Acta Phys. -Chim. Sin. ›› 2000, Vol. 16 ›› Issue (02): 180-183.doi: 10.3866/PKU.WHXB20000216

• Note • Previous Articles     Next Articles

Structure Characterization of the Supported Amorphous Ni-B/SiO2 Catalysts

Zhang Xiao-Xin, Ma Ai-Zeng, Mu Xu-Hong, Min En-Ze, Huang Xiao-Xi, Wang Rong   

  1. Research Institute of Petroleum Processing,Beijing 100083;University of Science Technology Beijing,Beijing 100083
  • Received:1999-03-29 Revised:1999-06-24 Published:2000-02-15
  • Contact: Zhang Xiao-Xin

PDF (PC)

3005

Like

Abstract:

Amorphous Ni-B/SiO2 catalysts were prepared by chemical reduction of Ni2＋with KBH4. ICP was used to analyze the composition of alloys. XRD,TEM,SAED and HREM were used to examine the structures of samples fresh and after thermal treatment in different atmospheres. The results indicated that the supported NiB has a higher structural stability than ultrafine NiB amorphous alloy. Low temperature pretreatment in hydrogen can reduce nickel oxide on the surface of catalysts. However, treatment in hydrogen is more favorable than in atmosphere and nitrogen for keeping it in stable state.

Key words: Ni-B amorphous catalyst, Crystallization, Structure characterization