锂金属电池用高浓度电解液体系研究进展

吴晨, 周颖, 朱晓龙, 詹忞之, 杨汉西, 钱江锋

Research Progress on High Concentration Electrolytes for Li Metal Batteries

Chen Wu, Ying Zhou, Xiaolong Zhu, Minzhi Zhan, Hanxi Yang, Jiangfeng Qian

表2 基于局部高浓度电解液(LHCEs)的锂金属电池性能对比表

Table 2 Compassion of the cycling performance of Li metal batteries based on localized-high concentration electrolytes (LHCEs).

Dilute	Electrolyte	Li metal battery	Cycling Performance	Ref.
HFE	LiTFSI-G4/HFE(1 : 1 : 4)	Li//S	85% @ 100^th	51
	1 mol·L^-1 LiPF₆ FEC/FEMC/HFE	Li//NMC811	90% @ 400^th	56
	1 mol·L^-1 LiPF₆ FEC/FEMC/HFE	Li// LiCoPO₄	93% @ 1000^th	56
	1 mol·L^-1 LiPF₆ FEC/FEMC/HFE + 2% LiDFOB	Li//LiNiO₂	80% @ 400^th	57
	1 mol·L^-1 LiPF₆ + 0.02 mol·L^-1 LiDFOB-FEC/FDEC/HFE	Li //LiCoMnO₄	80% @ 1000^th	58
	1.2 mol·L^-1 LiPF₆ FEC/DMC/HFE + 0.15 mol·L^-1 LiDFOB	Li//LiCoO₂	84% @ 300^th	59
	1.28 mol·L^-1 LiFSI-FEC/FEMC/HFE	Li //NCA	90% @4 50^th (-20 ℃)	60
BTFE	1.2 mol·L^-1 LiFSI-DMC/BTFE	Li//NCM333	80% @ 700^th	52
	1.2 mol·L^-1 LiFSI-TEP/BTFE	Li//NCM622	97% @ 600^th	53
TTE	LiFSI-1.2 DME/3TTE	Li//NCM811	90% @ 250^th	61
	LiFSI-3TMS/3TTE	Li//NCM111	80% @ 150^th	55
OFE	1 mol·L^-1 LiFSI-95OFE/5DME	Li//S	60% @ 150^th	62
1, 2-dfBen	2 mol·L^-1 LiFSI-DMC/1, 2-dfBen	Li//NCM523	82% @ 140^th	63