溶液稳定、高导电性波纹状石墨烯片

doi:10.3866/PKU.WHXB201209103

物理化学学报 >> 2012, Vol. 28 >> Issue (10): 2465-2470.doi: 10.3866/PKU.WHXB201209103

溶液稳定、高导电性波纹状石墨烯片

范承伟, 张新, 陈胜, 王海芳, 曹傲能

上海大学纳米化学与生物学研究所, 上海 200444

收稿日期:2012-07-23 修回日期:2012-09-10 发布日期:2012-09-26
通讯作者: 曹傲能 E-mail:ancao@shu.edu.cn
基金资助:
国家自然科学基金(21073117); 国家重点基础研究发展规划项目(973)(2009CB930200, 2011CB933402)和上海市重点学科(S30109)资助

Solution-Processable, Highly Conductive, Permanently Rippled Graphene Sheets

FAN Cheng-Wei, ZHANG Xin, CHEN Sheng, WANG Hai-Fang, CAO Ao-Neng

Institute of Nanochemistry and Nanobiology, Shanghai University, Shanghai 200444, P. R. China

Received:2012-07-23 Revised:2012-09-10 Published:2012-09-26
Supported by:
The project was supported by the National Natural Science Foundation of China (21073117), National Key Basic Research Program (973) (2009CB930200, 2011CB933402), and Shanghai Leading Academic Disciplines, China (S30109).

摘要/Abstract

摘要：

特殊的单原子层二维sp²碳结构给石墨烯带来众多独特的性能和潜在的应用. 然而, 单层石墨烯容易聚集并会逐渐重新石墨化, 这成为其应用的一个重要障碍. 本文报道了一种新策略来解决这个问题, 即通过在石墨烯表面引入sp²碳纳米结构作为永久的波纹来阻止石墨烯的聚集和石墨化, 并使之在溶液中易于分散和稳定. 和其他功能化方法不同, 该方法没有引入杂原子, 不破坏石墨烯的结构和功能. 制得的石墨烯具有优异的导电性能(~65000 S·m^-1), 并具有较好的溶液稳定性.

关键词: 石墨烯, 波纹, 碳纳米笼, 可膨胀石墨, 导电性, 溶液稳定性

Abstract:

The single atom thick sp² carbon structure of graphene gives rise to its unique properties and potential applications. However, one serious obstacle for its application is that graphene is prone to aggregate in suspension and gradually stack into graphite. Here, we report a novel approach to solve this problem. The basic idea is to introduce sp² carbon nano-islands on the graphene sheets that act as permanent ripples to prevent the stacking and graphitization of graphene and make it easy to re-suspend. Unlike most functionalization methods, this approach avoids the introduction of heteroatoms. Thus, it does not deteriorate the structure and change the properties of graphene. The carbon-rippled graphene has a remarkable electronic conductivity of ~65000 S·m^-1, and can be readily suspended in solvent.

Key words: Graphene, Ripple, Carbon nanocage, Expandable graphite, Conductivity, Solution stability

范承伟, 张新, 陈胜, 王海芳, 曹傲能. 溶液稳定、高导电性波纹状石墨烯片[J]. 物理化学学报, 2012, 28(10): 2465-2470.

FAN Cheng-Wei, ZHANG Xin, CHEN Sheng, WANG Hai-Fang, CAO Ao-Neng. Solution-Processable, Highly Conductive, Permanently Rippled Graphene Sheets[J]. Acta Phys. -Chim. Sin., 2012, 28(10): 2465-2470.

链接本文: https://www.whxb.pku.edu.cn/CN/10.3866/PKU.WHXB201209103

https://www.whxb.pku.edu.cn/CN/Y2012/V28/I10/2465

参考文献

(1) Mermin, N. D. Phys. Rev. 1968, 176, 250. doi: 10.1103/PhysRev.176.250
(2) Meyer, J. C.; Geim, A. K.; Katsnelson, M. I.; Novoselov, K. S.;Booth, T. J.; Roth, S. Nature 2007, 446, 60. doi: 10.1038/nature05545
(3) Novoselov, K. S.; Jiang, D.; Schedin, F.; Booth, T. J.;Khotkevich, V. V.; Morozov, S. V.; Geim, A. K. Proc. Natl. Acad. Sci. U. S. A. 2005, 102, 10451. doi: 10.1073/pnas.0502848102
(4) Fasolino, A.; Los, J. H.; Katsnelson, M. I. Nat. Mater. 2007, 6,858. doi: 10.1038/nmat2011
(5) Geim, A. K.; Novoselov, K. S. Nat. Mater. 2007, 6, 183. doi: 10.1038/nmat1849
(6) Huang, X.; Yin, Z. Y.;Wu, S. X.; Qi, X. Y.; He, Q. Y.; Zhang, Q.C.; Yan, Q. Y.; Boey, F.; Zhang, H. Small 2011, 7, 1876. doi: 10.1002/smll.201002009
(7) Geim, A. K. Science 2009, 324, 1530. doi: 10.1126/science.1158877
(8) Jiang, H. J. Small 2011, 7, 2413.
(9) Huang, X.; Qi, X. Y.; Boey, F.; Zhang, H. Chem. Soc. Rev. 2012,41, 666. doi: 10.1039/c1cs15078b
(10) Li, X. L.; Zhang, G. Y.; Bai, X. D.; Sun, X. M.;Wang, X. R.;Wang, E. G.; Dai, H. J. Nat. Nanotechnol. 2008, 3, 538. doi: 10.1038/nnano.2008.210
(11) Liu, Z.; Fan, C.W.; Chen, L.; Cao, A. N. J. Nanosci. Nanotech.2010, 10, 7382. doi: 10.1166/jnn.2010.2780
(12) Hernandez, Y.; Nicolosi, V.; Lotya, M.; Blighe, F.; Sun, Z.; De,S.; McGovern, I. T.; Holland, B.; Byrne, M.; Gunko, Y.; Boland,J.; Niraj, P.; Duesberg, G.; Krishnamurti, S.; Goodhue, R.;Hutchison, J.; Scardaci, V.; Ferrari, A. C.; Coleman, J. N. Nat. Nanotechnol. 2008, 3, 563.
(13) Eda, G.; Fanchini, G.; Chhowalla, M. Nat. Nanotechnol. 2008,3, 270. doi: 10.1038/nnano.2008.83
(14) Li, D.; Muller, M. B.; Gilje, S.; Kaner, R. B.;Wallace, G. G.Nat. Nanotechnol. 2008, 3, 101. doi: 10.1038/nnano.2007.451
(15) Cao, A. N.; Liu, Z.; Chu, S. S.;Wu, M. H.; Ye, Z. M.; Cai, Z.W.; Chang, Y. L.;Wang, S. F.; Gong, Q. H.; Liu, Y. F. Adv. Mater. 2010, 22, 103. doi: 10.1002/adma.v22:1
(16) Qi, X. Y.; Pu, K. Y.; Zhou, X. Z.; Li, H.; Liu, B.; Boey, F.;Huang, W.; Zhang, H. Small 2010, 6, 663. doi: 10.1002/smll.v6:5
(17) Stankovich, S.; Dikin, D. A.; Dommett, G. H. B.; Kohlhaas, K.M.; Zimney, E. J.; Stach, E. A.; Piner, R. D.; Nguyen, S. T.;Ruoff, R. S. Nature 2006, 442, 282. doi: 10.1038/nature04969
(18) Choucair, M.; Thordarson, P.; Stride, J. A. Nat. Nanotechnol.2009, 4, 30. doi: 10.1038/nnano.2008.365
(19) Qi, X. Y.; Pu, K. Y.; Li, H.; Zhou, X. Z.;Wu, S.; Fan, Q. L.; Liu,B.; Boey, F.; Huang,W.; Zhang, H. Angew. Chem. Int. Edit.2010, 49, 9426. doi: 10.1002/anie.201004497
(20) Feng, X.; Hu, G.; Hu, J. Nanoscale 2011, 3, 2099. doi: 10.1039/c1nr00004g
(21) Dreyer, D. R.; Park, S.; Bielawski, C.W.; Ruoff, R. S. Chem. Soc. Rev. 2010, 39, 228. doi: 10.1039/b917103g
(22) Park, S.; An, J.; Jung, I.; Piner, R. D.; An, S. J.; Li, X. S.;Velamakanni, A.; Ruoff, R. S. Nano Lett. 2009, 9, 1593. doi: 10.1021/nl803798y
(23) Dikin, D. A.; Stankovich, S.; Zimney, E. J.; Piner, R. D.;Dommett, G. H. B.; Evmenenko, G.; Nguyen, S. T.; Ruoff, R. S.Nature 2007, 448, 457. doi: 10.1038/nature06016
(24) Zhou, X. Z.; Huang, X.; Qi, X. Y.;Wu, S. X.; Xue, C.; Boey, F.Y. C.; Yan, Q. Y.; Chen, P.; Zhang, H. J. Phys. Chem. C 2009,113, 10842. doi: 10.1021/jp903821n
(25) Chang, Y. L.; Chen, S.; Cao, A. N. J. Shanghai University (Natural Science) 2010, 16 (6), 577. [常艳丽, 陈胜, 曹傲能. 上海大学学报(自然科学版), 2010, 16 (6), 577.]
(26) Yang, S. T.; Chen, S.; Chang, Y.; Cao, A.; Liu, Y.;Wang, H.J. Colloid Interface Sci. 2011, 359, 24. doi: 10.1016/j.jcis.2011.02.064
(27) Yang, S. T.; Chang, Y.;Wang, H.; Liu, G.; Chen, S.;Wang, Y.;Liu, Y.; Cao, A. J. Colloid Interface Sci. 2010, 351, 122. doi: 10.1016/j.jcis.2010.07.042
(28) Chang, Y.; Yang, S. T.; Liu, J. H.; Dong, E.;Wang, Y.; Cao, A.;Liu, Y.;Wang, H. Toxicol Lett. 2011, 200, 201. doi: 10.1016/j.toxlet.2010.11.016
(29) Hao, R.; Qian,W.; Zhang, L.; Hou, Y. Chem. Commun. 2008,6576.
(30) Qian,W.; Cui, X.; Hao, R.; Hou, Y.; Zhang, Z. ACS Appl. Mater. Interfaces 2011, 3 (7), 2259. doi: 10.1021/am200479d
(31) Qian,W.; Hao, R.; Hou, Y.; Tian, Y.; Shen, C.; Gao, H.; Liang,X. Nano Res. 2009, 2, 706. doi: 10.1007/s12274-009-9074-z
(32) Kauzmann,W. Adv. Protein Chem. 1959, 14, 1. doi: 10.1016/S0065-3233(08)60608-7
(33) Dill, K. A. Biochemistry 1990, 29, 7133. doi: 10.1021/bi00483a001
(34) Jung, I.; Dikin, D. A.; Piner, R. D.; Ruoff, R. S. Nano Lett.2008, 8, 4283. doi: 10.1021/nl8019938
(35) Gomez-Navarro, C.;Weitz, R. T.; Bittner, A. M.; Scolari, M.;Mews, A.; Burghard, M.; Kern, K. Nano Lett. 2007, 7, 3499.doi: 10.1021/nl072090c
(36) Si, Y. C.; Samulski, E. T. Nano Lett. 2008, 8, 1679. doi: 10.1021/nl080604h

[1]	吕浩亮, 王雪杰, 杨宇, 刘涛, 张留洋. 还原氧化石墨烯包覆MOF衍生In₂Se₃用于钠离子电池负极[J]. 物理化学学报, 2023, 39(3): 2210014 -0 .
[2]	刘若娟, 刘冰之, 孙靖宇, 刘忠范. 气相助剂辅助绝缘衬底上石墨烯生长：现状与展望[J]. 物理化学学报, 2023, 39(1): 2111011 -0 .
[3]	夏洲, 邵元龙. 湿法纺制石墨烯纤维：工艺、结构、性能与智能应用[J]. 物理化学学报, 2022, 38(9): 2103046 - .
[4]	贺文娅, 程虎虎, 曲良体. 烯碳纤维基能源器件的研究进展[J]. 物理化学学报, 2022, 38(9): 2203004 - .
[5]	刘汉卿, 周锋, 师晓宇, 史全, 吴忠帅. 石墨烯基纤维储能器件的研究进展与展望[J]. 物理化学学报, 2022, 38(9): 2204017 - .
[6]	何文倩, 邸亚, 姜南, 刘遵峰, 陈永胜. 石墨烯诱导水凝胶成核的高强韧人造蛛丝[J]. 物理化学学报, 2022, 38(9): 2204059 - .
[7]	彭景淞, 程群峰. 仿鲍鱼壳石墨烯多功能纳米复合材料[J]. 物理化学学报, 2022, 38(5): 2005006 - .
[8]	毛赫南, 王晓工. 影响高浓度氧化石墨烯分散液流变行为的重要因素及群体平衡动力学分析[J]. 物理化学学报, 2022, 38(4): 2004025 - .
[9]	杨贻顺, 周敏, 邢燕霞. 基于γ-石墨炔分子磁隧道结对称性依赖的输运性质[J]. 物理化学学报, 2022, 38(4): 2003004 - .
[10]	薄拯, 孔竞, 杨化超, 郑周威, 陈鹏鹏, 严建华, 岑可法. 基于混合溶剂有机电解液的超低温孔洞石墨烯超级电容[J]. 物理化学学报, 2022, 38(4): 2005054 - .
[11]	唐诗怡, 鹿高甜, 苏毅, 王广, 李炫璋, 张广琦, 魏洋, 张跃钢. 石墨烯嵌锂的拉曼成像[J]. 物理化学学报, 2022, 38(3): 2001007 - .
[12]	程熠, 王坤, 亓月, 刘忠范. 石墨烯纤维材料的化学气相沉积生长方法[J]. 物理化学学报, 2022, 38(2): 2006046 - .
[13]	姜蓓, 孙靖宇, 刘忠范. 石墨烯晶圆的制备：从高品质到规模化[J]. 物理化学学报, 2022, 38(2): 2007068 - .
[14]	蹇木强, 张莹莹, 刘忠范. 石墨烯纤维：制备、性能与应用[J]. 物理化学学报, 2022, 38(2): 2007093 - .
[15]	姜美慧, 盛利志, 王超, 江丽丽, 范壮军. 超级电容器用石墨烯薄膜：制备、基元结构及表面调控[J]. 物理化学学报, 2022, 38(2): 2012085 - .

溶液稳定、高导电性波纹状石墨烯片

Solution-Processable, Highly Conductive, Permanently Rippled Graphene Sheets

PDF

赞

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

Metrics

推荐阅读 0