009, 58 (9), 6108.
29	高当丽; 张翔宇; 张正龙; 徐良敏; 雷瑜; 郑海荣. 物理学报, 2009, 58 (9), 6108.
30	Gao D. L. ; Zheng H. R. ; Tian Y. ; Cui M. ; Lei Y. ; He E. J. ; Zhang X. S. J. Nanosci. Nanotech 2010, 10 (11), 7694.
31	Miyakawa T. ; Dexter D. L. Phys. Rev. B 1970, 1 (7), 2961.
32	Liu G. K. Chem. Soc. Rev 2015, 44 (6), 163.
33	Zhang, S. Y. Spectroscopy of Rare Earth Ions: Spectral Property and Spectral Theory; Science Press: Beijing, 2008; pp 138-153.
33	张思远.稀土离子的光谱学:光谱性质和光谱理论.北京:科学出版社, 2008: 138-153.
34	Fu J. X. ; Fu X. H. ; Wang C. M. ; Yang X. F. ; Zhuang J. L. ; Zhang G. G. ; Lai B. Y. ; Wu M. M. ; Wang J. ; Eur. J. Inorg. Chem 2013, 2013 (8), 1269.
35	Wu Z. ; Lin M. ; Liang S. ; Liu Y. ; Zhang H. ; Yang B. Part. Part. Syst. Charact 2013, 30 (4), 311.

[1]	靳治良, 李彦兵, 郝旭强. Ni,Co基硒化物修饰g-C₃N₄光催化产氢研究[J]. 物理化学学报, 0, (): 1912033 -0 .
[2]	刘阳, 郝旭强, 胡海强, 靳治良. 构建NiS₂/MoSe₂ S型异质结高效光催化产氢[J]. 物理化学学报, 2021, 37(6): 2008030 -0 .
[3]	李嘉碧, 吴熙, 刘升卫. 表面氟化TiO₂空心光催化剂制备及其应用[J]. 物理化学学报, 2021, 37(6): 200903038 -0 .
[4]	吴进, 刘京, 夏雾, 任颖异, 王锋. 基于CdS和CdSe纳米半导体材料的可见光催化二氧化碳还原研究进展[J]. 物理化学学报, 2021, 37(5): 2008043 -0 .
[5]	秦祖赠, 吴靖, 李斌, 苏通明, 纪红兵. 光催化CO₂还原的超薄层状催化剂[J]. 物理化学学报, 2021, 37(5): 2005027 -0 .
[6]	王嘉鑫, 沈威力, 胡锦宁, 陈军, 李晓明, 曾海波. 激光作用铅卤钙钛矿的机理与应用[J]. 物理化学学报, 2021, 37(4): 2008051 -0 .
[7]	赵娜, 彭静, 王建平, 翟茂林. 羧酸根功能化的PVP-CdS同质结及其高效的光催化析氢性能[J]. 物理化学学报, 0, (): 2004046 -0 .
[8]	樊晔, 曹崇梅, 方云, 夏咏梅. 自交联共轭亚油酸囊泡基荧光纳米点的构筑及其荧光特性[J]. 物理化学学报, 0, (): 2002032 -0 .
[9]	李小为,王彬,尹文轩,狄俊,夏杰祥,朱文帅,李华明. Cu²⁺改性g-C₃N₄光催化剂的光催化性能[J]. 物理化学学报, 2020, 36(3): 1902001 -0 .
[10]	李倩, 丁平平, 王亚平, 廖学品, 石碧. 稀土-天然皮革可穿戴X射线防护材料的合成及性能[J]. 物理化学学报, 0, (): 2001046 -0 .
[11]	秦妍妍, 佘鹏飞, 郭颂, 黄晓萌, 刘淑娟, 赵强, 黄维. 四卤化锰(Ⅱ)配合物的结构调控及力致发光性能[J]. 物理化学学报, 2020, 36(1): 1907078 -0 .
[12]	黄彦捷, 连超, 周瑾艳, 黄梓宸, 康晓红, 黄振宇, 李小菁, 陈玲, 关妍. 由蚕砂制备的碳量子点在不同激发、pH、金属离子、温度及极性环境下的荧光性质研究[J]. 物理化学学报, 2019, 35(11): 1267 -1275 .
[13]	王士昭, 李维军, 俞越, 刘进, 张诚. 具有聚集诱导发光特性的新型铂(Ⅱ)金属配合物及其光激发的自敏化氧化反应[J]. 物理化学学报, 2019, 35(11): 1276 -1281 .
[14]	黄靖, 王丹阳, 李淑花, 范红, 范楼珍. 红色荧光碳量子点用于肿瘤微酸环境诊断[J]. 物理化学学报, 0, (): 1905067 -0 .
[15]	李家意,丁一,张卫,周鹏. 基于二维材料及其范德瓦尔斯异质结的光电探测器[J]. 物理化学学报, 2019, 35(10): 1058 -1077 .

Tm³⁺掺杂的NaYF₄微米颗粒中强烈的单带下转换荧光发射

Strong Single-Band Down-Conversion Emission in Tm³⁺-Doped NaYF₄ Microparticles

RichHTML

PDF

赞

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

Metrics

本文评价

推荐阅读 0