关键词: CO₂还原制甲醇, Cu-ZnO催化剂, 硅酸铜, Cu-ZnO协同效应

Abstract:

Cu-ZnO is broadly used as a catalyst in CO₂ reduction to produce methanol, but fabricating small-sized Cu-ZnO catalysts with strong Cu-ZnO interactions remains a challenge. In this work, a simple, low-cost method is proposed to synthesize small-sized Cu-ZnO/SiO₂ with high activity and controllable Cu-ZnO interactions derived from copper silicate nanotubes. A series of Cu-ZnO/SiO₂ samples with different amounts of ZnO were prepared. The activities of the as-prepared catalysts for methanol synthesis were tested, and the results revealed a volcano relationship with the weight fraction of ZnO. At 523 K, the methanol selectivity increased from 20% to 67% when 14% ZnO was added to the Cu/SiO₂ catalyst, while the conversion of CO₂ increased first and then decreased with the addition of ZnO. The optimum space time yield (STY) of 244 g·kg^-1·h^-1 was obtained on C-SiO₂-7%ZnO at 543 K under 4.5 MPa H₂/CO₂. Furthermore, the synergistic effect of Cu and ZnO was studied by high resolution transmission electron microscopy (HRTEM), powder X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), in situ diffuse-reflectance infrared Fourier transform spectroscopy (DRIFTS), and temperature-programmed reduction (TPR) analyses. The HRTEM images showed that the Cu particles come in contact with ZnO more frequently with increased addition of ZnO, indicating that the catalysts with higher ZnO contents have a greater probability of formation of the Cu-ZnO interface, which promotes the catalytical activity of Cu-ZnO/SiO₂. Meanwhile, the HRTEM images, XRD patterns, and TPR results showed that the addition of excess ZnO leads to an increase in the size of the Cu particles, which in turn decreases the total number of active sites and further degrades the activity of the catalysts. The activation energy (E_a) for methanol synthesis and reverse water gas shift (RWGS) was calculated based on the results of the catalytical test. With the addition of ZnO, E_a for methanol synthesis decreased from 72.5 to 34.8 kJ·mol^-1, while that for RWGS increased from 61.3 to 102.7 kJ·mol^-1, illustrating that ZnO promotes the synergistic effect of Cu-ZnO. The results of XPS and in situ DRIFTS showed that the amount of Cu⁺ species decreases with the addition of ZnO, indicating that the Cu-ZnO interface serves as the active site. The Cu surface area and the turnover frequency (TOF) of methanol were calculated based on the H₂-TPR curves. The TOF of methanol on the Cu-ZnO/SiO₂ catalysts at 543 K increased from 1.5 × 10^-3 to 3.9 × 10^-3 s^-1 with the addition of ZnO, which further confirmed the promotion effect of the Cu-ZnO interface on the methanol synthesis. This study provides a method to construct Cu-ZnO interfaces based on copper silicate and to investigate the influence of ZnO on Cu-ZnO/SiO₂ catalysts.

Key words: CO₂ reduction to methanol, Cu-ZnO catalyst, Copper silicate, Cu-ZnO synergistic effect