物理化学学报 >> 1995, Vol. 11 >> Issue (01): 1-4.doi: 10.3866/PKU.WHXB19950101

通讯    下一篇

Er2O3纳米晶光伏特性及谱带解析

崔毅, 王德军, 王宝辉, 李铁津, 董相廷, 洪广言   

  1. 吉林大学化学系,长春 130023|中国科学院应用化学研究所,长春 130022
  • 收稿日期:1994-07-23 修回日期:1994-09-26 发布日期:1995-01-15
  • 通讯作者: 王德军

The Photovoltage Properties and the Spertrum Analyses of Nanocrystalline Er2O3

Cui Yi, WangDe-Jun, Wang Bao-Hui, LiTie-Jin, Dong Xiang-Ting, HONG Guang-Yan   

  1. Department of Chemistry,Jilin University, Changchun 130023|Institute of Applied Chemistry,Academia Sinica,Changchun 130022
  • Received:1994-07-23 Revised:1994-09-26 Published:1995-01-15
  • Contact: Wang De-Jun

PDF

2658

赞

关键词: Er2O3, 纳米晶, 表面光伏

Abstract:

The diffuse reflectance spectra of nanocrystalline Er2O3 were measured in theUV-vis region. It was found that the f →f transition bands become stronger with the decrease of the size of particles. The tail-band in the range of 300 ~ 550nm was assigned to the O2p→Er4f transition. Both behavior of light-induced charge transfer and photovoltaic properties of nanocrystalline Er2O3 were investigated with surface photovoltage spectroscopy (SPS). The SPS shows that two peaks appear at 340nm (p1) and 385nm (p2).The observed spectral features can be explained in terms of charge transfer and interband transition.

Key words: Er2O3, Nanocrystalline, Photovoltage