Electrochemical Behavior and Micro Adhesive Force Characteristic of Corrosion Inhibition Film

QU Jun-E; GUO Xing-Peng; ZHANG Jin-Zhi; CAI Shi-Gan   

  1. School of Chemistry and Chemical Engineering, Hubei University, Wuhan 430062, P. R. China; School of Chemistry and Chemical Engineering, Huazhong University of Science and Technology, Wuhan 430074, P. R. China; Hubei Key Laboratory of Materials Chemistry &Service Failure, Wuhan 430074, P. R. China
  • Received:2008-02-25 Revised:2008-03-24 Published:2008-08-06
  • Contact: QU Jun-E E-mail:chuchulily@163.com

PDF

2362

Like

Abstract: Traditional electrochemical testing technology and atomic force microscopy (AFM) force curve measurement were performed to research the adsorption behavior of corrosion inhibition film on dodecanethiol/gold electrode and sodiumdodecyl sulfate (SDS)/aluminumelectrode systems. The results showed that the corrosion inhibitor layer obtained at different concentrations presented different micro adhesive force characteristics, being associated with the changing regularity of the electrodes’ electrochemical behavior. The research demonstrated that AFM force curve technology was a successful way to investigate the adsorption behavior of corrosion inhibition film.

Key words: Corrosion inhibition film, Electrochemical behavior, AFM force curve, Adhesive force