氮掺杂六角石墨烯纳米结构的近红外等离激元研究

doi:10.3866/PKU.WHXB201404092

物理化学学报 >> 2014, Vol. 30 >> Issue (6): 1049-1054.doi: 10.3866/PKU.WHXB201404092

氮掺杂六角石墨烯纳米结构的近红外等离激元研究

尹海峰¹, 张红², 岳莉¹

1 凯里学院物理与电子工程学院, 贵州凯里556011;
2 四川大学物理科学与技术学院, 成都610065

收稿日期:2014-01-15 修回日期:2014-04-08 发布日期:2014-05-26
通讯作者: 尹海峰，张红 E-mail:yinhaifeng1212@126.com;hongzhang@scu.edu.cn
基金资助:
国家自然科学基金（11074176），贵州省科学技术基金（黔科合J 字LKK[2013]19 号），贵州省教育厅高校优秀科技创新人才支持计划（黔教合KY字[2013]152）及凯里学院规划项目（Z1308）资助项目

Near-Infrared Plasmon Study on N-Doped Hexagonal Graphene Nanostructures

YIN Hai-Feng¹, ZHANG Hong², YUE Li¹

1 College of Physics and Electronic Engineering, Kaili University, Kaili 556011, Guizhou Province, P. R. China;
2 College of Physical Science and Technology, Sichuan University, Chengdu 610065, P. R. China

Received:2014-01-15 Revised:2014-04-08 Published:2014-05-26
Contact: YIN Hai-Feng, ZHANG Hong E-mail:yinhaifeng1212@126.com;hongzhang@scu.edu.cn
Supported by:
The project was supported by the National Natural Science Foundation of China (11074176), Science and Technology Foundation of Guizhou Province, China (LKK[2013]19), Universities Outstanding Scientific and Technical Innovators Support Program of Department of Education of Guizhou Province, China (KY [2013]152), and Planning Project of Kaili University, China (Z1308).

摘要/Abstract

摘要：

基于含时密度泛函理论研究了氮掺杂六角石墨烯纳米结构的近红外等离激元. 沿一定的激发方向，边长为1 nm的氮掺杂六角石墨烯纳米结构在整个近红外光谱区都有强度较大的等离激元共振. 参与这种近红外等离激元模式共振的电子在六角纳米结构的中心和边缘区域之间来回振荡. 近红外等离激元共振模式的形成依赖于氮掺杂的位置和纳米结构的尺度大小. 只有当氮掺杂在靠近边界区域时体系才会在近红外光谱区形成等离激元共振模式. 对于边长小于1 nm的六角石墨烯纳米结构，氮掺杂后体系不能在近红外光谱区形成等离激元共振模式.

关键词: 等离激元, 氮掺杂石墨烯, 纳米结构, 近红外光谱, 含时密度泛函理论

Abstract:

Near-infrared plasmons in N-doped hexagonal graphene nanostructures were investigated using time-dependent density functional theory. Along a certain direction, N-doped hexagonal graphene nanostructures with a side length of 1 nm have more intense plasmon resonances throughout the nearinfrared spectral region. The electrons that participate in these near-infrared plasmon resonances oscillate back and forth between the center and edge regions of the hexagonal nanostructures. The formation of a near-infrared plasmon resonance mode depends on the nitrogen-doping position and the scale size of the graphene nanostructure. It is only when the nitrogen-doped location is close to the edge of the nanostructures, near-infrared plasmon resonance mode of the graphene nanostructure will be formed. For N-doped hexagonal graphene nanostructures with a side length of less than 1 nm, there is no plasmon resonance in the nearinfrared spectral region.

Key words: Plasmon, N-doped graphene, Nanostructure, Near-infrared spectroscopy, Time-dependent density functional theory

尹海峰, 张红, 岳莉. 氮掺杂六角石墨烯纳米结构的近红外等离激元研究[J]. 物理化学学报, 2014, 30(6): 1049-1054.

YIN Hai-Feng, ZHANG Hong, YUE Li. Near-Infrared Plasmon Study on N-Doped Hexagonal Graphene Nanostructures[J]. Acta Phys. -Chim. Sin., 2014, 30(6): 1049-1054.

链接本文: https://www.whxb.pku.edu.cn/CN/10.3866/PKU.WHXB201404092

https://www.whxb.pku.edu.cn/CN/Y2014/V30/I6/1049

参考文献

(1) Novoselov, K. S.; Geim, A. K.; Morozov, S. V.; Zhang, Y.; Dubonos, S. V.; Grigorieva, I. V.; Firsov, A. A. Science 2004, 306, 666. doi: 10.1126/science.1102896
(2) Chen, S.;Wu, Q.; Mishra, C.; Kang, J.; Zhang, H.; Cho, K.; Cai, W.; Balandin, A. A.; Ruoff, R. S. Nature Materials 2012, 11, 203. doi: 10.1038/nmat3207
(3) Zou, H.; Ni, X.; Peng, S. L.; Ouyang, J.; Chen, Y.; Ouyang, F. P. Acta Phys. -Chim. Sin. 2013, 29, 250. [邹辉, 倪祥, 彭盛霖, 欧阳俊, 陈羽, 欧阳方平. 物理化学学报, 2013, 29,250.] doi: 10.3866/PKU.WHXB201211141
(4) Grigorenko, A. N.; Polini, M.; Novoselov, K. S. Nature Photonics 2012, 6, 749. doi: 10.1038/nphoton.2012.262
(5) Javier Garcia de Abajo, F. Science 2013, 339, 917. doi: 10.1126/science.1231119
(6) Halas, N. J.; Lal, S.; Chang,W. S.; Link, S.; Nordlander, P. Chem. Rev. 2011, 111, 3913. doi: 10.1021/cr200061k
(7) Tong, L. M.; Xu, H. X. Front. Phys. 2014, 9, 1. doi: 10.1007/s11467-013-0399-4
(8) Bostwick, A.; Speck, F.; Seyller, T.; Horn, K.; Polini, M.; Asgari, R.; MacDonald, A. H.; Rotenberg, E. Science 2010, 328, 999. doi: 10.1126/science.1186489
(9) Schiros, T.; Nordlund, D.; Pálova, L.; Prezzi, D.; Zhao, L.; Kim, K. S.;Wurstbauer, U.; Gutiérrez, C.; Delongchamp, D.; Jaye, C.; Fischer, D.; Ogasawara, H.; Pettersson, L. G. M.; Reichman, D. R.; Kim, P.; Hybertsen, M. S.; Pasupathy, A. N. Nano Lett. 2012, 12, 3766. doi: 10.1021/nl3016335
(10) Zhao, L.; He, R.; Rim, K. T.; Kim, K. S.; Zhou, H.; Gutiérrez, C.; Chockalingam, S. P.; Arguello, C. J.; Pálová, L.; Nordlund, D.; Hybertsen, M. S.; Reichman, D. R.; Heinz, T. F.; Kim, P.; Pinczuk, A.; Flynn, G.W.; Pasupathy, A. N. Science 2011, 333, 999. doi: 10.1126/science.1208759
(11) Gao, H.; Song, L.; Guo,W.; Huang, L.; Yang, D.;Wang, F.; Zuo, Y.; Fan, X.; Liu, Z.; Gao,W.; Vajtai, R.; Hackenberg, K.; Ajayan, P. M. Carbon 2012, 50, 4476. doi: 10.1016/j.carbon.2012.05.026
(12) Li, M.;Wu,W.; Ren,W.; Cheng, H. M.; Tang, N.; Zhong,W.; Du, Y. Appl. Phys. Lett. 2012, 101, 103107. doi: 10.1063/1.4750065
(13) Guo, B.; Liu, Q.; Chen, E.; Zhu, H.; Fang, L.; Gong, J. R. Nano Lett. 2010, 10, 4975. doi: 10.1021/nl103079j
(14) Su, P.; Guo, H. L.; Peng, S.; Ning, S. K. Acta Phys. -Chim. Sin. 2012, 28, 2745. [苏鹏, 郭慧林, 彭三, 宁生科. 物理化学学报, 2012, 28, 2745.] doi: 10.3866/PKU.WHXB201208221
(15) Xiang, H. J.; Huang, B.; Li, Z. Y.;Wei, S. H.; Yang, J. L.; Gong, X. G. Phys. Rev. X 2012, 2, 011003.
(16) Hou, Z.;Wang, X.; Ikeda, T.; Terakura, K.; Oshima, M.; Kakimoto, M.; Miyata, S. Phys. Rev. B 2012, 85, 165439. doi: 10.1103/PhysRevB.85.165439
(17) Ritter, K. A.; Lyding, J.W. Nature Materials 2009, 8, 235. doi: 10.1038/nmat2378
(18) Thongrattanasiri, S.; Manjavacas, A.; Javier García de Abajo, F. ACS Nano 2012, 6,1766. doi: 10.1021/nn204780e
(19) Yin, H. F.; Zhang, H. J. Appl. Phys. 2012, 111, 103502. doi: 10.1063/1.4706566
(20) Yan, X.; Cui, X.; Li, B.; Li, L. S. Nano Lett. 2010, 10, 1869. doi: 10.1021/nl101060h
(21) Yan, X.; Cui, X.; Li, L. S. J. Am. Chem. Soc. 2010, 132, 5944. doi: 10.1021/ja1009376
(22) Li, Y.; Zhao, Y.; Cheng, H.; Hu, Y.; Shi, G.; Dai, L.; Qu, L. J. Am. Chem. Soc. 2012, 134, 15. doi: 10.1021/ja206030c
(23) Liu, Q.; Guo, B. D.; Rao, Z.; Zhang, B. H.; Gong, J. R. Nano Lett. 2013, 13, 2436. doi: 10.1021/nl400368v
(24) Brar, V.W.; Jang, M.; Sherrott, M.; Lopez, J. J.; Atwater, H. A. Nano Lett. 2013, 13, 2541. doi: 10.1021/nl400601c
(25) Robinson, T. J.; Tabakman, S. M.; Liang, Y.;Wang, H.; Casalongue, H. S.; Vinh, D.; Dai, H. J. J. Am. Chem. Soc. 2011, 133, 6825. doi: 10.1021/ja2010175
(26) Fang, Z. Y.;Wang, Y. M.; Schlather, A. E.; Liu, Z.; Ajayan, P. M.; Javier García de Abajo, F.; Nordlander, P.; Zhu, X.; Halas, N. J. Nano Lett. 2014, 14, 299. doi: 10.1021/nl404042h
(27) Marques, M. A. L.; Castro, A.; Bertsch, G. F.; Rubio, A. Comput. Phys. Commun. 2003, 151, 60. doi: 10.1016/S0010-4655(02)00686-0
(28) Troullier, N.; Martins, J. L. Phys. Rev. B 1991, 43, 1993. doi: 10.1103/PhysRevB.43.1993
(29) Ceperley, D. M.; Alder, B. J. Phys. Rev. Lett. 1980, 45, 566. doi: 10.1103/PhysRevLett.45.566
(30) Rubio, A.; Alonso, J. A.; Lopez, J. M.; Stott, M. J. Physica B 1993, 183, 247. doi: 10.1016/0921-4526(93)90035-5
(31) Marinopoulos, A. G.; Reining, L.; Olevano, V.; Rubio, A. Phys. Rev. Lett. 2002, 89, 076402. doi: 10.1103/PhysRevLett.89.076402
(32) Marinopoulos, A. G.; Reining, L.; Rubio, A.; Vast, N. Phys. Rev. Lett. 2003, 91, 046402. doi: 10.1103/PhysRevLett.91.046402
(33) Eberlein, T.; Bangert, U.; Nair, R. R.; Jones, R.; Gass, M.; Bleloch, A. L.; Novoselov, K. S.; Geim, A.; Briddon, P. R. Phys. Rev. B 2008, 77, 233406. doi: 10.1103/PhysRevB.77.233406
(34) Kim, S.; Hwang, S.W.; Kim, M. K.; Shin, D. Y.; Shin, D. H.; Kim, C. O.; Yang, S. B.; Park, J. H.; Hwang, E.; Choi, S. H.; Ko, G.; Sim, S.; Sone, C.; Choi, H. J.; Bae, S.; Hong, B. H. ACS Nano 2012, 6, 8203. doi: 10.1021/nn302878r
(35) Mishchenko, E. G.; Shytov, A. V.; Silvestrov, P. G. Phys. Rev. Lett. 2010, 104, 156806. doi: 10.1103/PhysRevLett.104.156806

[1]	王宁, 李一, 崔乾, 孙晓玥, 胡悦, 罗运军, 杜然. 金属气凝胶：可控制备与应用展望[J]. 物理化学学报, 2023, 39(9): 2212014 -0 .
[2]	周文杰, 景启航, 李家馨, 陈颖芝, 郝国栋, 王鲁宁. 有机光催化剂用于太阳能水分解：分子水平和聚集体水平改性[J]. 物理化学学报, 2023, 39(5): 2211010 -0 .
[3]	卢浩然, 魏雅清, 龙闰. 纳米孔缺陷导致单层黑磷电荷局域极大抑制非辐射电子-空穴复合的时域模拟[J]. 物理化学学报, 2022, 38(5): 2006064 - .
[4]	秦睿, 王鹏彦, 林灿, 曹菲, 张金咏, 陈磊, 木士春. 过渡金属氮化物的活性起源、合成方法及电催化应用[J]. 物理化学学报, 2021, 37(7): 2009099 - .
[5]	安平, 付宇, 韦丹蕾, 郭杨龙, 詹望成, 张金水. 富氮空心蠕虫状碳材料的合成及其苯甲醇非金属选择性催化氧化的高活性[J]. 物理化学学报, 2021, 37(10): 2001025 - .
[6]	陈锐杰,李娣,方振远,黄元勇,罗必富,施伟东. In₂O₃三维纳米结构的控制合成及高效光解水产氢活性研究[J]. 物理化学学报, 2020, 36(3): 1903047 - .
[7]	张书山,周剑章,吴德印,田中群. Ag纳米粒子修饰光纤探针在等离激元催化反应中的应用[J]. 物理化学学报, 2019, 35(3): 307 -316 .
[8]	黄浩,龙冉,熊宇杰. 应用于有机加氢反应的等离激元催化材料设计[J]. 物理化学学报, 2017, 33(4): 661 -669 .
[9]	孙海涛,钟成,孙真荣. 最优化“调控”区间分离密度泛函理论的研究进展[J]. 物理化学学报, 2016, 32(9): 2197 -2208 .
[10]	尹海峰. 硅烯量子点二聚物的等离激元激发[J]. 物理化学学报, 2016, 32(6): 1446 -1452 .
[11]	王元元,徐群星,谢华清,吴子华,邢姣娇. 表面活性剂对树形银纳米结构影响的蒙特-卡洛模拟[J]. 物理化学学报, 2016, 32(10): 2518 -2522 .
[12]	郑东,袁相爱,马晶. 邻位甲基红水溶液的光谱性质随pH值的变化：含时密度泛函理论计算与实验研究[J]. 物理化学学报, 2016, 32(1): 290 -300 .
[13]	王俊,李莉,魏子栋. 不同氮掺杂石墨烯氧还原反应活性的密度泛函理论研究[J]. 物理化学学报, 2016, 32(1): 321 -328 .
[14]	叶传香,马会利,梁万珍. 几个荧光蛋白发色团双光子吸收性质的理论研究[J]. 物理化学学报, 2016, 32(1): 301 -312 .
[15]	侯丽梅,温智,李银祥,胡华友,阚玉和,苏忠民. 含中氮茚有机太阳能电池染料敏化剂的分子设计[J]. 物理化学学报, 2015, 31(8): 1504 -1512 .

氮掺杂六角石墨烯纳米结构的近红外等离激元研究

Near-Infrared Plasmon Study on N-Doped Hexagonal Graphene Nanostructures

PDF

赞

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

Metrics

推荐阅读 0