Acta Physico-Chimica Sinica  2007, Vol. 23 Issue (06): 861-866    DOI: 10.3866/PKU.WHXB20070613
Article     
Hydrogen Chemisorption on the Ru(0001) Surface
CHEN Xin; CHEN Wen-Bin; SHANG Xue-Fu; TAO Xiang-Ming; DAI Jian-Hui; TAN Ming-Qiu

Department of Physics, Zhejiang University, Hangzhou 310027, P. R. China

Download:   PDF(457KB) Export: BibTeX | EndNote (RIS)      

Abstract  

The influence of hydrogen contamination on the atomic geometry of Ru(0001) surface was studied by using the density-functional theory and the projector-augmented wave (PAW) method. Based on the optimized structural parameters of hcp Ru from the PAWtotal energy calculation, the surface relaxation, surface energy, and work function of clean Ru(0001) surface were calculated in the same way. The adsorption geometries and total energies of several coverages of hydrogen on Ru(0001) surface including p(1×1), p(1×2), (3^(1/2)×3^(1/2))R30°, and p(2×2), were studied for the hcp and fcc site absorptions combined with the both sites occupation in p(1×1) structure. These results suggested that the Ru(0001) p(1×1)-H geometry had the largest energy gain among all these conformations, so under the condition of low coverage and low H2 pressure, the most possible conformation was p(1×1)-H adsorption. The shrink of Ru(0001) surface with H contamination was -3.7%fromavailable experiments and this work yields -1.11%for hcp and -1.55% for fcc adsorption geometries. It was deduced that the most possible adsorption configuration for a hydrogen contaminated Ru(0001) surface was a mixture of hcp and fcc adsorptions. For a clean Ru(0001) surface the surface contraction was calculated to be near -3.9%, while the experimental measurement predicted -1.9%. This observation implied that even for a“clean”Ru (0001) surface there was still about 13.6%of surface area covered with hydrogen adsorption. These results reflected that the hydrogen contamination could affect the Ru(0001) surface structure dramatically. Furthermore the present study could yield a conclusion naturally that the shrink of the Ru(0001) surface would be reduced with the increase of H atomadsorption below 1.0 ML (monolayer).



Key wordsRu(0001) surface      Hydrogen chemisorption      Surface contamination     
Received: 29 November 2006      Published: 26 April 2007
MSC2000:  O641  
Corresponding Authors: TAN Ming-Qiu     E-mail: mqtan@zju.edu.cn
Cite this article:

CHEN Xin; CHEN Wen-Bin; SHANG Xue-Fu; TAO Xiang-Ming; DAI Jian-Hui; TAN Ming-Qiu. Hydrogen Chemisorption on the Ru(0001) Surface. Acta Physico-Chimica Sinica, 2007, 23(06): 861-866.

URL:

http://www.whxb.pku.edu.cn/Jwk_wk/wlhx/10.3866/PKU.WHXB20070613     OR     http://www.whxb.pku.edu.cn/Jwk_wk/wlhx/Y2007/V23/I06/861

[1] Li Xin-Sheng,Sheng Shi-Shan,Chen Heng-Rong,Ji Chun-Xin,Zhang Yao-Jun,Xin Qin. Reduction Effects of the Passivated Mo2N Studied by XPS and H2 Chemisorption[J]. Acta Physico-Chimica Sinica, 1995, 11(08): 678-680.