Synthesis of LiNi1/3Co1/3Mn1/3O2 Cathode Material by Eutectic Molten Salt LiOH-LiNO3

CHANG Zhao-Rong; CHEN Zhong-Jun; WU Feng; TANG Hong-Wei; ZHU Zhi-Hong   

  1. College of Chemistry and Environmental Science, Henan Normal University, Xinxiang 453007, Henan Province, P. R. China; College of Chemical Engineering and Environmental, Beijing Institute of Technology, Beijing 100080, P. R. China
  • Received:2007-09-07 Revised:2007-12-18 Published:2008-03-10
  • Contact: WU Feng E-mail:wufeng863@vip.sina.com

Abstract: The powder of LiNi1/3Co1/3Mn1/3O2 were prepared directly without artificial grinding and washing by a eutectic molten-salt mixture (0.38LiOH·H2O-0.62LiNO3) method. According to this method, the eutectic molten-salt mixture was self-mixed with precursor thoroughly at low temperature, and then sintered at a certain temperature. The tap-density of the powder obtained was 2.87 g·cm-3. The well-layered 琢-NaFeO2 structure and regular morphology were confirmed by X-ray diffraction (XRD) and scanning electronmicroscopy (SEM).XPSstudies showed that the predominant oxidation states of Ni, Co, andMn in the compound were 2+, 3+, and 4+, respectively. Cathodic behaviour was examined by charge-discharge cycling. The synthesized powder showed a reversible capacity of 160 mAh·g -1 at a specific current of 0.2C in the rang 3.0-4.3 V up to 50 cycles without noticeable capacity-fading.

Key words: Eutectic molten salt, Cathode material, XPS, LiNi1/3Co1/3Mn1/3O2