五乙烯六胺修饰的MCF基吸附剂的制备及其CO2吸附性能研究

doi:10.3866/PKU.WHXB201304091

物理化学学报 >> 2013, Vol. 29 >> Issue (06): 1266-1272.doi: 10.3866/PKU.WHXB201304091

五乙烯六胺修饰的MCF基吸附剂的制备及其CO₂吸附性能研究

冯星星, 谢菁, 胡庚申, 贾爱平, 谢冠群, 罗孟飞

浙江师范大学物理化学研究所, 先进催化剂材料教育部重点实验室, 浙江金华 321004

收稿日期:2012-12-27 修回日期:2013-04-08 发布日期:2013-05-17
通讯作者: 胡庚申, 罗孟飞 E-mail:gshu@zjnu.edu.cn; mengfeiluo@zjnu.cn
基金资助:
国家自然科学基金(21203167)资助项目

Preparation of Pentaethylenehexamine-Functionalized Mesocellular Silica Foams and Their Application for CO₂ Adsorption

FENG Xing-Xing, XIE Jing, HU Geng-Shen, JIA Ai-Ping, XIE Guan-Qun, LUO Meng-Fei

Key Laboratory of the Ministry of Education for Advanced Catalysis Materials, Institute of Physical Chemistry, Zhejiang Normal University, Jinhua, Zhejiang 321004, China

Received:2012-12-27 Revised:2013-04-08 Published:2013-05-17
Supported by:
The project was supported by the National Natural Science Foundation of China (21203167).

摘要/Abstract

摘要：

以三嵌段共聚物P123 (EO₂₀-PO₇₀-EO₂₀)为模板剂合成了介孔泡沫氧化硅(MCF)材料. MCF经过五乙烯六胺(PEHA)修饰后用于捕捉CO₂. 采用扫描电镜(SEM)、透射电镜(TEM)、N2吸附-脱附、傅里叶变换红外(FTIR)光谱、热重分析(TGA)对MCF和MCF-PEHA进行了表征. 结果表明, PEHA对MCF改性后, 并没有破坏MCF载体本身的结构. MCF-PEHA的CO₂吸附量在75℃时达到最大. 随着PEHA含量的增加, MCF-PEHA的CO₂吸附量呈先增大后减小的趋势, 当PEHA含量为70% (w)时, CO₂吸附量达到最大, 为3.55 mmol·g^-1. 水汽促进了吸附剂的CO₂吸附性能. 研究结果还表明, MCF-70吸附剂经过四次吸脱附循环, 吸附性能基本保持不变, 表现出很好的可再生性能.

关键词: 介孔泡沫氧化硅, 五乙烯六胺, 吸附, CO₂

Abstract:

Mesocellular silica foam (MCF) was prepared using P123 (EO₂₀-PO₇₀-EO₂₀) as template and then functionalized with pentaethylenehexamine (PEHA) for CO₂ adsorption. The samples were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), nitrogen adsorptiondesorption isotherms, Fourier transform infrared (FTIR) spectroscopy and thermal gravimetric analysis (TGA). These results indicated that after modification with PEHA, the structure of the support itself was undamaged. The highest CO₂ adsorption capacity of MCF-PEHA was obtained at 75℃. With increasing PEHA loading, the CO₂ adsorption capacity increases and approached the highest adsorption capacity (3.55 mmol·g^-1) with a 70% (w) PEHA loading. Moisture improved the CO₂ adsorption performance of the adsorbents. Repeated adsorption-desorption cycling indicated that the sorbents maintained stable CO₂ adsorption capacity after 4 cycles, indicating potential for regeneration of the adsorbents.

Key words: Mesostructure cellar foam, Pentaethylenehexamine, Adsorption, CO₂

冯星星, 谢菁, 胡庚申, 贾爱平, 谢冠群, 罗孟飞. 五乙烯六胺修饰的MCF基吸附剂的制备及其CO₂吸附性能研究[J]. 物理化学学报, 2013, 29(06): 1266-1272.

FENG Xing-Xing, XIE Jing, HU Geng-Shen, JIA Ai-Ping, XIE Guan-Qun, LUO Meng-Fei. Preparation of Pentaethylenehexamine-Functionalized Mesocellular Silica Foams and Their Application for CO₂ Adsorption[J]. Acta Phys. -Chim. Sin., 2013, 29(06): 1266-1272.

链接本文: https://www.whxb.pku.edu.cn/CN/10.3866/PKU.WHXB201304091

https://www.whxb.pku.edu.cn/CN/Y2013/V29/I06/1266

参考文献

(1) Lee, S. S.; Mun, S. M.; Choi,W. J.; Min, B. M.; Cho, S.W.; Oh,K. J. J. Environ. Sci. 2012, 24, 897. doi: 10.1016/S1001-0742(11)60788-2
(2) Zhang, J.; Misch, R.; Tan, Y.; Agar, D.W. Chem. Eng. Technol.2011, 34, 1481. doi: 10.1002/ceat.v34.9
(3) Kemper, J.; Ewert, G.; Grünewald, M. Energy Procedia 2011, 4,232. doi: 10.1016/j.egypro.2011.01.046
(4) Du, M.; Feng, B.; An, H.; Liu,W.; Zhang, L. Korean J. Chem. Eng. 2012, 29, 362. doi: 10.1007/s11814-011-0184-4
(5) Chew, T. L.; Ahmad, L. A.; Bhatia, S. Adv. Colloid Interface Sci.2010, 153, 43. doi: 10.1016/j.cis.2009.12.001
(6) Wang, M.; Yang, D.;Wang, Z.;Wang, J.;Wang, S. Front. Chem. Eng. Chin. 2010, 4, 127. doi: 10.1007/s11705-009-0231-4
(7) Lee, S. C.; Choi, B. Y.; Lee, T. J.; Ryu, C. K.; Ahn, Y. S.; Kim,J. C. Catal. Today 2006, 111, 385. doi: 10.1016/j.cattod.2005.10.051
(8) Choi, S.; Drese, J. H.; Eisenberger, P. M.; Jones, C.W. Environ. Sci. Technol. 2011, 45, 2420. doi: 10.1021/es102797w
(9) Gray, M. L.; Hoffman, J. S.; Hreha, D. C.; Fauth, D. J.; Hedges,S.W.; Champagne, K. J.; Pennline, H.W. Energy Fuels 2009,23, 4840. doi: 10.1021/ef9001204
(10) Hu, G. S.; Zhu, L.; Jia, A. P.; Hu, X.; Lu, J. Q.; Luo, M. F. Appl. Spectrosc. 2012, 66, 122. doi: 10.1366/11-06466
(11) Wei, L.; Lan, R. K.; Jing, Y.; Gao, Z. M.;Wang, Y. D. Chem. Ind. Eng. Prog. 2011, 30, 143. [韦力, 蓝任凯, 靖宇, 高正明, 王运冬. 化工进展, 2011, 30, 143.]
(12) Xu, X.; Song, C.; Andresen, J. M.; Miller, B. G.; Scaroni, A.W.Energy Fuels 2002, 16, 1463. doi: 10.1021/ef020058u
(13) Ye, Q.; Zhang, Y.; Li, M.; Shi, Y. Acta Phys. -Chin.Sin. 2012, 28,1223. [叶青, 张瑜, 李茗, 施耀. 物理化学学报,2012, 28, 1223.] doi: 10.3866/PKU.WHXB201202234
(14) Belmabkhout, Y.; Serna-Guerrero, R.; Sayari, A. Ind. Eng. Chem. Res. 2010, 49, 359. doi: 10.1021/ie900837t
(15) Kim, S.; Ida, J.; Guliants, V. V.; Lin, J. Y. S. J. Phys. Chem. B2005, 109, 6287. doi: 10.1021/jp045634x
(16) Wang, L.; Ma, L.;Wang, A.; Liu, Q.; Zhang, T. Chin. J. Catal.2007, 28, 805. doi: 10.1016/S1872-2067(07)60066-7
(17) Zheng, F.; Tran, D. N.; Busche, B. J.; Fryxell, G. E.; Addleman,R. S.; Zemanian, T. S.; Aardahl, C. L. Ind. Eng. Chem. Res.2005, 44, 3099. doi: 10.1021/ie049488t
(18) Zelenak, V.; Halamova, D.; Gaberova, L.; Bloch, E.; Llewellyn,P. Microporous Mesoporous Mat. 2008, 116, 358. doi: 10.1016/j.micromeso.2008.04.023
(19) Knofel, C.; Descarpentries, J.; Benzaouia, A.; Zelenak, V.;Mornet, S.; Llewellyn, P. L.; Hornebecq, V. Microporous Mesoporous Mat. 2007, 99, 79. doi: 10.1016/j.micromeso.2006.09.018
(20) Serna-Guerrero, R.; Belmabkhout, Y.; Sayari, A. Chem. Eng. J.2010, 158, 513. doi: 10.1016/j.cej.2010.01.041
(21) Son,W. J.; Choi, J. S.; Ahn,W. S. Microporous Mesoporous Mat. 2008, 113, 31. doi: 10.1016/j.micromeso.2007.10.049
(22) Ma, X.;Wang, X.; Song, C. J. Am. Chem. Soc. 2009, 131, 5777.doi: 10.1021/ja8074105
(23) Qi, G.;Wang, Y.; Estevez, L.; Duan, X.; Anako, N.; Park, A. H.A. Energy Environ. Sci. 2011, 4, 444. doi: 10.1039/c0ee00213e
(24) Zhang, H. D. Mater. Rev. 2009, 23, 93. [张海东. 材料导报,2009, 23, 93.]
(25) Subagyono, D. J. N.; Liang, Z.; Knowles, G. P.; Chaffee, A. L.Chem. Eng. Res. Des. 2011, 89, 1647. doi: 10.1016/j.cherd.2011.02.019
(26) Zou, Z. C.;Wei, Q.; Na,W.; Sun, H.; Nei, Z. R. J. Inorg. Mater.2009, 24, 702. [邹泽昌, 韦奇, 纳薇, 孙慧, 聂祚仁. 无机材料学报, 2009, 24, 702.] doi: 10.3724/SP.J.1077.2009.00702
(27) Yan, X.; Zhang, L.; Zhang, Y.; Qiao, K.; Yan, Z.; Komarneni, S.Chem. Eng. J. 2011, 168, 918. doi: 10.1016/j.cej.2011.01.066
(28) Qi, G.; Fu, L.; Choi, B. H.; Giannelis, E. P. Energy Environ. Sci.2012, 5, 7368. doi: 10.1039/c2ee21394j
(29) Zhao, J.; Simeon, F.;Wang, Y.; Luo, G.; Hatton, T. A. RSC Adv.2012, 2, 6509. doi: 10.1039/c2ra20149f
(30) Feng, X. X.; Hu, G. S.; Hu, X.; Xie, G. Q.; Xie, Y. L.; Lu, J. Q.;Luo, M. F. Ind. Eng. Chem. Res. 2013, 52, 4221. doi: 10.1021/ie301946p
(31) Schmidt-Winkel, P.; Lukens,W.W.; Yang, P.; Margolese, D. I.;Lettow, J. S.; Ying, J. Y.; Stucky, G. D. Chem. Mater. 2000, 12,686. doi: 10.1021/cm991097v
(32) Harlick, P. J. E.; Sayari, A. Ind. Eng. Chem. Res. 2006, 45,3248. doi: 10.1021/ie051286p
(33) Franchi, R. S.; Harlick, P. J. E.; Sayari, A. Ind. Eng. Chem. Res.2005, 44, 8007. doi: 10.1021/ie0504194

[1]	王吉超, 乔秀, 史维娜, 贺景, 陈军, 张万庆. 多面体状Cu₂O修饰片状BiOI的S型异质结构筑及光催化水蒸气中CO₂转化性能研究[J]. 物理化学学报, 2023, 39(6): 2210003 -0 .
[2]	孙涛, 李晨曦, 鲍钰鹏, 樊君, 刘恩周. S-型MnCo₂S₄/g-C₃N₄异质结光催化产氢性能研究[J]. 物理化学学报, 2023, 39(6): 2212009 -0 .
[3]	张怡宁, 高明, 陈松涛, 王会琴, 霍鹏伟. Ag/CN/ZnIn₂S₄ S型异质结等离子体光催化剂的制备及其增强光还原CO₂研究[J]. 物理化学学报, 2023, 39(6): 2211051 -0 .
[4]	罗铖, 龙庆, 程蓓, 朱必成, 王临曦. Pt-C₃N₄/BiOCl S型异质结应用于光催化CO₂还原的理论计算研究[J]. 物理化学学报, 2023, 39(6): 2212026 -0 .
[5]	荣佑文, 桑佳琪, 车丽, 高敦峰, 汪国雄. 二氧化碳电催化还原中的电解质效应[J]. 物理化学学报, 2023, 39(5): 2212027 -0 .
[6]	刘志成, 伊晓东, 高飞雪, 谢在库, 韩布兴, 孙予罕, 何鸣元, 杨俊林. 绿色碳科学：双碳目标下的科学基础——第292期“双清论坛”学术综述[J]. 物理化学学报, 2023, 39(1): 2112029 -0 .
[7]	马骋, 窦翔宇, 刘泽宇, 廖培龙, 朱志扬, 刘卡尔顿, 黄建滨. 一种新型CO₂/原油助混剂CAA8-X的应用与助混机理[J]. 物理化学学报, 2022, 38(8): 2012019 - .
[8]	叶成玉, 郁晓菲, 李文翠, 贺雷, 郝广平, 陆安慧. 磷化镍@镍-氮-碳双功能催化剂电还原CO₂-H₂O制合成气[J]. 物理化学学报, 2022, 38(4): 2004054 - .
[9]	刘影, 刘晓放, 夏林, 黄超杰, 吴兆萱, 王慧, 孙予罕. 以类水滑石为前驱体的Cu/ZnO/Al₂O₃催化剂用于CO_x加氢合成甲醇：CO在反应混合物中的作用[J]. 物理化学学报, 2022, 38(3): 2002017 - .
[10]	常明凯, 胡娜, 李遥, 鲜东帆, 周万强, 王静一, 时燕琳, 刘春立. Eu(Ⅲ)在蒙脱石上的吸附及碳酸根和磷酸根对其吸附的影响[J]. 物理化学学报, 2022, 38(3): 2003031 - .
[11]	何科林, 沈荣晨, 郝磊, 李佑稷, 张鹏, 江吉周, 李鑫. 纳米SiC基光催化剂研究进展[J]. 物理化学学报, 2022, 38(11): 2201021 - .
[12]	石永霞, 侯曼, 李俊俊, 李丽, 张志成. 铜基串联催化剂电催化CO₂还原的研究进展[J]. 物理化学学报, 2022, 38(11): 2206020 - .
[13]	周君慧, 敖志敏, 安太成. 基于密度泛函理论下H₂S在单原子催化剂V/Ti₂CO₂上的分解机理研究[J]. 物理化学学报, 2021, 37(8): 2007086 - .
[14]	赵康宁, 李潇, 苏东. 高熵纳米合金在电化学催化中的应用[J]. 物理化学学报, 2021, 37(7): 2009077 - .
[15]	李云锋, 张敏, 周亮, 杨思佳, 武占省, 马玉花. g-C₃N₄表面改性及其光催化制H₂与CO₂还原研究进展[J]. 物理化学学报, 2021, 37(6): 2009030 - .

五乙烯六胺修饰的MCF基吸附剂的制备及其CO₂吸附性能研究

Preparation of Pentaethylenehexamine-Functionalized Mesocellular Silica Foams and Their Application for CO₂ Adsorption

PDF

赞

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

Metrics

推荐阅读 0