Acta Phys Chim Sin >> 2006,Vol.22>> Issue(05)>> 584-589     doi: 10.3866/PKU.WHXB20060514         中文摘要
Synthesis of TiO2/[[gamma]]r-Al2O3 and Effect of CuO Loading on NO Reduction
LI Hui-Juan;JIANG Xiao-Yuan;ZHENG Xiao-Ming
Institute of Catalysis, Faculty of Science, Zhejiang University, Hangzhou 310028, P. R. China
Full text: PDF (281KB) Export: BibTeX | EndNote (RIS)
TiO2/[alpha]-Al2O3 was prepared with TiCl4 as starting material, and the catalytic activities of CuO/TiO2/[alpha]-Al2O3 were examined using a GC micro-reactor NO+CO reaction system. The catalysts, especially 12%CuO/TiO2/[alpha]-Al2O3,showed high activities in NO+CO reaction. The NO conversion temperatures(T100%) were 300C[deg]and 275C[deg]for the catalysts pretreated by air and H2, respectively. The structural and reduction properties of CuO/TiO2/[alpha]-Al2O3 catalysts were analyzed using the H2-TPR, XRD, and FT-IR methods. It was found that proper amount of TiO2 increased the CuO dispersion on TiO2/[deg]-Al2O3. The 12%CuO/TiO2/[alpha]-Al2O3 catalyst had four reduction peaks ([alpha], [beta],[gamma] , and [delta]). The [alpha] and [deg]peaks were attributed to the reductions of highly dispersed CuO and crystalline CuO on the exposed TiO2 of TiO2 / [alpha]-Al2O3, respectively. On the other hand, the [beta] and [gamma]peaks were attributed to the reductions of highly dispersed CuOand crystalline CuOon TiO2/[alpha]-Al2O3, respectively. H2-pretreated 12%CuO/15%TiO2/[alpha]-Al2O3 had a strong adsorption of NO and CO, N2O and NO2 were formed. When NO and CO were adsorbed by 12%CuO/15%TiO2/[alpha]-Al2O3 the peak temperatures of N2O absorption were 200[deg]and 150C[deg] for the catalysts pretreated by air and H2, respectively.

Keywords: 12%CuO/15%TiO2/[alpha]-Al2O3   NO+CO reaction   CO、NO and NO+CO adsorption   FT-IR  
Received: 2005-11-01 Accepted: 2005-12-28 Publication Date (Web): 2006-04-28
Corresponding Authors: JIANG, Xiao-Yuan Email: xyjiang@mail.hz.zj.cn


Cite this article: LI Hui-Juan;JIANG Xiao-Yuan;ZHENG Xiao-Ming. Synthesis of TiO2/[[gamma]]r-Al2O3 and Effect of CuO Loading on NO Reduction[J]. Acta Phys. -Chim. Sin., 2006,22 (05): 584-589.    doi: 10.3866/PKU.WHXB20060514
Copyright © 2006-2016 Editorial office of Acta Physico-Chimica Sinica
Address: College of Chemistry and Molecular Engineering, Peking University, Beijing 100871, P.R.China
Service Tel: +8610-62751724 Fax: +8610-62756388 Email:whxb@pku.edu.cn
^ Top