Abstract:

The formation of polymer film of propargyl alcohol(PA) and its protective ability against corrosion in Fe/H_2SO_4 and Fe/H_2SO_4+H_2S systems have been investigated using impedance measurement. The composition and morphology of the corrosion surface of iron, on which PA polymerized at different bines, were obtained with the aid of SEM and AFM as well as EDX. The results showed that PA polymerized into compact polymer film in Fe/H_2SO_4 and Fe/ H_2SO_4 + H_2S systems, which made iron surface smooth and have a morphologies of regular square structure in microscopic level. In Fe/H_2SO_4 system, macroscopic continuous polymer film of PA was not formed leading to local corrosion on electrode surface. In Fe/H_2SO_4 +H_2S system, the adsorption of H_2S and HS - on electrode surface slowed down the formation of polymer film of PA. However, the iron sulfide, produced after a longer time, increased the continuity of the polymer film of PA and therefore, the polymer film could perform its long-te...更多rm inhibition action.

Key words: Polymer film of PA;H₂S, Fe/H₂SO₄, Inhibition effect