羧酸根功能化的PVP-CdS同质结及其高效的光催化析氢性能

doi:10.3866/PKU.WHXB202004046

物理化学学报 >> 2022, Vol. 38 >> Issue (4): 2004046.doi: 10.3866/PKU.WHXB202004046

羧酸根功能化的PVP-CdS同质结及其高效的光催化析氢性能

赵娜¹^,², 彭静², 王建平¹, 翟茂林²^,*()

¹ 中国国家博物馆，北京 100006
² 北京大学化学与分子工程学院，放射化学与辐射化学重点学科实验室，北京分子科学国家研究中心，北京 100871

收稿日期:2020-04-15 录用日期:2020-05-06 发布日期:2020-05-11
通讯作者: 翟茂林 E-mail:mlzhai@pku.edu.cn
基金资助:
科学挑战项目(TZ2018004);国家自然科学基金(11575009);国家自然科学基金(11405168)

Novel Carboxy-Functionalized PVP-CdS Nanopopcorns with Homojunctions for Enhanced Photocatalytic Hydrogen Evolution

Na Zhao¹^,², Jing Peng², Jianping Wang¹, Maolin Zhai²^,*()

¹ The National Museum of China, Beijing 100006, China
² Beijing National Laboratory for Molecular Sciences, Radiochemistry and Radiation Chemistry Key Laboratory of Fundamental Science, College of Chemistry and Molecular Engineering, Peking University, Beijing 100871, China

Received:2020-04-15 Accepted:2020-05-06 Published:2020-05-11
Contact: Maolin Zhai E-mail:mlzhai@pku.edu.cn
About author:Maolin Zhai, Email: mlzhai@pku.edu.cn; Tel.: +86-10-62753794
Supported by:
the Science Challenge Project, China(TZ2018004);the National Natural Science Foundation of China(11575009);the National Natural Science Foundation of China(11405168)

摘要/Abstract

摘要：

光催化制氢是一种十分绿色、环保可持续的产氢方式。为了构建高效的光催化体系，对光催化剂进行表面修饰可以提高反应分子的吸附/活化的能力和电荷转移的效率。在本文中，我们通过γ-射线辐射还原法一步合成了聚乙烯吡咯烷酮包裹的硫化镉(P-CdS)同质结纳米粒子，之后通过室温下的碱化后处理，将P-CdS表面的PVP水解成为具有羧酸根和铵根的MPVP，而CdS的WZ-ZB同质结的晶体结构并未受到影响。一方面，由于MPVP在碱性溶液中的溶解度的提高，一部分MPVP溶解于溶液中，最终从MP-CdS表面去除，从而暴露出更多WZ-ZB同质结的活性位点。另一方面，水解后的MPVP保留在CdS表面，其羧酸根离子与CdS的配位作用，会影响到催化剂的价带结构，进而促进光催化析氢过程。在二者的协同作用下，当碱化NaOH浓度为1 mol·L^-1时，MP-CdS-3碱化样品的光催化析氢速率达到477 μmol·g^-1·h^-1，是未碱化样品的2倍。这种碱化后处理的策略简单且廉价，可以引申到合成一些PVP包裹的各类光催化剂的表面修饰当中，有利于促进硫化镉材料的光催化应用。

关键词: CdS, 同质结, 碱化处理, 光催化析氢

Abstract:

Photocatalytic hydrogen evolution is a scalable pathway to generate hydrogen fuels while mitigating environmental crisis. Strategies based on modification of the host photocatalyst surface are key to improve the adsorption/activation ability of the reaction molecules and the efficiency of charge transport, so that high-efficiency photocatalytic systems can be realized. Cadmium sulfide (CdS), a visible light-responsive semiconductor material, is widely used in photocatalysis because of its simple synthesis, low cost, abundant raw materials, and appropriate bandgap structure. Many researchers have focused on improving the photocatalytic efficiency of CdS because the rapid charge recombination in this material limits its applications. Among the various strategies proposed in this regard, surface modification is an effective and simple method used to improve the photocatalytic performance of materials. In this work, polyvinyl pyrrolidone (PVP)-capped CdS (denoted as P-CdS) nanopopcorns with hexagonal wurtzite (WZ)-cubic zinc blende (ZB) homojunctions were fabricated via one-step gamma-ray radiation-induced reduction under ambient conditions. Subsequent alkaline treatment under ambient conditions led to a dramatic improvement in the activity of the alkalized PVP-capped CdS (MP-CdS) photocatalyst. The structure and properties of the photocatalyst were determined by X-ray diffraction (XRD) analysis, field-emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), Fourier transform infrared (FTIR) analysis, Brunauer-Emmett-Teller (BET) specific surface area measurements, and photoelectric tests. The photocatalytic performance was evaluated based on the photocatalytic H₂ evolution under visible-light irradiation. The mechanism underlying the enhancement of the photocatalytic activity is also discussed. The results showed that after the alkaline treatment, the crystal structure of CdS with WZ-ZB homojunctions was preserved, but PVP on the surface of CdS hydrolyzed to form PVP hydrolysis product (MPVP) with carboxyl and amino groups. Owing to the increased alkaline solubility, a portion of MPVP dissolved into the solution and was removed from the surface of MP-CdS, exposing a greater number of active sites of the WZ-ZB phase junctions with a larger specific surface area. On the other hand, the carboxyl groups in MPVP coordinated with CdS could affect the bandgap and valence band position of CdS to facilitate the photocatalysis. Because of the synergistic effects of the exposure of WZ-ZB phase junctions and band structure engineering, the alkalized samples at a 1 mol·L^-1 concentration of NaOH showed a H₂ evolution rate of 477 μmol·g^-1·h^-1 under visible-light illumination, which was twice that obtained for the pristine P-CdS photocatalysts. This simple and low-cost post-synthesis strategy can be extended to the preparation of diverse functional photocatalysts. The present work is expected to contribute to the practical application of sulfide photocatalysts.

Key words: CdS, Homojunction, Alkaline treatment, Photocatalytic hydrogen evolution

赵娜, 彭静, 王建平, 翟茂林. 羧酸根功能化的PVP-CdS同质结及其高效的光催化析氢性能[J]. 物理化学学报, 2022, 38(4), 2004046. doi: 10.3866/PKU.WHXB202004046

Na Zhao, Jing Peng, Jianping Wang, Maolin Zhai. Novel Carboxy-Functionalized PVP-CdS Nanopopcorns with Homojunctions for Enhanced Photocatalytic Hydrogen Evolution[J]. Acta Phys. -Chim. Sin. 2022, 38(4), 2004046. doi: 10.3866/PKU.WHXB202004046

链接本文: https://www.whxb.pku.edu.cn/CN/10.3866/PKU.WHXB202004046

https://www.whxb.pku.edu.cn/CN/Y2022/V38/I4/2004046

图/表 14

Table 1

Fig 1

Fig 2

Fig 3

Fig 4

Table 2

Fig 5

Fig 6

Fig 7

Fig 8

Table 3

Table 4

Fig 9

Fig 10

参考文献 47

1	Ning X. ; Lu G. Nanoscale 2020, 12, 1213. doi: 10.1039/C9NR09183A
2	Zhang J. ; Chen X. ; Bai Y. ; Li C. ; Gao Y. ; Li R. ; Li C. J. Mater. Chem. A 2019, 7, 10264. doi: 10.1039/C8TA08199A
3	Li R. ; Li C. Adv. Catal. 2017, 60, 1. doi: 10.1016/bs.acat.2017.09.001
4	Cao P. F. ; Hu Y. ; Zhang Y. W. ; Peng J. ; Zhai M. L. Acta Phys. -Chim. Sin. 2017, 33, 2542.
	曹朋飞; 胡杨; 张有为; 彭静; 翟茂林; 物理化学学报, 2017, 33, 2542. doi: 10.3866/pku.whxb201706151
5	Wang Z. ; Wang L. Chin. J. Catal. 2018, 39, 369. doi: 10.1016/S1872-2067(17)62998-X
6	Chen J. Z. ; Wu X. J. ; Yin L. S. ; Li B. ; Hong X. ; Fan Z. X. ; Chen B. ; Xue C. ; Zhang H. Angew. Chem. -Int. Edit. 2015, 54, 1210. doi: 10.1002/anie.201410172
7	Jang J. S. ; Joshi U. A. ; Lee J. S. J. Phys. Chem. C 2007, 111, 13280. doi: 10.1021/jp072683b
8	Jing D. W. ; Guo L. J. J. Phys. Chem. B 2006, 110, 11139. doi: 10.1021/jp060905k
9	Yuan Y. J. ; Li Z. ; Wu S. ; Chen D. ; Yang L. X. ; Cao D. ; Tu W. G. ; Yu Z. T. ; Zou Z. G. Chem. Eng. J. 2018, 350, 335. doi: 10.1016/j.cej.2018.05.172
10	Li L. ; Wu J. ; Liu B. ; Liu X. ; Li C. ; Gong Y. ; Huang Y. ; Pan L. Catal. Today 2018, 315, 110. doi: 10.1016/j.cattod.2018.03.072
11	Low J. ; Dai B. ; Tong T. ; Jiang C. ; Yu J. Adv. Mater. 2019, 31, 1802981. doi: 10.1002/adma.201802981
12	Wang P. ; Yi X. ; Lu Y. ; Yu H. ; Yu J. J. Colloid Interface Sci. 2018, 532, 272. doi: 10.1016/j.jcis.2018.07.139
13	Zhao D. ; Chen C. ; Yu C. ; Ma W. ; Zhao J. J. Phys. Chem. C 2009, 113, 13160. doi: 10.1021/jp9002774
14	Ai Z. Z. ; Zhao G. ; Zhong Y. Y. ; Shao Y. L. ; Huang B. B. ; Wu Y. Z. ; Hao X. P. Appl. Catal. B-Environ. 2018, 221, 179. doi: 10.1016/j.apcatb.2017.09.002
15	Li K. ; Han M. ; Chen R. ; Li S. L. ; Xie S. L. ; Mao C. ; Bu X. ; Cao X. L. ; Dong L. Z. ; Feng P. ; et al Adv. Mater. 2016, 28, 8906. doi: 10.1002/adma.201601047
16	Zhao N. ; Peng J. ; Liu G. ; Zhang Y. ; Lei W. ; Yin Z. ; Li J. ; Zhai M. J. Mater. Chem. A 2018, 6, 18458. doi: 10.1039/C8TA03414A
17	Wang J. ; Cui W. ; Chen R. ; He Y. ; Yuan C. ; Sheng J. ; Li J. ; Zhang Y. ; Dong F. ; Sun Y. Catal. Sci. Technol. 2020, 10, 529. doi: 10.1039/C9CY02048A
18	Chen S. ; Qi Y. ; Li C. ; Domen K. ; Zhang F. Joule 2018, 2, 2260. doi: 10.1016/j.joule.2018.07.030
19	Liao Y. ; Cao S. W. ; Yuan Y. ; Gu Q. ; Zhang Z. ; Xue C. Chem. -A Eur. J. 2014, 20, 10220. doi: 10.1002/chem.201403321
20	Zhong W. ; Wu X. ; Wang P. ; Fan J. ; Yu H. ACS Sustain. Chem. Eng. 2020, 8, 543. doi: 10.1021/acssuschemeng.9b06046
21	Meng X. ; Ouyang S. ; Kako T. ; Li P. ; Yu Q. ; Wang T. ; Ye J. Chem. Commun. 2014, 50, 11517. doi: 10.1039/C4CC04848B
22	Zhang H. ; Yang Z. ; Shangguan L. ; Song X. ; Sun J. ; Lei W. Nanotechnology 2020, 31, 145716. doi: 10.1088/1361-6528/ab6750
23	Zhao F. ; Feng Y. ; Wang Y. ; Zhang X. ; Liang X. ; Li Z. ; Zhang F. ; Wang T. ; Gong J. ; Feng W. Nat. Commun. 2020, 11, 1443. doi: 10.1038/s41467-020-15262-4
24	Muruganandam S. ; Anbalagan G. ; Murugadoss G. Optik 2017, 131, 826. doi: 10.1016/j.ijleo.2016.12.001
25	Aisida S. O. ; Ahmad I. ; Ezema F. I. Phys. B: Conden. Matter 2020, 579, 411907. doi: 10.1016/j.physb.2019.411907
26	Senthil S. ; Srinivasan S. ; Thangeeswari T. ; Ratchagar V. J. Mater. Sci.-Mater. Electron. 2019, 30, 19841. doi: 10.1007/s10854-019-02351-4
27	Bibi R. ; Huang H. ; Kalulu M. ; Shen Q. ; Wei L. ; Oderinde O. ; Li N. ; Zhou J. ACS Sustain. Chem. Eng. 2019, 7, 4868. doi: 10.1021/acssuschemeng.8b05352
28	Kour G. ; Gupta M. Dalton Trans. 2017, 46, 7039. doi: 10.1039/C7DT00822H
29	Huang P. ; Jiang Q. ; Yu P. ; Yang L. ; Mao L. ACS Appl. Mater. Interfaces 2013, 5, 5239. doi: 10.1021/am401082n
30	Kumar D. P. ; Hong S. ; Reddy D. A. ; Kim T. K. J. Mater. Chem. A 2016, 4, 18551. doi: 10.1039/C6TA08628D
31	Xiong J. ; Liu Y. ; Wang D. ; Liang S. ; Wu W. ; Wu L. J. Mater. Chem. A 2015, 3, 12631. doi: 10.1039/C5TA02438B
32	Li Y. H. ; Zhang F. ; Chen Y. ; Li J. Y. ; Xu Y. J. Green Chem. 2020, 22, 163. doi: 10.1039/C9GC03332G
33	Abdelghany A. M. ; Abdelrazek E. M. ; Rashad D. S. Spectrochim. Acta A 2014, 130, 302. doi: 10.1016/j.saa.2014.04.049
34	Guo Y. ; Shi W. ; Zhu Y. ; Xu Y. ; Cui F. Appl. Catal. B-Environ. 2020, 262, 118262. doi: 10.1016/j.apcatb.2019.118262
35	Waehayee A. ; Watthaisong P. ; Wannapaiboon S. ; Chanlek N. ; Nakajima H. ; Wittayakun J. ; Suthirakun S. ; Siritanon T. Catal. Sci. Technol. 2020, 10, 978. doi: 10.1039/C9CY01782H
36	Buxton G. V. ; Greenstock C. L. ; Helman W. P. ; Ross A. B. J. Phys. Chem. Ref. Data 1988, 17, 513. doi: 10.1063/1.555805
37	Rossetti R. ; Nakahara S. ; Brus L. E. J. Chem. Phys. 1983, 79, 1086. doi: 10.1063/1.445834
38	Zhang L. ; Cheng Z. Q. ; Wang D. F. ; Li J. F. Mater. Lett. 2015, 158, 439. doi: 10.1016/j.matlet.2015.06.042
39	Chava R. K. ; Son N. ; Kim Y. S. ; Kang M. Nanomaterials 2020, 10, 619. doi: 10.3390/nano10040619
40	Wang L. ; Gao Z. ; Li Y. ; She H. ; Huang J. ; Yu B. ; Wang Q. Appl. Surf. Sci. 2019, 492, 598. doi: 10.1016/j.apsusc.2019.06.222
41	Jiang Z. ; Zhang X. ; Yang G. ; Yuan Z. ; Ji X. ; Kong F. ; Huang B. ; Dionysiou D. D. ; Chen J. Chem. Eng. J. 2019, 373, 814. doi: 10.1016/j.cej.2019.05.112
42	Sun Q. ; Wang N. ; Yu J. ; Yu J. C. Adv. Mater. 2018, 30, 1804368. doi: 10.1002/adma.201804368
43	Wu Y. ; Wang H. ; Tu W. ; Wu S. ; Liu Y. ; Tan Y. Z. ; Luo H. ; Yuan X. ; Chew J. W. Appl. Catal. B-Environ. 2018, 229, 181. doi: 10.1016/j.apcatb.2018.02.029
44	Ruan D. ; Fujitsuka M. ; Majima T. Appl. Catal. B-Environ. 2020, 264, 118541. doi: 10.1016/j.apcatb.2019.118541
45	Xing P. ; Chen Z. ; Chen P. ; Lin H. ; Zhao L. ; Wu Y. ; He Y. J. Colloid Interface Sci. 2019, 552, 622. doi: 10.1016/j.jcis.2019.05.098
46	Qin Y. ; Li H. ; Lu J. ; Meng F. ; Ma C. ; Yan Y. ; Meng M. Chem. Eng. J. 2020, 384, 123275. doi: 10.1016/j.cej.2019.123275
47	Moniruddin M. ; Oppong E. ; Stewart D. ; McCleese C. ; Roy A. ; Warzywoda J. ; Nuraje N. Inorg. Chem. 2019, 58, 12325. doi: 10.1021/acs.inorgchem.9b01854

Sample	Dose rate (Gy·min^-1)	Absorbed dose (kGy)	c_NaOH/(mol·L^-1))
P-CdS	200	300	0
MP-CdS-1	200	300	0.1
MP-CdS-2	200	300	0.5
MP-CdS-3	200	300	1.0
MP-CdS-4	200	300	2.0
MP-CdS-5	200	300	4.0

Samples	C 1s spectrum (atomic ratio (%))						N 1s/Cd 3d atomic ratios (%)
Samples	COO^-	C＝O	C-N	C	COO^-/C-N atomic ratio (%)	Hydrolysis degree (%) ^a	N 1s/Cd 3d atomic ratios (%)
P-CdS	0.0	16.9	40.2	43.0	0.0	0.0	35.5
MP-CdS-1	2.5	15.4	37.7	44.5	6.5	13.7	11.6
MP-CdS-2	2.3	14.7	36.7	46.2	6.3	13.6	9.8
MP-CdS-3	3.4	14.2	36.3	46.1	9.4	19.4	7.3
MP-CdS-4	1.9	15.1	38.8	44.3	4.8	11.0	13.0
MP-CdS-5	1.5	15.6	39.7	43.2	3.9	8.9	15.1

Sample	E_g/eV ^a	VBM/eV^b	S_BET/(m² ·g^-1) ^c	H₂ production rate /(μmol·h^-1·g^-1)
P-CdS	2.42	1.34	50.03	237
MP-CdS-1	2.31	1.45	79.85	403
MP-CdS-2	2.34	1.48	81.78	410
MP-CdS-3	2.38	1.48	87.1	477
MP-CdS-4	2.33	1.41	74.64	421
MP-CdS-5	2.32	1.39	63.96	350

Samples	Light Source	Co-catalyst	Reaction solution	Activity/(μmol·g^-1·h^-1)	Ref. (year)
CdS nanorods	150 W Xe > 420 nm	No	Lactic acid	206	39 (2020)
CdS modified by acid red-94	300 W Xe > 420 nm	No	Na₂SO₃ + Na₂S	475	40 (2019)
CdS nanodots	300 W Xe > 420 nm	No	Na₂SO₃ + Na₂S	83	41 (2019)
Hollow Porous CdS	300 W Xe > 400 nm	No	Na₂SO₃ + Na₂S	1110	42 (2018)
Petal-like CdS	300 W Xe > 420 nm	No	Lactic acid	248	43 (2018)
CdS nanoparticles	320 W Xe > 420 nm	No	Lactic acid	481	44 (2020)
CdS nanoparticles	300 W Xe > 420 nm	0.37%(w) Pt	Na₂S	26	45 (2019)
CdS nanorods	300 W Xe > 420 nm	3%(w) Pt	Na₂SO₃ + Na₂S	286.5	46 (2020)
CdS nanorods	300 W Xe > 420 nm	No	Na₂SO₃ + Na₂S	10.4	47 (2019)
MP-CdS-3	300 W Xe > 420 nm 100 mW·cm^-2	No	Lactic acid	477	this work

[1]	黄火帅, 韦之栋, 严嘉玮, 池家晟, 苏千翔, 陈铭夏, 江治, 孙洋洲, 上官文峰. 揭示Zn_xCd_1−xS固溶体光催化析氢中的直接-间接带隙跃迁机制[J]. 物理化学学报, 2026, 42(1): 100141 - .
[2]	王文龙, 郝文韬, 何浪, 乔佳, 李宁, 陈朝秋, 覃勇. 碳量子点/TiO₂ S型异质结的能带和吸附工程促进光催化CO₂甲烷化[J]. 物理化学学报, 2025, 41(9): 100116 - .
[3]	苗鑫宇, 杨浩, 何杰, 王晶, 靳治良. 调整Keggin型多金属氧酸盐电子结构构建S型异质结用于光催化析氢[J]. 物理化学学报, 2025, 41(6): 100051 - .
[4]	赵鑫婉, 曹越, 雷敏军, 靳治良, Tsubaki Noritatsu. 构建S型异质结：通过将共价有机框架与过渡金属硫化物结合实现高效无贵金属光催化制氢[J]. 物理化学学报, 2025, 41(12): 100152 - .
[5]	杨佳琦, 郝旭强, 景杰杰, 郝宇强, 靳治良. 3D/2D ReSe₂/ZnCdS S型光催化剂高效界面电荷分离增强光催化析氢[J]. 物理化学学报, 2025, 41(10): 100131 - .
[6]	黄凯辉, 陈德俊, 张欣, 沈荣晨, 张鹏, 许第发, 李鑫. 构建共价三嗪框架/氮掺杂碳包覆氧化亚铜S型异质结促进光催化析氢[J]. 物理化学学报, 2024, 40(12): 2407020 - .
[7]	张利君, 吴有林, Tsubaki Noritatsu, 靳治良. CeO₂-Cu₂O 2D/3D S型异质结界面促进有序电荷转移以实现高效光催化析氢[J]. 物理化学学报, 2023, 39(12): 2302051 - .
[8]	何科林, 沈荣晨, 郝磊, 李佑稷, 张鹏, 江吉周, 李鑫. 纳米SiC基光催化剂研究进展[J]. 物理化学学报, 2022, 38(11): 2201021 - .
[9]	吴进, 刘京, 夏雾, 任颖异, 王锋. 基于CdS和CdSe纳米半导体材料的可见光催化二氧化碳还原研究进展[J]. 物理化学学报, 2021, 37(5): 2008043 - .
[10]	纪军, 刘新, 黄浩, 蒋皓然, 段明君, 刘本玉, 崔鹏, 李英峰, 李美成. 钙钛矿同质结太阳电池研究进展[J]. 物理化学学报, 2021, 37(4): 2008095 - .
[11]	曹丹,安华,严孝清,赵宇鑫,杨贵东,梅辉. SiC/Pt/CdS纳米棒Z型异质结的制备及其高效光催化产氢性能[J]. 物理化学学报, 2020, 36(3): 1901051 - .
[12]	刘志明, 刘国亮, 洪昕林. 表面缺陷与钯的沉积对硫化镉纳米晶粒的光催化制氢性能的影响[J]. 物理化学学报, 2019, 35(2): 215 -222 .
[13]	胡海龙,王晟,侯美顺,刘福生,王田珍,李天龙,董乾乾,张鑫. 水热法制备p-CoFe₂O₄/n-CdS及其光催化制氢性能[J]. 物理化学学报, 2017, 33(3): 590 -601 .
[14]	王丽娟,李琦,郝彦忠,申世刚,徐东升. CdS/CdSe/TiO₂多级空心微球光阳极中量子点覆盖度的提高[J]. 物理化学学报, 2016, 32(4): 983 -989 .
[15]	周丽,刘欢欢,杨玉林,强亮生. SILAR法制备TiO₂/CdS/Co-Pi水氧化光阳极及其性能[J]. 物理化学学报, 2016, 32(11): 2731 -2736 .

羧酸根功能化的PVP-CdS同质结及其高效的光催化析氢性能

Novel Carboxy-Functionalized PVP-CdS Nanopopcorns with Homojunctions for Enhanced Photocatalytic Hydrogen Evolution

RichHTML

PDF

赞

可视化

摘要/Abstract

引用本文

使用本文

图/表 14

参考文献 47

相关文章 15

Metrics

推荐阅读 0