Ce4+替代Pu4+的模拟固化体(Gd1-xCex)2Zr2O7+x的合成及结构演变

doi:10.3866/PKU.WHXB201304013

摘要/Abstract

摘要：

Gd₂Zr₂O₇中Gd具有很大的中子吸收截面, 其烧绿石结构-缺陷萤石结构的转变能较低, 使其成为理想的核废料固化基材. 使用硝酸盐为原料, 添加少量NaF作助熔剂, 在较低温度下(和传统高温固相反应相比), 合成了烧绿石型Gd₂Zr₂O₇. 以Ce⁴⁺模拟Pu⁴⁺, 研究了Gd₂Zr₂O₇对锕系核素的固化, 并合成了系列模拟固化体(Gd_1-xCe_x)₂Zr₂O_7+x (0≤x≤0.6). 采用粉末X射线衍射(XRD)对系列样品进行了表征. 结果表明: 随着x值的增大,样品从烧绿石结构向缺陷萤石结构转变, 且晶胞大小基本保持恒定, 但当x=0.6时, 衍射峰明显宽化, 晶格畸变比较严重, 晶格稳定性降低. 当x=1时, 即用Ce⁴⁺完全取代Gd³⁺进行合成, 不能得到Ce₂Zr₂O₈, 产物发生了相分离, 为四方结构的(Zr_0.88Ce_0.12)O₂和萤石结构的(Ce_0.75Zr_0.25)O₂的混合物. 模拟固化体的浸出率测试表明: 当x≤0.2时, 各元素浸出率均很低, 但当x≥0.4时, 各元素的浸出率明显升高, 说明以Gd₂Zr₂O₇作为固化Pu⁴⁺的基材, Pu⁴⁺掺入量不宜高于40%.

关键词: 核废料固化, Ce⁴⁺替代Pu⁴⁺, 烧绿石结构, 缺陷萤石结构, 结构演变

Abstract:

Gd₂Zr₂O₇ is a well known host for nuclear waste immobilization because of the high neutron absorption cross section of Gd and low energy transformation between ordered pyrochlore and disordered defect-fluorite structures. Pyrochlore Gd₂Zr₂O₇ was synthesized at relatively low temperature (compared with traditional high temperature solid-state reaction) using Gd(NO₃)₃·nH₂O, Zr(NO₃)₄·nH₂O as a starting material and a small amount of NaF as fluxing agent. Ce⁴⁺ was used as an analogue for Pu⁴⁺ and its immobilization behavior in Gd₂Zr₂O₇ was studied in a series of solidified forms comprising (Gd_1-xCe_x)₂Zr₂O_7+x (0≤x≤0.6). Powder X-ray diffraction (XRD) data showed that the sample structure transformed from pyrochlore to defect-fluorite type with increasing x but maintained constant unit cell volumes. As x was increased to 0.6, the diffraction peaks showed broadening, suggesting considerable lattice distortion. When x=1, i.e., all Gd³⁺ are placed by Ce⁴⁺, the product was not Ce₂Zr₂O₈, but a phase separated mixture of tetragonal (Zr_0.88Ce_0.12)O₂ and an ideal fluorite (Ce_0.75Zr_0.25)O₂. Leach rate measurements indicated that the leach rate of Gd³⁺, Zr⁴⁺, Ce⁴⁺ was low when x≤0.2, but increased significantly when x≥0.4. This suggests that the substitution rate of Pu⁴⁺ for Gd³⁺ should not be more than 40% when Gd₂Zr₂O₇ used as the host matrix for Pu⁴⁺.

Key words: Immobilization of nuclear waste, Surrogate of Ce⁴⁺ for Pu⁴⁺, Pyrochlore structure, Defect fluorite structure, Structure transformation

赵培柱, 李林艳, 徐盛明, 张覃. Ce⁴⁺替代Pu⁴⁺的模拟固化体(Gd_1-xCe_x)₂Zr₂O_7+x的合成及结构演变[J]. 物理化学学报, 2013, 29(06), 1168-1172. doi: 10.3866/PKU.WHXB201304013

ZHAO Pei-Zhu, LI Lin-Yan, XU Sheng-Ming, ZHANG Qin. Synthesis and Structural Transformations of (Gd_1-xCe_x)₂Zr₂O_7+x: An Analogue for Pu Immobilization[J]. Acta Phys. -Chim. Sin. 2013, 29(06), 1168-1172. doi: 10.3866/PKU.WHXB201304013

链接本文: https://www.whxb.pku.edu.cn/CN/10.3866/PKU.WHXB201304013

https://www.whxb.pku.edu.cn/CN/Y2013/V29/I06/1168

参考文献

(1) Moriga, T.; Yoshiasa, A.; Kanamaru, F.; Koto, K.; Yoshimura,M.; Somiya, S. Solid State Ionics 1989, 31 (4), 319.doi: 10.1016/0167-2738(89)90472-4
(2) Nyman, H.; Andersson, S.; Hyde, B. G.; O'Keeffe, M. J. SolidState Chem. 1978, 26, 123." target=_blank>10.1016/0167-2738(89)90472-4
(2) Nyman, H.; Andersson, S.; Hyde, B. G.; O'Keeffe, M. J. SolidState Chem. 1978, 26, 123.
(3) Raison, P. E.; Haire, R. G.; Sato, T.; Ogawa, T. Mater. Res. Symp.Proc. 1999, 556, 3. doi: 10.1557/PROC-556-3
(4) Kulkarni, N. K.; Sampath, S.; Venugopal, V. J. Nucl. Mater.2000, 281, 248. doi: 10.1016/S0022-3115(00)00336-6
(5) Li, H. J.; Chen, G.; Li, Z. H.; Zhou, C. Acta Phys. -Chim. Sin.2007, 23 (5), 761. [李鸿建, 陈刚, 李中华, 周超. 物理化学学报, 2007, 23 (5), 761.] doi: 10.3866/PKU.WHXB20070527
(6) Qu, Z. X.;Wan, C. L.; Pan,W. Chem. Mater. 2007, 19 (20),4913. doi: 10.1021/cm071615z
(7) Wu, D. C. Chinese Journal of Nuclear Science and Engineering1992, 12 (3), 280. [吴德昌. 核科学与工程, 1992, 12 (3), 280.]" target=_blank>10.1557/PROC-556-3
(4) Kulkarni, N. K.; Sampath, S.; Venugopal, V. J. Nucl. Mater.2000, 281, 248. doi: 10.1016/S0022-3115(00)00336-6
(5) Li, H. J.; Chen, G.; Li, Z. H.; Zhou, C. Acta Phys. -Chim. Sin.2007, 23 (5), 761. [李鸿建, 陈刚, 李中华, 周超. 物理化学学报, 2007, 23 (5), 761.] doi: 10.3866/PKU.WHXB20070527
(6) Qu, Z. X.;Wan, C. L.; Pan,W. Chem. Mater. 2007, 19 (20),4913. doi: 10.1021/cm071615z
(7) Wu, D. C. Chinese Journal of Nuclear Science and Engineering1992, 12 (3), 280. [吴德昌. 核科学与工程, 1992, 12 (3), 280.]
(8) Wang, S. X.;Wang, L. M.; Ewing, R. C.; Kutty, K. V. G. Nucl.Instrum. Methods Phys. Res. Sec. B 2000, 169 (1-4), 135.doi: 10.1016/S0168-583X(00)00030-6
(9) Wang, S. X.; Begg, B. D.;Wang, L. M.; Ewing, R. C.;Weber,W. J.; Kutty, K. V. G. J. Mater. Res. 1999, 14 (12), 4470.doi: 10.1557/JMR.1999.0606
(10) Weber,W. J.; Ewing, R. C. Science 2000, 289, 2051. doi: 10.1126/science.289.5487.2051
(11) Stefanovsky, S. V.; Yudintsev, S. V.; Livshits, T. S. Mater. Sci.Eng. 2010, 9, 012001." target=_blank>10.1016/S0168-583X(00)00030-6
(9) Wang, S. X.; Begg, B. D.;Wang, L. M.; Ewing, R. C.;Weber,W. J.; Kutty, K. V. G. J. Mater. Res. 1999, 14 (12), 4470.doi: 10.1557/JMR.1999.0606
(10) Weber,W. J.; Ewing, R. C. Science 2000, 289, 2051. doi: 10.1126/science.289.5487.2051
(11) Stefanovsky, S. V.; Yudintsev, S. V.; Livshits, T. S. Mater. Sci.Eng. 2010, 9, 012001.
(12) Cleave, A.; Grimes, R.; Sickafus, K. Philos. Mag. 2005, 85 (9),967. doi: 10.1080/14786430412331314672
(13) Ewing, R. C.;Weber,W. J.; Lian, J. J. Appl. Phys. 2004, 95,5949. doi: 10.1063/1.1707213
(14) Lu, X. R.; Dong, F. Q.; Hu, S.;Wang, X. L.;Wu, Y. L. ActaPhys. Sin. 2012, 61 (15), 152401-1. [卢喜瑞, 董发琴, 胡淞,王晓丽, 吴彦霖. 物理学报, 2012, 61 (15), 152401-1.]doi: 10.7498/aps.61.152401
(15) Zhong, Y. H.; Tang, J. Y.; Mao, X. L.; Lu, X. R.; Yang, Y. S.Journal of Southwest University of Science and Tchnology 2011,26 (2), 10. [钟宇宏, 唐敬友, 毛雪丽, 卢喜瑞, 杨玉山. 西南科技大学学报, 2011, 26 (2), 10.]" target=_blank>10.1080/14786430412331314672
(13) Ewing, R. C.;Weber,W. J.; Lian, J. J. Appl. Phys. 2004, 95,5949. doi: 10.1063/1.1707213
(14) Lu, X. R.; Dong, F. Q.; Hu, S.;Wang, X. L.;Wu, Y. L. ActaPhys. Sin. 2012, 61 (15), 152401-1. [卢喜瑞, 董发琴, 胡淞,王晓丽, 吴彦霖. 物理学报, 2012, 61 (15), 152401-1.]doi: 10.7498/aps.61.152401
(15) Zhong, Y. H.; Tang, J. Y.; Mao, X. L.; Lu, X. R.; Yang, Y. S.Journal of Southwest University of Science and Tchnology 2011,26 (2), 10. [钟宇宏, 唐敬友, 毛雪丽, 卢喜瑞, 杨玉山. 西南科技大学学报, 2011, 26 (2), 10.]
(16) Reid, D. P.; Stennett, M. C.; Hyatt, N. C. J. Solid State Chem.2012, 191, 2. doi: 10.1016/j.jssc.2011.12.039
(17) Patwe, S. J.; Ambekar, B. R.; Tyagi, A. K. J. Alloy. Compd.2005, 389 (1-2), 243. doi: 10.1016/j.jallcom.2004.06.094
(18) Jantzen, C. M.; Bibler, N. E.; Beam, D. C.; Ramsey,W. G.;Waters, B. J. Standard Test Method Relative to Durability ofNuclear Waste Glasses: the Product Consistency Test (PCT),Version 5.0, 1991." target=_blank>10.1016/j.jssc.2011.12.039
(17) Patwe, S. J.; Ambekar, B. R.; Tyagi, A. K. J. Alloy. Compd.2005, 389 (1-2), 243. doi: 10.1016/j.jallcom.2004.06.094
(18) Jantzen, C. M.; Bibler, N. E.; Beam, D. C.; Ramsey,W. G.;Waters, B. J. Standard Test Method Relative to Durability ofNuclear Waste Glasses: the Product Consistency Test (PCT),Version 5.0, 1991.
(19) Wang, G. B.;Wang, Y. J.; Zhao, X. Q.; Song, B. J. ActaPhys. -Chim. Sin. 2005, 21 (5), 84. [王桂斌, 王延吉, 赵新强,宋宝俊. 物理化学学报, 2005, 21 (5), 84.] doi: 10.3866/PKU.WHXB20050117
(20) Chen, R.; Gong, Y. J.; Li, Q.; Dou, T.; Zhao, Z.; Xu, Q. H. ActaPhys. -Chim. Sin. 2009, 25 (3), 539. [陈然, 巩雁军, 李强,窦涛, 赵震, 徐庆虎. 物理化学学报, 2009, 25 (3), 539.]doi: 10.3866/PKU.WHXB20090323
(21) Subramanian, M. A.; Sleight, A.W. Handbook on the Physicsand Chemistry of Rare Earths; Elsevier Science Publishers:Oxford, UK, 1993; Vol. 16, pp 225-240." target=_blank>10.3866/PKU.WHXB20050117
(20) Chen, R.; Gong, Y. J.; Li, Q.; Dou, T.; Zhao, Z.; Xu, Q. H. ActaPhys. -Chim. Sin. 2009, 25 (3), 539. [陈然, 巩雁军, 李强,窦涛, 赵震, 徐庆虎. 物理化学学报, 2009, 25 (3), 539.]doi: 10.3866/PKU.WHXB20090323
(21) Subramanian, M. A.; Sleight, A.W. Handbook on the Physicsand Chemistry of Rare Earths; Elsevier Science Publishers:Oxford, UK, 1993; Vol. 16, pp 225-240.
(22) Perez-Y-Jorba, M. Ann. Chim. 1962, 7, 479. (23) Subramanian, M. A.; Aravamudan, G.; Rao, G. V. S. Prog.Solid State Chem. 1983, 15, 55. doi: 10.1016/0079-6786(83)90001-8
(24) Mandal, B. P.; Shukla, R.; Achary, S. N.; Tyagi, A. K. Inorg.Chem. 2010, 49, 10415. doi: 10.1021/ic1018482
(25) McCullough, J. D.; Britton, J. D. J. Am. Chem. Soc. 1952, 74,5225." target=_blank>10.1016/0079-6786(83)90001-8
(24) Mandal, B. P.; Shukla, R.; Achary, S. N.; Tyagi, A. K. Inorg.Chem. 2010, 49, 10415. doi: 10.1021/ic1018482
(25) McCullough, J. D.; Britton, J. D. J. Am. Chem. Soc. 1952, 74,5225.
(26) Ringwood, A. E.; Kesson, S. E.; Reeve, K. D.; Levins, D. M.;Ramm, E. J. Radioactive Waste Forms for the Future; ElsevierScience: Amersterdam, 1988; pp 233-234. (27) Icenhower, J. P.;Weber,W. J.; Hess, N. J.; Thevuthasen, S.;Begg, B.; McGrail, P.; Rodriguez, E. A.; Steele, J. L.; Geiszler,K. N. Scientific Basis for Nuclear Waste Management XXVI;Material Research Society: Pittsburgh, 2003; pp 23-30.

[1]	张昊,李新刚,蔡金孟,王亚婷,武墨青,丁彤,孟明,田野. 氢氟酸加入量对钛基半导体结构演变及光催化性能的影响[J]. 物理化学学报, 2017, 33(10): 2072 -2081 .
[2]	刘姗姗,季姗,陈启斌,彭昌军,刘洪来. 超分子聚合物刷PVP-Chol表面图案化及其力诱导的可逆结构转变[J]. 物理化学学报, 2016, 32(9): 2318 -2326 .
[3]	夏祥来,李林艳,郭放,苏伟,刘艳,陈晓谋,潘社奇. Pu在Gd₂Zr₂O₇基质中的模拟固化: (Gd_1-xCe_x)₂Zr₂O_7+x的热物理性能研究[J]. 物理化学学报, 2015, 31(9): 1810 -1814 .
[4]	李鸿建;陈刚;李中华;周超. 烧绿石结构La₂Ti_2-xCo_xO₇的制备及可见光分解水性能[J]. 物理化学学报, 2007, 23(05): 761 -764 .

Ce⁴⁺替代Pu⁴⁺的模拟固化体(Gd_1-xCe_x)₂Zr₂O_7+x的合成及结构演变

Synthesis and Structural Transformations of (Gd_1-xCe_x)₂Zr₂O_7+x: An Analogue for Pu Immobilization

PDF

赞

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 4

Metrics

推荐阅读 0