Facile Preparation of Hollow Hydroxyapatite Microspheres

LIU Ying, ZHAO Xu, PAN Yan, ZHAO Jing-Zhe, WANG Zi-Chen   

  1. College of Chemistry, Jilin University, Changchun 130012, P. R. China|School of Chemistry and Chemical Engineering, Hunan University, Changsha 410082, P. R. China
  • Received:2008-12-09 Revised:2009-03-27 Published:2009-06-26
  • Contact: ZHAO Jing-Zhe, WANG Zi-Chen E-mail:wangzc@jlu.edu.cn; zhaojz@hun.cn

Abstract:

Without anyorganic additives andmetal ions, hollowhydroxyapatite (HAp)microsphereswere successfully synthesized using hollow CaCO3 microspheres and Na2HPO4 as reactants. The hollow microspheres were characterized by scanning electron microscopy (SEM), field emission scanning electron microscope (FESEM) and X-ray diffraction (XRD). The results showed that the as-prepared HAp was hollow microspheres with diameter of 2-4 μm and were composed of many needle-like particles of 40-60 nm in diameter and 80-200 nm in length. The effects of synthesis conditions, such as reaction temperature, were studied. Furthermore, the reaction temperature has an important influence on the morphology of the hollow HAp microspheres. Based on this result, the formation mechanism of hollow HAp microspheres was discussed preliminarily.

Key words: Hydroxyapatite, Calciumcarbonate, Hollow microsphere