Synthesis of Ordered Conducting Polymer Ultrathin Film and Its Application as Hole Injection Layer for Organic Light-Emitting Diode

XU Jian-Hua; YANG Ya-Jie; JIANG Ya-Dong; YU Jun-Sheng   

  1. State Key Laboratory of Electronic Thin Films & Integrated Devices, School of Optoelectronic Information, University of Electronic Science and Technology of China (UESTC), Chengdu 610054, P. R. China
  • Received:2008-09-03 Revised:2008-10-14 Published:2008-12-31
  • Contact: YANG Ya-Jie E-mail:jj_eagle@163.com

PDF

2820

赞

摘要： 采用修饰多层LB膜的方法制备了导电聚合物聚-3,4-乙烯二氧噻吩/二十烷酸(PEDOT:AA)复合层状有序膜, 构筑了一种导电聚合物镶嵌的多层有序膜结构. 将这种导电聚合物有序薄膜沉积于ITO电极表面, 将其作为有机电致发光二极管(OLED)的空穴注入层, 并研究了ITO/(PEDOT:AA)/MEH-PPV/Al器件的性能. 研究结果表明, 与采用聚3,4-乙烯二氧噻吩/聚苯乙烯磺酸(PEDOT:PSS)自组装膜和旋涂膜作为空穴注入层的ITO/(PEDOT:PSS)/MEH-PPV/Al器件相比, 器件的发光效率增加, 起亮电压降低. 我们认为这是由于PEDOT:AA薄膜提供了一种有序层状结构后, 减小了ITO与MEH-PPV间的接触势垒, 改善了空穴载流子注入效率. 进一步的研究表明, 由于PEDOT:AA多层膜间靠较弱的亲水、疏水作用结合, 这种导电多层有序膜的热稳定性与普通LB膜相似, 在较高温度下发生从层状有序态到无序态的变化, 这是导致OLED器件性能发生劣化的主要原因.

关键词: 导电聚合物, LB膜, OLED, 空穴注入层, 自组装膜

Abstract: A novel layer-ordered ultrathin film of poly(3,4-ethylene dioxythiophene)/arachidic acid (PEDOT:AA) was prepared by a modified Langmuir-Blodgett (LB) technique and an ordered conducting polymer embedded multilayer structure was constructed. The layer-ordered structure was deposited on an indium-tin oxide (ITO) surface as a hole injection layer for use as an organic light-emitting diode (OLED) and the luminance performance of the ITO/(PEDOT:PSS)/MEH-PPV(poly(2-methoxy-5-(2’-ethyl-hexyloxy)-1,4-phenylene-vinylene))/Al device was investigated. Compared with electrostatic self-assembly (ESA) and spin-coating the poly(3,4-ethylene dioxythiophene)/polystyrenesulfonate (PEDOT:PSS) film showed enhanced luminance efficiency. The higher luminance at an equivalent voltage and lower turn-on voltage was observed after the PEDOT:AA film was utilized as hole injection layer in OLED. The enhanced carrie injection efficiency was attributed to the good layer-ordered structure of PEDOT:AA film, which decreased the contact resistance between ITO and the emitting layer. Further investigation revealed that this layer-ordered conducting polymer film exhibited poor temperature stability because of weak hydrophilic and hydrophobic interactions between adjacent LB layers. These weak interactions result in the film structure changing from a layer-ordered structure into an unordered structure at higher temperatures.

Key words: Conducting polymer, Langmuir-Blodgett film, OLED, Hole injection layer, Self-assembly film