The Preparation of Poly(ophenylenediamine) Sarin Acid Imprinting Nanometer Layer and Its Structural Characterization

Zuo Yan-Jun;Yu Jian-Hua;Huang Qi-Bin;Zhao Jian-Jun;Pan Yong;Lin Yuan   

  1. The Institute of Chemical Defence, Beijing 102205; 1The Center of Molecular Science, Institute of Chemistry, Chinese
  • Received:2002-10-31 Revised:2003-01-13 Published:2003-06-15
  • Contact: Huang Qi-Bin E-mail:Qibinhuang@sohu.com

Abstract: The poly(ophenylenediamine) molecularly imprinting nanometer layer with high sensitivity to phosphorus agent sarin has been prepared by electropolymerization. Quartz crystal microbalance verifies the existence of molecularly imprinting. Cyclovoltammetry,atomic force microscope and Xray photoelectron spectroscopy have been used to characterize these films. The results show that the layer thickness is only 20 nm,and the film surface is hollowprotruding, lax and has many holes. XPS further certifies that molecularly imprinting mostly influence the threedimension arrangement of polymers, but the chemical composition of polymers does not change. The poly(ophenylenediamine) molecularly imprinting nanometer layers have wide application foreground on the selective detection to the nerve agent sarin.

Key words: Molecularly imprinting techonology, Electropolymerization, Sarin(GB)