尿素作为造孔剂对聚乙烯支撑的PAMS聚合物电解质性能的改进

doi:10.3866/PKU.WHXB20110712

物理化学学报 >> 2011, Vol. 27 >> Issue (07): 1689-1694.doi: 10.3866/PKU.WHXB20110712

尿素作为造孔剂对聚乙烯支撑的PAMS聚合物电解质性能的改进

陈朗¹, 饶睦敏¹, 李伟善^1,2,3, 许梦清^1,2,3, 廖友好¹, 谭春林^1,2,3, 易金¹

1. 华南师范大学化学与环境学院, 广州 510006;
2. 广东高校电化学储能与发电技术重点实验室, 华南师范大学, 广州 510006;
3. 电化学储能材料与技术教育部工程研究中心, 华南师范大学, 广州 510006

收稿日期:2011-01-18 修回日期:2011-05-03 发布日期:2011-06-28
通讯作者: 李伟善 E-mail:liwsh@scnu.edu.cn
基金资助:
国家自然科学基金(20873046)和广东省自然科学基金(10351063101000001)资助项目

Performance Improvement of Polyethylene-Supported PAMS Electrolyte Using Urea as Foaming Agent

CHEN Lang¹, RAO Mu-Min¹, LI Wei-Shan^1,2,3, XU Meng-Qing^1,2,3, LIAO You-Hao¹, TAN Chun-Lin^1,2,3, YI Jin¹

1. School of Chemistry and Environment, South China Normal University, Guangzhou 510006, P. R. China;
2. Key Laboratory of Electrochemical Technology on Energy Storage and Power Generation of Guangdong Higher Education Institutes, South China Normal University, Guangzhou 510006, P. R. China;
3. Engineering Research Center of Materials and Technology for Electrochemical Energy Storage (MOE), South China Normal University, Guangzhou 510006, P. R. China

Received:2011-01-18 Revised:2011-05-03 Published:2011-06-28
Contact: LI Wei-Shan E-mail:liwsh@scnu.edu.cn
Supported by:
The project was supported by the National Natural Science Foundation of China (20873046) and Natural Science Foundation of Guangdong Province, China (10351063101000001).

摘要/Abstract

摘要：

采用乳液聚合法合成聚(丙烯腈-甲基丙烯酸甲酯-苯乙烯) (P(AN-MMA-ST)或者共聚物PAMS), 并利用尿素作为造孔剂制备了聚乙烯(PE)支撑的PAMS聚合物膜(PE-PAMS-U)及凝胶聚合物电解质(GPE). 利用傅里叶变换红外(FTIR)光谱、X射线衍射(XRD)、扫描电子显微镜(SEM)、热重(TG)分析、线性电位扫描(LSV)、电化学阻抗谱(EIS)以及充放电等方法对PAMS聚合物以及PE支撑的聚(丙烯腈-甲基丙烯酸甲酯-苯乙烯) (PE-PAMS)聚合物隔膜及凝胶聚合物电解质的性能进行了研究. 结果表明, 利用尿素作为造孔剂可以提高PE-PAMS凝胶聚合物的性能. 由于尿素的加入, 聚合物膜呈现均匀的微孔结构, 室温下的电导率从1.1×10^-3 S·cm^-1提高到2.15×10^-3 S·cm^-1. 同时, 锂电极/聚合物电解质界面上的电荷传递电阻也从480 Ω·cm²降低到 250 Ω·cm². 电化学稳定窗口为5.0 V. 电池(Li/PE支撑的GPE/LiCoO₂)的测试证明, 用尿素作为造孔剂的凝胶聚合物锂离子电池表现出优良的倍率性能和循环性能.

关键词: 锂离子电池, 凝胶聚合物电解质, 聚(丙烯腈-甲基丙烯酸甲酯-苯乙烯), 尿素, 造孔剂

Abstract:

Poly(acrylonitrile-methyl methacrylate-styrene) (PAMS) was synthesized by emulsion polymerization and a polyethylene (PE)-supported membrane was prepared using urea as foaming agent (PE-PAMS-U). The structure and performance of the PAMS copolymer, PE-PAMS-U membrane and corresponding gel polymer electrolyte (GPE) were characterized by Fourier transform infrared (FTIR) spectroscopy, scanning electron microscopy (SEM), X-ray diffraction (XRD), thermogravimetry (TG), linear sweep voltammetry (LSV), electrochemical impedance spectroscopy (EIS) and by a charge/discharge test. We found that the performance of the PE-PAMS-U based GPE could be improved when using urea as a foaming agent. With the use of urea the pore size of the membrane becomes uniform, the ionic conductivity of the GPE improves from 1.1×10^-3 to 2.15×10^-3 S·cm^-1 at room temperature and the interfacial resistance between the GPE and lithium is reduced from 480 to 250 Ω·cm². The GPE is stable up to 5.0 V (vs Li/Li⁺) at room temperature and the battery made using the Li/PE-supported GPE/LiCoO₂ shows a good rate and good cycle performance.

Key words: Lithium ion battery, Gel polymer electrolyte, Poly((acrylonitrile-methyl methacrylate-styrene), Urea, Foaming agent

陈朗, 饶睦敏, 李伟善, 许梦清, 廖友好, 谭春林, 易金. 尿素作为造孔剂对聚乙烯支撑的PAMS聚合物电解质性能的改进[J]. 物理化学学报, 2011, 27(07): 1689-1694.

CHEN Lang, RAO Mu-Min, LI Wei-Shan, XU Meng-Qing, LIAO You-Hao, TAN Chun-Lin, YI Jin. Performance Improvement of Polyethylene-Supported PAMS Electrolyte Using Urea as Foaming Agent[J]. Acta Phys. -Chim. Sin., 2011, 27(07): 1689-1694.

链接本文: https://www.whxb.pku.edu.cn/CN/10.3866/PKU.WHXB20110712

https://www.whxb.pku.edu.cn/CN/Y2011/V27/I07/1689

参考文献

(1) Liao, Y. H.; Zhou, D. Y.; Rao, M. M.; Li,W. S.; Cai, Z. P.; Liang, Y.; Tan, C. L. J. Power Sources 2009, 189, 139.
(2) Tarascon, J. M.; Armand, M. Nature 2001, 414, 359.
(3) Subba, C. V. R.;Wu, G. P.; Zhao, C. X.; Zhu, Q. Y.; Chen,W.; Kalluru Rajamohan, R. J. Non-Cryst. Solids 2007, 353, 440.
(4) Sundaram, N. T. K.; Subramania, A. J. Membr. Sci. 2007, 289, 1.
(5) Zuo, X. X.; Xu, M. Q.; Li,W. S.; Su, D. G.; Liu, J. S. Electrochem. Solid-State Lett. 2006, 9, A196.
(6) Jeon, J. D.; Kim, M. J.; Kwak, S. Y. J. Power Sources 2006, 162, 1304.
(7) Xie, H.; Tang, Z. Y.; Li, Z. Y.; He, Y. B.; Liu, Y.;Wang, H. J. Solid State Electrochem. 2008, 12, 1497.
(8) Chen-Yang, Y.W.; Chen, H. C.; Lin, F. J.; Chen, C. C. Solid State Ionics 2002, 150, 327.
(9) Pu,W. H.; He, X. M.;Wang, L.; Tian, Z.; Jiang, C. Y.;Wan, C. R. J. Membr. Sci. 2006, 280, 6.
(10) Zhang, G. Q.; Ma, L.;Wu, Z. J.; Zhang, H. Y.; Ni, P. Acta Phys. -Chim. Sin. 2009, 25, 555. [张国庆, 马莉, 吴忠杰, 张海燕, 倪佩. 物理化学学报, 2009, 25, 555.]
(11) Ahmad, A.; Rahman, M. Y. A.; Su'ait, M. S. Physica B 2008, 403, 4128.
(12) Reddy, C. V. S.; Zhu, Q. Y.; Mai, L. Q.; Chen,W. J. Solid State Electrochem. 2007, 11, 543.
(13) Stephan, A. M.; Nahm, K. S. Polymer 2006, 47, 5952.
(14) Kim, D.W.; Oh, B.; Park, J. H.; Sun, Y. K. Solid State Ionics 2000, 138, 41.
(15) Song, M. K.; Kim, Y. T.; Cho, J. Y.; Cho, B.W.; Popov, B. N.; Rhee, H.W. J. Power Sources 2004, 125, 10.
(16) Rao, M. M.; Liu, J. S.; Li,W. S.; Liao, Y. H.; Liang, Y.; Zhao, L. Z. J. Solid State Electrochem. 2010, 14, 255.
(17) Liao, Y. H.; Rao, M. M.; Li,W. S.; Tan, C. L.; Yi, J.; Chen, L. Electrochim. Acta 2009, 54, 6396.
(18) Liao, Y. H.; Rao, M. M.; Li,W. S.; Yang, L. T.; Zhu, B. K.; Xu, R.; Fu, C. H. J. Membr. Sci. 2010, 352, 95.
(19) Li, Z. H.; Cheng, C.; Zhan, X. Y.;Wu, Y. P.; Zhou, X. D. Electrochim. Acta 2009, 54, 4403.
(20) Rao, M. M.; Liu, J. S.; Li,W. S.; Liang, Y.; Zhou, D. Y. J. Membr. Sci. 2008, 322, 314.
(21) Liang, Y. H.;Wang, C. C.; Chen, C. Y. J. Power Sources 2005, 148, 55.
(22) Wang, Z. L.; Tang, Z. Y. Electrochim. Acta 2004, 49, 1063.
(23) Yang, M. J.; Li,W. L.;Wang, G. G.; Zhang, J. Q. Solid State Ionics 2005, 176, 2829.
(24) Liu, H. R.; Du, J. H. Solid State Sci. 2006, 8, 526.
(25) Zhang, H. P.; Zhang, P.; Li, Z. H.; Sun, M.;Wu, Y. P.;Wu, H. Q. Electrochem. Commun. 2007, 9, 1700.
(26) Yang, C. C. Mater. Lett. 2004, 58, 33.
(27) Miao, R. Y.; Liu, B.W.; Zhu, Z. Z.; Liu, Y.; Li, J. L.;Wang, X. D.; Li, F. Q. J. Power Sources 2008, 184, 420.
(28) Nookala, M.; Kumar, B.; Rodrigues, S. J. Power Sources 2002, 111, 165.
(29) Lee, Y. G.; Park, J. K.; Moon, S. I. Electrochim. Acta 2000, 46, 533.
(30) Chaix, N.; Alloin, F.; Bélières, J. P.; Saunier, J.; Sanchez, J. Y. Electrochim. Acta 2002, 47, 1327.
(31) Rao, M. M.; Liu, J. S.; Li,W. S.; Liang, Y.; Liao, Y. H.; Zhao, L. Z. J. Power Sources 2009, 189, 711.

[1]	鲁航语, 侯瑞林, 褚世勇, 周豪慎, 郭少华. 高比能锂离子电池层状富锂正极材料改性策略研究进展[J]. 物理化学学报, 2023, 39(7): 2211057 -0 .
[2]	汪茹, 刘志康, 严超, 伽龙, 黄云辉. 高安全锂离子电池复合集流体的界面强化[J]. 物理化学学报, 2023, 39(2): 2203043 -0 .
[3]	刘瑶钰, 王宇辰, 刘碧莹, Amer Mahmoud, 严凯. 钴钒水滑石纳米片用于电催化尿素氧化[J]. 物理化学学报, 2023, 39(2): 2205028 -0 .
[4]	朱思颖, 李辉阳, 胡忠利, 张桥保, 赵金保, 张力. 锂离子电池氧化亚硅负极结构优化和界面改性研究进展[J]. 物理化学学报, 2022, 38(6): 2103052 - .
[5]	杨越, 朱加伟, 王鹏彦, 刘海咪, 曾炜豪, 陈磊, 陈志祥, 木士春. 镶嵌于NH₂-MIL-125 (Ti)衍生氮掺多孔碳中的花状超细纳米TiO₂作为高活性和稳定性的锂离子电池负极材料[J]. 物理化学学报, 2022, 38(6): 2106002 - .
[6]	莫英, 肖逵逵, 吴剑芳, 刘辉, 胡爱平, 高鹏, 刘继磊. 锂离子电池隔膜的功能化改性及表征技术[J]. 物理化学学报, 2022, 38(6): 2107030 - .
[7]	吴锋, 李晴, 陈来, 王紫润, 陈刚, 包丽颖, 卢赟, 陈实, 苏岳锋. 高镍正极材料中钴元素的替代方案及其合成工艺优化[J]. 物理化学学报, 2022, 38(5): 2007017 - .
[8]	刘学伟, 牛莹, 曹瑞雄, 陈晓红, 商红岩, 宋怀河. 石墨烯包覆天然球形石墨作为锂离子电池的负极材料，是否需要乙炔黑导电剂？[J]. 物理化学学报, 2022, 38(2): 2012062 - .
[9]	丁晓博, 黄倩晖, 熊训辉. 锂离子电池快充石墨负极研究与应用[J]. 物理化学学报, 2022, 38(11): 2204057 - .
[10]	苏岳锋, 张其雨, 陈来, 包丽颖, 卢赟, 陈实, 吴锋. ZrO₂包覆高镍LiNi_0.8Co_0.1Mn_0.1O₂正极材料提高其循环稳定性的作用机理[J]. 物理化学学报, 2021, 37(3): 2005062 - .
[11]	张思东, 刘园, 祁慕尧, 曹安民. 表面限域掺杂提升高比能正极材料稳定性[J]. 物理化学学报, 2021, 37(11): 2011007 - .
[12]	叶耀坤, 胡宗祥, 刘佳华, 林伟成, 陈涛文, 郑家新, 潘锋. 锂离子电池正极材料中的极化子现象理论计算研究进展[J]. 物理化学学报, 2021, 37(11): 2011003 - .
[13]	安惠芳, 姜莉, 李峰, 吴平, 朱晓舒, 魏少华, 周益明. 基于水凝胶衍生的硅/碳纳米管/石墨烯纳米复合材料及储锂性能[J]. 物理化学学报, 2020, 36(7): 1905034 - .
[14]	李超, 沈明, 胡炳文. 面向金属离子电池研究的固体核磁共振和电子顺磁共振方法[J]. 物理化学学报, 2020, 36(4): 1902019 - .
[15]	史永超, 唐明学. 可充电池的磁共振研究[J]. 物理化学学报, 2020, 36(4): 1905004 - .

尿素作为造孔剂对聚乙烯支撑的PAMS聚合物电解质性能的改进

Performance Improvement of Polyethylene-Supported PAMS Electrolyte Using Urea as Foaming Agent

PDF

赞

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

Metrics

推荐阅读 0