Study of Organic Silicon Protection Film by Magnetic-Controlling Plasma Polymerization on the Y-Ba-Cu-O Superconductor

Wang Rui,Jin Xin-Yu,Cheng Kang-Sheng,Liang Su-Zhen   

  1. Department of Information and Electronics,Zhejiang University,Hangzhou 310027
  • Received:1996-05-22 Revised:1996-06-21 Published:1996-09-15
  • Contact:

PDF

2800

Like

Abstract:

A new method of deposition of organic silicon film by magnetic-controlling plasma polymerization was used to protect Y-Ba-Cu-O superconductor from corrosion. The deposition rate of plasma polymer film with magnetic-controlling is 20 times over that without magnetic-controlling. The relation between the deposition rate of film and the process factors of magnetic-controlling plasma were studied. The Y-Ba-Cu-O superconductor covered with organic silicon film was formed by magnetic-controlling plasma polymerization had been protected from corrosion in water over 48 hours.

Key words: Magnetic-controlling plasma polymerization, Y-Ba-Cu-O superconductor, Organic silicon protective film