(苄基三乙基铵)双(1,3-二硫杂环戊烯-2-硫酮-4,5-二硫基)-金的三阶非线性光学性质

doi:10.3866/PKU.WHXB20110340

物理化学学报 >> 2011, Vol. 27 >> Issue (03): 717-721.doi: 10.3866/PKU.WHXB20110340

(苄基三乙基铵)双(1,3-二硫杂环戊烯-2-硫酮-4,5-二硫基)-金的三阶非线性光学性质

陈经纬¹, 王新强², 任诠¹, 李廷斌³, 杨洪亮¹, 张敬楠¹, 李国超¹

1. 山东大学光学系, 济南 250100;
2. 山东大学晶体材料国家重点实验室, 济南 250100;
3. 泰山学院材料与化学工程系, 山东泰安 271021

收稿日期:2010-10-29 修回日期:2011-01-06 发布日期:2011-03-03
通讯作者: 任诠 E-mail:qren@sdu.edu.cn
基金资助:
国家自然科学基金(60778037, 50772059, 11004123), 高等学校全国优秀博士学位论文专项资金(200539)和山东省自然科学基金(ZR2009GQ007)资助项目

Third Order Nonlinear Optical Properties of Benzyltriethylamine Bis(2-thioxo-1,3-dithiole-4,5-dithiolato) Aurate(III)

CHEN Jing-Wei¹, WANG Xin-Qiang², REN Quan¹, LI Ting-Bin³, YANG Hong-Liang¹, ZHANG Jing-Nan¹, LI Guo-Chao¹

1. Department of Optics, Shandong University, Jinan 250100, P. R. China;
2. State Key Laboratory of Crystal Materials, Shandong University, Jinan 250100, P. R. China;
3. Department of Material Science and Technology, Taishan University, Tai′an 271021, Shandong Province, P. R. China

Received:2010-10-29 Revised:2011-01-06 Published:2011-03-03
Contact: REN Quan E-mail:qren@sdu.edu.cn
Supported by:
The project was supported by the National Natural Science Foundation of China (60778037, 50772059, 11004123), Foundation for the Author of National Excellent Doctoral Dissertation of China (200539), and Science Foundation of Shandong Province, China (ZR2009GQ007).

摘要/Abstract

摘要：

合成了一种新的配位化合物(苄基三乙基铵)双(1,3-二硫杂环戊烯-2-硫酮-4,5-二硫基)-金(BTEAADT). 利用旋涂技术制备了该材料与聚甲基丙烯酸甲酯(PMMA)掺杂的复合薄膜, 该材料在复合薄膜中的质量分数为1%. 采用Z扫描方法, 分别测试了该材料的乙腈溶液和该材料与PMMA复合薄膜在波长为1064 nm, 脉宽为20 ps条件下的三阶非线性光学特性. 同时还研究了复合薄膜的线性光学性质. Z扫描的结果表明, 复合薄膜和该材料的乙腈溶液都具有自散焦效应, 非线性折射率都是负值. 在实验条件下, 两者的非线性吸收效应都是可以忽略的. 经过计算得出溶液样品的非线性折射率为-1.459×10^-18 m²·W^-1, 复合薄膜样品的非线性折射率为-3.978×10^-15 m²·W^-1. 该材料在1064 nm处的非线性光学器件方面有潜在应用价值.

关键词: 非线性光学性质, Z扫描技术, 薄膜

Abstract:

We prepared a new crystalline nonlinear optical coordination compound, benzyltriethylamine bis (2-thioxo-1,3-dithiole-4,5-dithiolato) aurate(III) (BTEAADT). A BTEAADT-doped poly(methyl methacrylate) (PMMA) thin film with a mass fraction of 1% was prepared by spin-coating. The third-order nonlinear optical properties of BTEAADT in acetonitrile and a BTEAADT-doped PMMA film were investigated using the laser Z-scan technique with 20 ps pulses at 1064 nm. The linear optical properties of the polymer thin film were also studied. The Z-scan spectra revealed that the polymer thin film sample possessed negative nonlinear refraction and exhibited a similar self-defocusing effect to that found for the solution. In addition, nonlinear absorption was negligible for both systems under the experimental conditions used. The nonlinear refractive index was calculated to be -1.459×10^-18 m²·W^-1 for the solution sample and -3.978×10^-15 m²·W^-1 for the film. These results suggest that this material is a promising candidate for application in nonlinear optical devices such as all-optical switching manufacture at 1064 nm.

Key words: Nonlinear optical property, Z-scan, Thin film

陈经纬, 王新强, 任诠, 李廷斌, 杨洪亮, 张敬楠, 李国超. (苄基三乙基铵)双(1,3-二硫杂环戊烯-2-硫酮-4,5-二硫基)-金的三阶非线性光学性质[J]. 物理化学学报, 2011, 27(03), 717-721. doi: 10.3866/PKU.WHXB20110340

CHEN Jing-Wei, WANG Xin-Qiang, REN Quan, LI Ting-Bin, YANG Hong-Liang, ZHANG Jing-Nan, LI Guo-Chao. Third Order Nonlinear Optical Properties of Benzyltriethylamine Bis(2-thioxo-1,3-dithiole-4,5-dithiolato) Aurate(III)[J]. Acta Phys. -Chim. Sin. 2011, 27(03), 717-721. doi: 10.3866/PKU.WHXB20110340

链接本文: https://www.whxb.pku.edu.cn/CN/10.3866/PKU.WHXB20110340

https://www.whxb.pku.edu.cn/CN/Y2011/V27/I03/717

参考文献

(1) Bredas, J. L.; Adant, C.; Persoons, A. Chem. Rev. 1994, 94, 243.
(2) Huang, W. T.; Wang, S. F.; Yang, H.; Gong, Q. H.; Zhan, X. W.; Liu, Y. Q.; Zhu, D. B. Chem. Phys. Lett. 2001, 350, 99.
(3) Stegeman, G. I.; Wright, E. M.; Finlayson, N.; Seaton, R.; Seaton, C. T. J. Lightwave Technol. 1988, 6, 953.
(4) Gu, Y. Z.; Yang, W.; Gan, F. X. Mater. Lett. 2002, 52, 404.
(5) Poornesh, P.; Umesh, G.; Hegde, P. K.; Manjunatha, M. G; Manjunatha, K. B.; Adhikari, A. V. Appl. Phys. B 2009, 97, 117.
(6) Shettigar, S.; Umeh, G.; Chandrasekharan, K.; Kalluraya, B. Synthetic Met. 2007, 157, 142.
(7) He, T. C.; Wang, C.; Pan, X.; Yang, H.; Lu, G. Y. Dyes. Pigm. 2008, 82, 47.
(8) Nalwa, H. S. Appl Organomet Chem. 1991, 5, 349.
(9) Mclean, D. G.; Sutherland, R. L.; Brant, M. C.; Brandelik, D. M.; Fleitz, P. Z.; Pottenger, T. Opt. Lett. 1993, 18, 858.
(10) Perry, J. W.; Mansour, K.; Lee, I. Y. S.; Wu, X. L.; Bedworth, P. V.; Chen, C. T. Science 1996, 273, 1533.
(11) Cassoux, P.; Valade, L.; Obayashi, H. K.; Kobayashi, A.; Clark, R. A.; Underhill, A. E. Coordin. Chem. Rev. 1991, 110, 115.
(12) Pullen, A. E.; Olk, R. M. Coordin. Chem. Rev. 1999, 188, 211.
(13) Kandasamy, K.; Rao, K. D.; Deshpande, R.; Puntambekar, P. N.; Singh, B. P.; Shetty, S. J.; Sribastava, T. S. Appl. Phys. B 1997, 64, 479.
(14) Falconieri, M.; Amato, R. D.; Furlani, A.; Russo, M. V. Synthetic Met. 2001, 124, 217.
(15) Zidan, H. M. J. Appl. Polym. Sci. 2003, 88, 104.
(16) Shettigar, S.; Chandrasekharan, K.; Umesh, G.; Sarojini, B. K.; Narayana, B. Polymer 2006, 47, 3565.
(17) Sheik-bahat, M.; Said, A. A.; Wei, T. H.; Hagan, D. J.; Van Stryland, E. W. IEEE J. Quant. Electron. 1990, 26, 760.
(18) Henary, F. Z.; Werner, J. B.; Milgrom, L. R.; Yahioglu, G.; Philips, D.; Lacey, J. A. Chem. Phys. Lett. 1997, 267, 229.
(19) Sun, X. B.; Ren, Q.; Wang, X. Q.; Zhang, G. H.; Yang, H. L.; Feng, L.; Xu, D.; Liu, Z. B. Chinese Phys. 2006, 15, 2618.
(20) Zhang, X.; Ren, Q.; Guo, W. F.; Sun, X. B.; Wang, X. Q.; Yang, H. L.; Zhang, F. J.; Gao, Y.; Xu, D. Mod. Phys. Lett. B 2008, 22, 191.
(21) Fan, H. L.; Wang, X. Q.; Ren, Q.; Li, T. B.; Zhao, X.; Sun, J.; Zhang, G. H.; Xu, D.; Sun, Z. H.; Yu, G. Appl. Phys. A 2010, 99, 279.
(22) Chen, J. W.; Ren, Q.; Wang, X. Q.; Fan, H. L.; Sun, Q. Mod. Phys. Lett. B 2010, 24, 2659.
(23) Steimeck, G.; Kirmse, R. Phosphorus Sulfur 1979, 79, 7.
(24) Varma, K. S.; Bury, A.; Harris, N. J.; Underhill, A. E. Synthesis-Stuttgart 1987, 9, 837.
(25) Wang, C. S.; Batsanov, A. S.; Bryce, M. R.; Howard, J. A. K. Synthesis-Stuttgart.1998, 11, 1615.
(26) Wang, X. Q.; Yu, W. T.; Xu, D.; Fan, J. D.; Zhang, G. H.; Ren, Q. Acta Cryst. C 2008, 64, 46.
(27) Liu, S. G.; Wu, P. J.; Li, Y. F.; Zhu, D. B. Phosphorus Sulfur. 1994, 90, 219.
(28) Yang, G.; Wang, W. T.; Yan, L.; Lu, H. B.; Yang, G. Z.; Chen, Z. H. Opt. Commun. 2002, 209, 445.
(29) Wang, S. F.; Huang, W. T.; Zhang, T. Q.; Gong, Q. H.; Okuma, Y.; Horikiri, M.; Miura, Y. F. Appl. Phys. Lett. 1999, 75, 1845.

[1]	夏求应, 蔡雨, 刘威, 王金石, 吴川智, 昝峰, 徐璟, 夏晖. 锂负极失效的全固态薄膜锂电池的直接回收再利用[J]. 物理化学学报, 2023, 39(8): 2212051 -0 .
[2]	姜美慧, 盛利志, 王超, 江丽丽, 范壮军. 超级电容器用石墨烯薄膜：制备、基元结构及表面调控[J]. 物理化学学报, 2022, 38(2): 2012085 - .
[3]	陈恒, 张金灿, 刘晓婷, 刘忠范. 气相反应对CVD生长石墨烯的影响[J]. 物理化学学报, 2022, 38(1): 2101053 - .
[4]	吴炯桦, 李一明, 石将建, 吴会觉, 罗艳红, 李冬梅, 孟庆波. 两步互扩散法制备高性能CsPbCl₃薄膜紫外光电探测器[J]. 物理化学学报, 2021, 37(4): 2004041 - .
[5]	王菲, 陈召龙, 杨嘉炜, 黎豪, 单婧媛, 张峰, 关宝璐, 刘忠范. 石墨烯玻璃透明薄膜加热特性[J]. 物理化学学报, 2021, 37(10): 2001024 - .
[6]	葛杨, 牟许霖, 卢岳, 隋曼龄. 空气下光诱导有机金属卤化钙钛矿薄膜的降解机理[J]. 物理化学学报, 2020, 36(8): 1905039 - .
[7]	刘太宏, 苗荣, 彭浩南, 刘静, 丁立平, 房喻. 薄膜基荧光气体传感器中的涂层化学[J]. 物理化学学报, 2020, 36(10): 1908025 - .
[8]	曹丹丹, 吕荣, 于安池. 高光学质量氮化碳薄膜的制备和表征[J]. 物理化学学报, 2019, 35(4): 442 -450 .
[9]	夏慧芸,耿通,赵旭,李芳芳,王凤燕,高莉宁. 基于ZnS纳米粒子的有机凝胶荧光薄膜的制备及其传感性能[J]. 物理化学学报, 2019, 35(3): 337 -344 .
[10]	殷鸿尧,于跃,李宗诚,张港鸿,冯玉军. 智能蜂窝状有序多孔薄膜：体系构建、响应性能及应用探索[J]. 物理化学学报, 2019, 35(12): 1341 -1356 .
[11]	王明越,谭世倞,崔雪峰,王兵. 引入应力的锐钛矿TiO₂(001)薄膜的外延生长[J]. 物理化学学报, 2019, 35(12): 1412 -1421 .
[12]	王灏珉,何茂帅,张莹莹. 碳纳米管薄膜的制备及其在柔性电子器件中的应用[J]. 物理化学学报, 2019, 35(11): 1207 -1223 .
[13]	刘新科,王佳乐,许楚瑜,罗江流,梁迪斯,岑俞诺,吕有明,李治文. 单层，少层和块状WS₂薄膜中声子位移随温度的变化[J]. 物理化学学报, 2019, 35(10): 1134 -1141 .
[14]	程龙,刘公平,金万勤. 二维材料膜在气体分离领域的最新研究进展[J]. 物理化学学报, 2019, 35(10): 1090 -1098 .
[15]	杜惟实,吕耀康,蔡志威,张诚. 基于三维多孔石墨烯/含钛共轭聚合物复合多孔薄膜的柔性全固态超级电容器[J]. 物理化学学报, 2017, 33(9): 1828 -1837 .

(苄基三乙基铵)双(1,3-二硫杂环戊烯-2-硫酮-4,5-二硫基)-金的三阶非线性光学性质

Third Order Nonlinear Optical Properties of Benzyltriethylamine Bis(2-thioxo-1,3-dithiole-4,5-dithiolato) Aurate(III)

PDF

赞

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

Metrics

推荐阅读 0