聚苯胺-还原氧化石墨烯复合材料的比电容及超级电容性能

doi:10.3866/PKU.WHXB201705182

摘要/Abstract

摘要：

通过同步还原聚苯胺（PANI）-氧化石墨烯（GO）复合物制备得到了聚苯胺-还原氧化石墨烯（PANI-rGO）。由于复合材料中PANI提供了氧化还原反应的电荷，使得PANI-rGO复合材料具有较大的比电容。通过扫描电子显微镜（SEM），紫外-可见光谱和热重量分析法（TGA）对复合物进行了结构和形态的分析。复合材料的形态呈薄片状，聚苯胺是均匀地包裹在氧化石墨烯上的。当电流密度为20 A·g^-1时，PANI-rGO复合材料的比电容可高达1069 F·g^-1（1.71 F·cm^-2），是PANI-GO复合材料的五倍，这是因为复合材料中还原氧化化石墨烯的大比表面和高电导性所引起的。

关键词: 聚苯胺-还原氧化石墨烯, 聚苯胺-氧化石墨烯, 比电容, 操作电压

Abstract:

Flaky polyaniline-reduced graphene oxide (PANI-rGO) composites have larger specific capacitance due to the improved redox charge of PANI in the composites, fabricated by simultaneous reduction of PANI-GO. The structural and morphological analyses were carried out using scanning electron microscopy, UV-Vis spectroscopy, and thermogravimetry. The results showed that the composites are flaky in shape. PANI is uniformly coated on GO, and PANI-rGO has specific capacitance as high as 1069 F·g^-1 (1.71 F·cm^-2) at a current density of 20 A·g^-1, 5 times higher than PANI-GO; this is caused by the large surface and conductivity of the rGO in the composite.

Key words: Polyaniline-reduced graphene oxide, Polyaniline-graphene oxide, Specific capacitance, Operating voltage

曾向东,赵晓昱,韦会鸽,王彦飞,唐娜,沙作良. 聚苯胺-还原氧化石墨烯复合材料的比电容及超级电容性能[J]. 物理化学学报, 2017, 33(10), 2035-2041. doi: 10.3866/PKU.WHXB201705182

Xiang-Dong ZENG,Xiao-Yu ZHAO,Hui-Ge WEI,Yan-Fei WANG,Na TANG,Zuo-Liang SHA. Specific Capacitance and Supercapacitive Properties of Polyaniline-Reduced Graphene Oxide Composite[J]. Acta Phys. -Chim. Sin. 2017, 33(10), 2035-2041. doi: 10.3866/PKU.WHXB201705182

链接本文: https://www.whxb.pku.edu.cn/CN/10.3866/PKU.WHXB201705182

https://www.whxb.pku.edu.cn/CN/Y2017/V33/I10/2035

参考文献

1	Geim A. K. ; Novoselov K. S. Nature Mater. 2007, 6, 183.
2	Novoselov K. S. ; Geim A. K. ; Morozov S. V. ; Jiang D. ; Zhang Y. ; Dubonos S. V. ; Grigorieva I. V. ; Firsov A. A. Science 2004, 306, 666.
3	Ghosh D. ; Giri S. ; Dhibar S. ; Das C. K. Electrochim. Acta 2014, 147, 557.
4	Mishra A. K. ; Ramaprabhu S. J.Phys. Chem. C 2011, 115, 14006.
5	Yan J. ; Wei T. ; Shao B. ; Fan Z. J. ; Qian W. Z. ; Zhang M. L. ; Wei F. Carbon 2010, 48, 487.
6	Hao Q. ; Xia X. ; Lei W. ; Wang W. ; Qiu J. Carbon 2015, 81, 552.
7	Wang H. ; Hao Q. ; Yang X. ; Lu L. ; Wang X. Nanoscale 2010, 2, 2164.
8	Conway B. E. ; Pell W. G. J.Solid State Electrochem. 2003, 7, 637.
9	Rauda I. E. ; Augustyn V. ; Dunn B. ; Tolbert S. H. Acc. Chem.Res. 2013, 46, 1113.
10	Wang Z. L. ; He X. J. ; Ye S. H. ; Tong Y. X. ; Li G. R. ACSAppl. Mater. Interfaces 2014, 6, 642.
11	Lu X. F. ; Chen X. Y. ; Zhou W. ; Tong Y. X. ; Li G. R. ACSAppl. Mater. Interfaces 2015, 7, 14843.
12	Simon P. ; Gogotsi Y. ; Dunn B. Science 2014, 343, 1210.
13	Augustyn V. ; Simon P. ; Dunn B. Energy Environ. Sci. 2014, 7, 1597.
14	Wu Q. ; Xu Y. ; Yao Z. ; Liu A. ; Shi G. ACS Nano 2010, 4, 1963.
15	Tan Y. T. ; Ran F. ; Kong L. B. ; Liu J. ; Kang L. Synth. Met. 2012, 162, 114.
16	Wang H. Z. ; Gao C. X. ; Zhang P. ; Yao S. W. ; Zhang W. G. Acta Phys. -Chim. Sin. 2013, 29, 117.
16	王宏智; 高翠侠; 张鹏; 姚素薇; 张卫国. 物理化学学报, 2013, 29, 117.
17	Wang L. L. ; Xing R. G. ; Zhang B. W. ; Hou Y. ActaPhys. -Chim. Sin. 2014, 30, 1659.
17	汪丽丽; 邢瑞光; 张邦文; 侯渊. 物理化学学报, 2014, 30, 1659.
18	Orata D. ; Buttry D. A. J.Am. Chem. Soc. 1987, 109, 3574.
19	Kumar N. A. ; Choi H. J. ; Shin Y. R. ; Chang D. W. ; Dai L. ; Baek J. B. ACS Nano 2012, 6, 1715.
20	Zhang K. ; Zhang L. L. ; Zhao X. S. ; Wu J. Chem. Mater. 2010, 22, 1392.
21	Lindfors T. ; Latonen R. M. Carbon 2014, 69, 122.
22	Co?kun E. ; Zaragoza-Contreras E. A. ; Salavagione H. J. Carbon 2012, 50, 2235.
23	Shulga Y. M. ; Baskakov S. A. ; Abalyaeva V. V. ; Efimov O.N. ; Shulga N. Y. ; Michtchenko A. ; Lartundo-Rojas L. ; Moreno L. A. ; Cabanas-Moreno J. G. ; Vasilets V. N. J.PowerSources 2013, 224, 195.
24	Zhang W. L. ; Park B. J. ; Choi H. J. Chem. Commun. 2010, 46, 5596.
25	Luo Z. H. ; Zhu L. H. ; Zhang H. Y. ; Tang H. Q. Mater. Chem.Phys. 2013, 139, 572.
26	Zhang Q. ; Li Y. ; Feng Y. ; Feng W. Electrochim. Acta 2013, 90, 95.
27	Xu G. ; Wang N. ; Wei J. ; Lv L. ; Zhang J. ; Chen Z. ; Xu Q. Ind. Eng. Chem. Res. 2012, 51, 14390.
28	Xu D. ; Xu Q. ; Wang K. ; Chen J. ; Chen Z. ACS Appl. Mater.Interfaces 2013, 6, 200.
29	Meng Y. ; Wang K. ; Zhang Y. ; Wei Z. Adv. Mater. 2013, 25, 6985.
30	Xu J. ; Wang K. ; Zu S. Z. ; Han B. H. ; Wei Z. ACS Nano 2010, 4, 5019.
31	Huang W. S. ; MacDiarmid A. G. Polymer 1993, 34, 1833.
32	Blinova N. V. ; Sapurina I. ; Klimovi? J. ; Stejskal J. Polym.Degrad. Stabil. 2005, 88, 428.
33	Stejskal J. ; Kratochvíl P. ; Helmstedt M. Langmuir 1996, 12, 3389.
34	Ghosh P. ; Siddhanta S. K. ; Chakrabarti A. Eur. Polym. J. 1999, 35, 699.
35	Sulimenko T. ; Stejskal J. ; Krivka I. ; Prokes J. Eur. Polym. J. 2001, 37, 219.
36	Somani P. R. Mater. Chem. Phys. 2003, 77, 81.
37	Abu Y. M. ; Aoki K. Electrochim. Acta 2005, 50, 3634.
38	Chen J. ; Zeng X. ; Aoki K. J. ; Nishiumi T. InternationalJournal of Chemistry 2015, 7, 1.
39	Vallés C. ; Jiménez P. ; Mu?oz E. ; Benito A. M. ; Maser W. K. J.Phys. Chem. C 2011, 115, 10468.
40	Choi E. Y. ; Han T. H. ; Hong J. H. ; Kim J. E. ; Lee S. H. ; Kim H. W. ; Kim S. O. J.Mater. Chem. 2010, 20, 1907.
41	Paredes J. I. ; Villar-Rodil S. ; Solis-Fernandez P. ; Martinez-Alonso A. ; Tascon J. M. Langmuir 2009, 25, 5957.
42	Stankovich S. ; Dikin D. A. ; Piner R. D. ; Kohlhaas K. A. ; Kleinhammes A. ; Jia Y. ; Wu Y. ; Nguyen S. T. ; Ruoff R. S. Carbon 2007, 45, 1558.
43	McAllister M. J. ; Li J. L. ; Adamson D. H. ; Schniepp H. C. ; Abdala A. A. ; Liu J. ; Herrera-Alonso M. ; Milius D. L. ; Car R. ; Prud'homme R. K. ; Aksay I. A. Chem. Mater. 2007, 19, 4396.
44	Zhang H. ; Yu H. M. ; Xu C. H. ; Zhang M. H. ; Pan X. H. ; Gao Y. F. Acta Phys -Chim. Sin. 2016, 32, 1634.
44	张恒; 于惠梅; 徐朝和; 张明辉; 潘秀红; 高彦峰. 物理化学学报, 2016, 32, 1634.
45	Stejskal J. ; Kratochvíl P. ; Radhakrishnan N. Synth. Met. 1993, 61, 225.
46	Stejskal J. ; Sapurina I. ; Trchová M. Prog. Polym. Sci. 2010, 35, 1420.
47	Wang P. C. ; Huang Z. ; MacDiarmid A. G. Synth. Met. 1999, 101, 852.
48	Mazur M. ; Predeep P. Polymer 2005, 46, 1724.
49	Tong Z. ; Yang Y. ; Wang J. ; Zhao J. ; Su B. L. ; Li Y. J.Mater. Chem. A 2014, 2, 4642.
50	Li H. L. ; Wang J. X. ; Chu Q. X. ; Wang Z. ; Zhang F. B. ; Wang S. C. J.Power Sources 2009, 190, 578.
51	Zhu C. ; Guo S. ; Fang Y. ; Dong S. ACS Nano 2010, 4, 2429.
52	Guo H. L. ; Wang X. F. ; Qian Q. Y. ; Wang F. B. ; Xia X. H. ACS Nano 2009, 3, 2653.
53	Yang X. H. ; Xie Q. J. ; Yao S. Z. Synth. Met. 2004, 143, 119.
54	O'Neil G. D. ; Weber A. W. ; Buiculescu R. ; Chaniotakis N.A. ; Kounaves S. P. Langmuir 2014, 30, 9599.
55	Yang W. Z. ; Widenkvist E. ; Jansson U. ; Grennberg H. New J. Chem. 2011, 35, 780.
56	O'Neill A. ; Khan U. ; Nirmalraj P. N. ; Boland J. ; Coleman J.N. J.Phys. Chem. C 2011, 115, 5422.
57	Gogotsi Y. ; Simon P. Science 2011, 334, 917.
58	Fan W. ; Zhang C. ; Tjiu W. W. ; Pramoda K. P. ; He C. ; Liu T. ACS Appl. Mater. Interfaces 2013, 5, 3382.
59	Aoki K. ; Cao J. A. ; Hoshino Y. Electrochim. Acta 1993, 38, 1711.
60	Aoki K. ; Kawase M. J.Electroanal. Chem. 1994, 377, 125.

[1]	陈阳, 张梓澜, 隋志军, 刘芝婷, 周静红, 周兴贵. 氢氧化镍纳米线/三维石墨烯复合材料的制备及其电化学性能[J]. 物理化学学报, 2015, 31(6): 1105 -1112 .
[2]	汪建德, 彭同江, 孙红娟, 侯云丹. 水热反应温度对三维还原氧化石墨烯的形貌、结构和超级电容性能的影响[J]. 物理化学学报, 2014, 30(11): 2077 -2084 .
[3]	申保收, 冯旺军, 郎俊伟, 王儒涛, 邰志新, 阎兴斌. 电弧放电法制备石墨烯的硝酸改性及其电化学性能增强[J]. 物理化学学报, 2012, 28(07): 1726 -1732 .
[4]	李钊, 徐菊良, 李旭晏, 郭丽芳, 李劲, 蒋益明. 基于双相不锈钢制备超级电容器电极材料MnO₂[J]. 物理化学学报, 2011, 27(06): 1424 -1430 .
[5]	孔德帅, 王建明, 皮欧阳, 邵海波, 张鉴清. 纳米多孔结构镍基复合膜电极的电化学法制备及其电容特性[J]. 物理化学学报, 2011, 27(04): 764 -768 .
[6]	张雷勇, 何水剑, 陈水亮, 郭乔辉, 侯豪情. 聚苯胺/碳纳米纤维复合材料的制备及电容性能[J]. 物理化学学报, 2010, 26(12): 3181 -3186 .
[7]	王涛, 何建平, 张传香, 周建华, 郭云霞, 陈秀, 狄志勇, 孙盾, 王道军. 有序介孔C/NiO复合材料的合成及其电化学性能[J]. 物理化学学报, 2008, 24(12): 2314 -2320 .
[8]	刘亚菲;胡中华;许琨;郑祥伟;高强. 活性炭电极材料的表面改性和性能[J]. 物理化学学报, 2008, 24(07): 1143 -1148 .
[9]	陈宏;陈劲松;周海晖;焦树强;陈金华;旷亚非. 纳米纤维聚苯胺在电化学电容器中的应用[J]. 物理化学学报, 2004, 20(06): 593 -597 .
[10]	刘献明;张以河;张校刚;付绍云. Ni-Ru复合氧化物的超电容特性研究[J]. 物理化学学报, 2004, 20(04): 417 -420 .