Acta Phys. -Chim. Sin. ›› 2003, Vol. 19 ›› Issue (05): 398-402.doi: 10.3866/PKU.WHXB20030504

• ARTICLE • Previous Articles     Next Articles

Synthesis and Luminescent Properties of Tb-doped SiO2-B2O3-NaF Glass

Wang Xi-Gui;Wu Hong-Ying;Weng Shi-Fu;Wu Jin-Guang   

  1. Department of Chemistry, Inner Mongolia Normal University, Huhhot 010022;State Key Laboratory of Rare Earth Materials Chemistry and Application, College of Chemistry and Molecular Engineering, Peking University, Beijing 100871
  • Received:2002-08-29 Revised:2002-10-28 Published:2003-05-15
  • Contact: Wang Xi-Gui

Abstract: Tb-doped SiO2-B2O3-NaF glass was prepared by sol-gel process,using tetraethoxy silcane, boric acid and sodium fluoride as precursors,0.10 mol•L-1 TbCl3 solution as the dopant. The luminescent properties of Tb3+ doped SiO2-B2O3-NaF phosphors were investigated. The phosphors showed prominent luminescence in green, due to the electronic transition of 5D4—7F5 (Tb3+).For all Tb3+ concentrations used the emission spectrum was essentially the same with the exception of intensity and weak peak belonging to transition from 5D3 was detected in lower Tb3+ doped samples and lower annealing temperature samples. The intensity of emission from 5D3 quenches with increasing of the Tb3+ concentration and annealing temperature. The observation showed that cross-relaxation obviously took place in the transition 5D3-5D47F6—7F0 and/or 5D3—7F07F6—5D4.The excitation spectra of Tb3+ emission in SiO2-B2O3-NaF glass consist of broad bands with a maximum at about 230 nm, corresponding to 4f 8—4f 75d 1 transition of Tb3+ ion, and a series of sharp lines in the range of 300 to 380 nm which belong to transitions between the energy levels of the 4f 8 configuration. The structural characterization of these luminescent materials were carried by using XRD and TEM. The results showed that the phosphor was in amorphous phase.

Key words: Tb3+, Luminescent property, SiO2-B2O3-NaF glass