构筑Z型MnO2/BiOBr异质结用于光催化环丙沙星去除和CO2还原

doi:10.3866/PKU.WHXB202212011

物理化学学报 >> 2023, Vol. 39 >> Issue (11): 2212011.doi: 10.3866/PKU.WHXB202212011

构筑Z型MnO₂/BiOBr异质结用于光催化环丙沙星去除和CO₂还原

董金涛¹, 季赛楠², 张屹¹, 季梦夏¹, 王彬¹, 李英杰¹, 陈志刚², 夏杰祥¹^,*(), 李华明¹

¹ 江苏大学化学化工学院，能源研究院，江苏镇江 212013
² 江苏大学环境与安全工程学院，江苏镇江 212013

收稿日期:2022-12-06 录用日期:2023-02-17 发布日期:2023-02-28
通讯作者: 夏杰祥 E-mail:xjx@ujs.edu.cn
基金资助:
江苏省研究生科研与实践创新计划(KYCX22_3692);国家自然科学基金(21878134);国家自然科学基金(22108106);国家自然科学基金(22108108);中国博士后科学基金(2020M680065);香江学者计划(XJ2021021)

Construction of Z-Scheme MnO₂/BiOBr Heterojunction for Photocatalytic Ciprofloxacin Removal and CO₂ Reduction

Jintao Dong¹, Sainan Ji², Yi Zhang¹, Mengxia Ji¹, Bin Wang¹, Yingjie Li¹, Zhigang Chen², Jiexiang Xia¹^,*(), Huaming Li¹

¹ School of Chemistry and Chemical Engineering, Institute for Energy Research, Jiangsu University, Zhenjiang 212013, Jiangsu Province, China
² School of the Environment and Safety Engineering, Jiangsu University, Zhenjiang 212013, Jiangsu Province, China

Received:2022-12-06 Accepted:2023-02-17 Published:2023-02-28
Contact: Jiexiang Xia E-mail:xjx@ujs.edu.cn
Supported by:
the Postgraduate Research & Practice Innovation Program of Jiangsu Province(KYCX22_3692);the National Natural Science Foundation of China(21878134);the National Natural Science Foundation of China(22108106);the National Natural Science Foundation of China(22108108);the China Postdoctoral Science Foundation(2020M680065);the Hong Kong Scholar Program(XJ2021021)

摘要/Abstract

摘要：

日益严峻的能源短缺以及生态环境污染问题已成为引发全球持续关注的焦点问题，这严重影响了人类自身健康和社会可持续发展。多种技术被开发出来用于实现新能源开发和污染物控制，其中，光催化因其具有低耗能、无二次污染、操作流程简单、温和的反应条件等优点成为环境治理与能源催化领域的研究重点。不过值得注意的是，光催化技术尽管在抗生素的高效去除和CO₂还原领域的应用方兴未艾，但其工业化应用和大规模推广始终受限于光催化剂的光吸收效率、氧化还原能力和光生电子分离或迁移效率等诸多因素。基于当前光催化剂的组成/结构调控及其催化性能研究，探索高效实用的改性策略构筑性能更加优化的复合结构光催化剂，使光催化剂发挥出更高的光吸收/利用以及光催化表/界面反应性能是亟待解决的关键问题。在常见的改性策略中，Z型异质结构构筑不仅明显可以提高光吸收能力和显著降低光生电子空穴复合率，更重要的是，还可以保持光生电子/空穴的强还原/氧化能力来实现环境污染物去除和清洁能源转化。在本文中，采用机械辅助球磨法构建了MnO₂/BiOBr (MO/BiOBr) Z型异质结复合材料。在黑暗和光照条件下进行的原位X射线光电子能谱(XPS)测试可以证实MnO₂中的光生电子可以通过Mn³⁺/Mn⁴⁺氧化还原电对实现向BiOBr的定向迁移，以构建Z型载流子转移路径。通过电子自旋共振谱(ESR)和能带结构分析也可以推导出类似的结论。基于MnO₂中存在的Mn³⁺/Mn⁴⁺氧化还原电对以及MnO₂与BiOBr材料交错的能带位置，MnO₂和BiOBr材料可以构筑Z型异质结以实现氧化中心和还原中心的空间分离。此外，通过紫外可见光吸收光谱(UV-Vis DRS)和稳态荧光光谱(PL)分析相比较于BiOBr，MO/BiOBr复合材料具有增强的光吸收和显著降低的光生电子-空穴复合率。因此，MO/BiOBr复合材料表现出优异的光催化环丙沙星(CIP)氧化和CO释放性能。MO/BiOBr复合材料的CIP去除率在60 min时可达77.3%，是BiOBr(60.2%)的1.28倍。同时，MO/BiOBr复合材料(20.02 µmol∙g⁻¹∙h⁻¹)的光催化CO生成性能是BiOBr (9.08 µmol∙g⁻¹∙h⁻¹)的2.2倍。光电流和电化学阻抗分析表明，相比于MnO₂和BiOBr单体，构筑的MnO₂/BiOBr Z型异质结具有更高的界面电子转移效率。此外，选用液相质谱联用光谱(LC-MS)和原位傅里叶变换红外光谱(in situ FTIR)对光催化CIP去除和CO₂还原过程的中间体生成路径进行分析。并通过毒性评估软件(T.E.S.T.)计算CIP和在MO/BiOBr复合材料光催化降解CIP过程中产生的中间体对应的大型溞的48 h半数致死浓度、黑头软口鲦的96 h半数致死量、致突变性和生物累积因子来评估CIP和相应中间体的实际生理毒性。因此，本研究提供了一种简便方法来构筑Z型异质结以实现太阳能驱动的高效抗生素去除和燃料合成。

关键词: Z型异质结, BiOBr, 环丙沙星去除, 二氧化碳还原, 光催化

Abstract:

Rapid increase in energy shortage and ecological environmental pollution has become a major issue that has been continuously drawing global attention, because it severely affects human health and limits sustainable social development. Various technologies have been developed and used to rationalize the utilization of new energy sources and pollution control. Among these technologies, photocatalysis has become a research priority in the field of environmental governance and energy development. Advantages such as low energy consumption, no secondary pollution, simple operation methods, and mild reaction conditions make photocatalysis an attractive choice. Notably, although photocatalysis is a promising approach for enhancing antibiotic removal and CO₂ reduction efficiency, the industrialization and large-scale application of photocatalysts is limited because of issues such as low photo-absorption efficiency, redox capacity, and photogenerated electron separation or migration efficiency. The progress of current research on the regulation of composition/structure and performance of photocatalysts has promoted the exploration of efficient and practical modification strategies to construct photocatalyst composites with improved performance by facilitating light absorption/utilization and enhancing photocatalytic surface/interface reaction performance. Among the many common modification strategies, the construction of a Z-scheme heterojunction can enhance the light absorption ability and significantly reduce the recombination rate of photogenerated electron-hole pairs. Additionally, this strategy maintains the strong reduction/oxidation ability of photogenerated electrons/holes to facilitate the oxidation of environmental pollutants and conversion to clean energy. In this study, Z-scheme MnO₂/BiOBr (MO/BiOBr) composites were effectively constructed using a mechanically assisted ball-milling process. In situ X-ray photoelectron spectroscopy under dark and light conditions confirmed that photoexcited electrons in MnO₂ can migrate directionally to BiOBr through Mn³⁺/Mn⁴⁺ redox couple to create a Z-scheme transfer path. A similar conclusion can also be deduced from the results of electron spin-resonance spectroscopy and band structure analysis. The formation of a Z-scheme heterojunction between MnO₂ and BiOBr, attributed to the Mn³⁺/Mn⁴⁺ redox couple from MnO₂ and staggered energy band, enabled the space separation of oxidation and reduction centers. Furthermore, compared with BiOBr, MO/BiOBr composites exhibited enhanced light absorption and a markedly reduced photoinduced electron-hole pair recombination rate, as confirmed by ultraviolet-visible diffuse reflectance spectroscopy and photoluminescence spectroscopy. Thus, the MO/BiOBr composites exhibited exceptional photocatalytic performance toward ciprofloxacin (CIP) oxidation and CO evolution. The CIP removal efficiency of the MO/BiOBr composites reached 77.3% in just 60 min, which is 1.28 times higher than that of BiOBr (60.2%). Simultaneously, the photocatalytic CO₂-to-CO performance of the MO/BiOBr composites (20.02 µmol·g⁻¹·h⁻¹) was found to be 2.20-fold higher than that of BiOBr (9.08 µmol·g⁻¹·h⁻¹). Photocurrent measurement and electrochemical impedance spectroscopy indicated that the MnO₂/BiOBr Z-scheme heterojunction has higher interfacial electron transfer efficiency than pure MnO₂ and BiOBr. Additionally, liquid chromatograph mass spectrometry and in situ Fourier transform infrared spectroscopy is conducted to study the generation of intermediates during the photocatalytic CIP removal and CO₂ reduction process. The toxicity of CIP and corresponding intermediates after the photocatalytic degradation of the MO/BiOBr composites was evaluated using toxicity estimation software (T.E.S.T.) to analyze the actual physiological toxicity, based on indexes such as Daphnia Magna lethal concentration 50% (LC₅₀, 48 h), Fathead Minnow lethal dose 50% (LD₅₀, 96 h), mutagenicity, and bioaccumulation factor. Thus, this study proposed a novel and simplified approach for constructing a Z-scheme heterojunction to facilitate solar-derived antibiotic removal and fuel synthesis.

Key words: Z-scheme heterojunction, BiOBr, Ciprofloxacin removal, CO₂ reduction, Photocatalysis

董金涛, 季赛楠, 张屹, 季梦夏, 王彬, 李英杰, 陈志刚, 夏杰祥, 李华明. 构筑Z型MnO₂/BiOBr异质结用于光催化环丙沙星去除和CO₂还原[J]. 物理化学学报, 2023, 39(11), 2212011. doi: 10.3866/PKU.WHXB202212011

Jintao Dong, Sainan Ji, Yi Zhang, Mengxia Ji, Bin Wang, Yingjie Li, Zhigang Chen, Jiexiang Xia, Huaming Li. Construction of Z-Scheme MnO₂/BiOBr Heterojunction for Photocatalytic Ciprofloxacin Removal and CO₂ Reduction[J]. Acta Phys. -Chim. Sin. 2023, 39(11), 2212011. doi: 10.3866/PKU.WHXB202212011

链接本文: https://www.whxb.pku.edu.cn/CN/10.3866/PKU.WHXB202212011

https://www.whxb.pku.edu.cn/CN/Y2023/V39/I11/2212011

图/表 12

Fig 1

Fig 2

Fig 3

Fig 4

Fig 5

Table 1

Fig 6

Fig 7

Fig 8

Fig 9

Fig 10

Fig 11

参考文献 69

1	Wang L. ; Bahnemann D. W. ; Bian L. ; Dong G. H. ; Zhao J. ; Wang C. Y. Angew. Chem. Int. Ed. 2019, 58, 8103. doi: 10.1002/anie.201903027
2	Raziq F. ; Qu Y. ; Humayun M. ; Zada A. ; Yu H. ; Jing L. Q. Appl. Catal. B 2017, 201, 486. doi: 10.1016/j.apcatb.2016.08.057
3	Chen R. Y. ; Xia J. Z. ; Chen Y. G. ; Shi H. F. Acta Phys. -Chim. Sin. 2023, 39, 2209012.
	陈茹瑶; 夏加增; 陈义钢; 史海峰; 物理化学学报, 2023, 39, 2209012. doi: 10.3866/PKU.WHXB202209012
4	Chen G. Y. ; Yu Y. ; Liang L. ; Duan X. G. ; Li R. ; Lu X. K. ; Yan B. B. ; Li N. ; Wang S. B. J. Hazard. Mater. 2021, 408, 124461. doi: 10.1016/j.jhazmat.2020.124461
5	Dautzenberg F. M. ; Lu Y. ; Xu B. Acta Phys. -Chim. Sin. 2021, 37, 2008066.
	DautzenbergF. M.; 路勇; 徐彬; 物理化学学报, 2021, 37, 2008066. doi: 10.3866/PKU.WHXB202008066
6	Wang J. C. ; Qiao X. ; Shi W. N. ; He J. ; Chen J. ; Zhang W. Q. Acta Phys. -Chim. Sin. 2023, 39, 2210003.
	王吉超; 乔秀; 史维娜; 贺景; 陈军; 张万庆; 物理化学学报, 2023, 39, 2210003. doi: 10.3866/PKU.WHXB202210003
7	Li S. J. ; Dong X. ; Zhao Y. H. ; Mao J. N. ; Chen W. ; Chen A. H. ; Song Y. F. ; Li G. H. ; Jiang Z. ; Wei W. ; et al Angew. Chem. Int. Ed. 2022, 61, 2210432. doi: 10.1002/anie.202210432
8	Ru R. ; Zhang F. ; Sun K. H. ; Liu Z. Y. ; Xu W. Q. ; Stavitski E. ; Senanayake D. S. ; Rodriguez J. A. ; Liu C. J. ACS Catal. 2020, 10, 11307. doi: 10.1021/acscatal.0c02120
9	Liu S. ; Jin M. M. ; Sun J. Q. ; Qin Y. J. ; Gao S. S. ; Chen Y. ; Zhang S. S. ; Luo J. ; Liu X. J. Chem. Eng. J. 2022, 437, 135294. doi: 10.1016/j.cej.2022.135294
10	Wang B. ; Zhu X. W. ; Huang F. C. ; Quan Y. ; Liu G. P. ; Zhang X. L. ; Xiong F. Y. ; Huang C. ; Ji M. X. ; Li H. M. ; et al Appl. Catal. B 2022, 325, 122304. doi: 10.1016/j.apcatb.2022.122304
11	Zhang Y. ; Zhan G. P. ; Di J. ; Xia J. X. Curr. Opin. Green Sustain. Chem. 2023, 39, 100718. doi: 10.1016/j.cogsc.2022.100718
12	Zhu Q. H. ; Xu Q. ; Du M. M. ; Zeng X. F. ; Zhong G. F. ; Qiu B. C. ; Zhang J. L. Adv. Mater. 2022, 34, 2202929. doi: 10.1002/adma.202202929
13	Fu J. W. ; Jiang K. X. ; Qiu X. Q. ; Yu J. G. ; Liu M. Mater. Today 2020, 32, 222. doi: 10.1016/j.mattod.2019.06.009
14	Zhang L. Y. ; Zhang J. J. ; Yu H. G. ; Yu J. G. Adv. Mater. 2022, 34, 2107668. doi: 10.1002/adma.202107668
15	Liao G. F. ; Li C. X. ; Liu S. Y. ; Fang B. Z. ; Yang H. M. Trends Chem. 2022, 4, 111. doi: 10.1016/j.trechm.2021.11.005
16	Low J. X. ; Yu J. G. ; Jaroniec M. ; Wageh S. ; Al-Ghamdi A. A. Adv. Mater. 2017, 29, 1601694. doi: 10.1002/adma.201601694
17	Hu J. D. ; Chen D. Y. ; Mo Z. ; Li N. J. ; Xu Q. F. ; Li H. ; He J. H. ; Xu H. ; Lu J. M. Angew. Chem. Int. Ed. 2019, 58, 2073. doi: 10.1002/anie.201813417
18	Zan Z. Q. ; Li X. B. ; Gao X. M. ; Huang J. T. ; Luo Y. D. ; Han L. Acta Phys. -Chim. Sin. 2023, 39, 2209016.
	昝忠奇; 李喜宝; 高晓明; 黄军同; 罗一丹; 韩露; 物理化学学报, 2023, 39, 2209016. doi: 10.3866/PKU.WHXB202209016
19	Dong J. T. ; Chen F. ; Xu L. ; Yan P. C. ; Qian J. C. ; Chen Y. ; Yang M. Y. ; Li H. N. Microchem. J. 2022, 178, 107317. doi: 10.1016/j.microc.2022.107317
20	Liu G. P. ; Wang L. ; Chen X. ; Zhu X. W. ; Wang B. ; Xu X. Y. ; Chen Z. R. ; Zhu W. S. ; Li H. M. ; Xia J. X. Green Chem. Eng. 2022, 3, 157. doi: 10.1016/j.gce.2021.11.007
21	Wang F. ; Ma N. ; Zheng L. ; Zhang L. ; Bian Z. Y. ; Wang H. Chemosphere 2022, 307, 135666. doi: 10.1016/j.chemosphere.2022.135666
22	Zhao W. L. ; Wang W. L. ; Han T. Y. ; Wang H. T. ; Zhang H. C. ; Shi H. F. Sep. Purif. Technol. 2021, 269, 118693. doi: 10.1016/j.seppur.2021.118693
23	Mo Z. ; Xu H. ; Chen Z. G. ; She X. J. ; Song Y. H. ; Lian J. B. ; Zhu X. W. ; Yan P. C. ; Lei Y. C. ; Yuan S. Q. ; et al Appl. Catal. B 2019, 241, 452. doi: 10.1016/j.apcatb.2018.08.073
24	Dhingra S. ; Chhabra T. ; Krishnan V. ; Nagaraja C. M. ACS Appl. Energy Mater. 2020, 3, 7138. doi: 10.1021/acsaem.0c01189
25	Jin Y. ; Zou L. F. ; Liu L. L. ; Engelhard M. H. ; Patel R. L. ; Nie Z. M. ; Han K. S. ; Shao Y. Y. ; Wang C. M. ; Zhu J. ; et al Adv. Mater. 2019, 31, 1900567. doi: 10.1002/adma.201900567
26	Jiang Q. ; Ji M. X. ; Chen R. ; Zhang Y. ; Li K. ; Meng C. X. ; Chen Z. G. ; Li H. M. ; Xia J. X. J. Colloid Interface Sci. 2020, 574, 131. doi: 10.1016/j.jcis.2020.04.018
27	Zhang M. L. ; Duo F. F. ; Lan J. H. ; Li L. X. ; Zhou J. W. ; Chu L. L. ; Wang C. B. Appl. Surf. Sci. 2022, 583, 152544. doi: 10.1016/j.apsusc.2022.152544
28	Wang X. J. ; Yang W. Y. ; Li F. T. ; Zhao J. ; Liu R. H. ; Liu S. J. ; Li B. J. Hazard. Mater. 2015, 292, 126. doi: 10.1016/j.jhazmat.2015.03.030
29	Zhang G. Q. ; Cai L. ; Zhang Y. F. ; Wei Y. Chem. - Eur. J. 2018, 24, 7434. doi: 10.1002/chem.201706164
30	Wang B. ; Zhao J. Z. ; Chen H. L. ; Weng Y. X. ; Tang H. ; Chen Z. R. ; Zhu W. S. ; She Y. B. ; Xia J. X. ; Li H. M. Appl. Catal. B 2021, 293, 120182. doi: 10.1016/j.apcatb.2021.120182
31	Huang S. H. ; Wang Y. ; Wan J. Q. ; Yan Z. C. ; Ma Y. W. ; Zhang G. H. ; Wang S. L. Appl. Catal. B 2022, 319, 121913. doi: 10.1016/j.apcatb.2022.121913
32	Mu Y. F. ; Zhang W. ; Dong G. X. ; Su K. ; Zhang M. ; Lu T. B. Small 2020, 16, 2002140. doi: 10.1002/smll.202002140
33	Mu Y. F. ; Zhang C. ; Zhang M. R. ; Zhang W. ; Zhang M. ; Lu T. B. ACS Appl. Mater. Interfaces 2021, 13, 22314. doi: 10.1021/acsami.1c01718
34	Zhao Y. X. ; Chang C. ; Teng F. ; Zhao Y. F. ; Chen G. B. ; Shi R. ; Waterhouse G. I. N. ; Huang W. F. ; Zhang T. R. Adv. Energy Mater. 2017, 7, 1700005. doi: 10.1002/aenm.201700005
35	Mo Z. ; Wu G. Y. ; Yan P. C. ; Zhu X. W. ; Qian J. C. ; Lei Y. C. ; Xu L. ; Xu H. ; Li H. M. Mater. Today Chem. 2022, 25, 100956. doi: 10.1016/j.mtchem.2022.100956
36	Chen M. X. ; Dai Y. Z. ; Guo J. ; Yang H. T. ; Liu D. N. ; Zhai Y. L. Appl. Surf. Sci. 2019, 493, 1361. doi: 10.1016/j.apsusc.2019.04.160
37	Liu H. J. ; Wang B. J. ; Chen M. ; Zhang H. ; Peng J. B. ; Ding L. ; Wang W. F. Sep. Purif. Technol. 2021, 261, 118286. doi: 10.1016/j.seppur.2020.118286
38	Zhang D. ; Wu M. Q. ; Hao J. Y. ; Zheng S. L. ; Yang Y. ; Yao T. J. ; Wang Y. J. Colloid Interface Sci. 2022, 612, 550. doi: 10.1016/j.jcis.2021.12.152
39	Liu W. J. ; Wang S. ; Zhao Y. ; Sun C. X. ; Xu H. T. ; Zhao J. Z. J. Alloys Compd. 2021, 861, 157995. doi: 10.1016/j.jallcom.2020.157995
40	Ma Y. C. ; Chen Z. W. ; Qu D. ; Shi J. S. Appl. Surf. Sci. 2016, 361, 63. doi: 10.1016/j.apsusc.2015.11.130
41	Yan M. ; Hua Y. Q. ; Zhu F. F. ; Gu W. ; Jiang J. H. ; Shen H. Q. ; Shi W. D. Appl. Catal. B 2017, 202, 518. doi: 10.1016/j.apcatb.2016.09.039
42	Kandi D. ; Behera A. ; Sahoo S. ; Parida K. Sep. Purif. Technol. 2020, 253, 117523. doi: 10.1016/j.seppur.2020.117523
43	Liu G. P. ; Wang B. ; Zhu X. W. ; Ding P. H. ; Zhao J. Z. ; Li H. M. ; Chen Z. R. ; Zhu W. S. ; Xia J. X. Small 2021, 18, 2105228. doi: 10.1002/smll.202105228
44	Zhu B. C. ; Hong X. Y. ; Tang L. Y. ; Liu Q. Q. ; Tang H. Acta Phys. -Chim. Sin. 2022, 38, 2111008.
	朱弼辰; 洪小洋; 唐丽永; 刘芹芹; 唐华; 物理化学学报, 2022, 38, 2111008. doi: 10.3866/PKU.WHXB202111008
45	Wang B.; Zhang W.; Liu G. P.; Chen H. L. ; Weng Y. X. ; Li H. M. ; Chu P. K. ; Xia J. X. Adv. Funct. Mater. 2022, 32, 2202885. doi: 10.1002/adfm.202202885
46	Gao M. C. ; Yang J. X. ; Sun T. ; Zhang Z. Z. ; Zhang D. F. ; Huang H. J. ; Lin H. X.; Fang Y.; Wang X. X. Appl. Catal. B 2019, 234, 734. doi: 10.1016/j.apcatb.2018.11.020
47	Sun N. C. ; Zhou M. ; Ma X. X. ; Cheng Z. H. ; Wu J. ; Qi Y. F. ; Sun Y. J. ; Zhou F. H. ; Shen Y. X. ; Lu S. Y. J. CO₂ Util. 2022, 65, 102220. doi: 10.1016/j.jcou.2022.102220
48	Zhao X. Z. ; Xia Y. G. ; Li H. P. ; Wang X. ; Wei J. ; Jiao X. L. ; Chen D. R. Appl. Catal. B 2021, 297, 120426. doi: 10.1016/j.apcatb.2021.120426
49	Li D. S. ; Zhu B. C. ; Sun Z. T. ; Liu Q. Q. ; Wang L. L. ; Tang H. Front. Chem. 2021, 9, 804204. doi: 10.3389/fchem.2021.804204
50	Bai Y. ; Chen T. ; Wang P. Q. ; Wang L. ; Ye L. Q. ; Shi X. ; Bai W. Sol. Energy Mater. Sol. Cells 2016, 157, 406. doi: 10.1016/j.solmat.2016.07.001
51	Jin X. L. ; Cao J. ; Wang H. Q. ; Lv C. D. ; Xie H. Q. ; Su F. Y. ; Li X. ; Sun R. X. ; Shi S. K. ; Dang M. F. ; et al Appl. Surf. Sci. 2022, 598, 153758. doi: 10.1016/j.apsusc.2022.153758
52	Wu D. ; Ye L. Q. ; Yip H. Y. ; Wong P. Y. Catal. Sci. Technol. 2017, 7, 265. doi: 10.1039/c6cy02040b
53	Jin X. L. ; Lv C. D. ; Zhou X. ; Xie H. Q. ; Sun S. F. ; Liu Y. ; Meng Q. Q. ; Chen G. Nano Energy 2019, 4, 103955. doi: 10.1016/j.nanoen.2019.103955
54	Yan X. W. ; Wang B. ; Zhao J. Z. ; Liu G. P. ; Ji M. X. ; Zhang X. L. ; Chu P. K. ; Li H. M. ; Xia J. X. Chem. Eng. J. 2023, 452, 139271. doi: 10.1016/j.cej.2022.139271
55	Liu D. N. ; Chen D. Y. ; Li N. J. ; Xu Q. F. ; Li H. ; He J. H. ; Lu J. M. Angew. Chem. Int. Ed. 2020, 59, 4519. doi: 10.1002/anie.201914949
56	Gao S. ; Gu B. C. ; Jiao X. C. ; Sun Y. F. ; Zu X. L. ; Yang F. ; Zhu W. G. ; Wang C. M. ; Feng Z. M. ; Ye B. J. ; et al J. Am. Chem. Soc. 2017, 139, 3438. doi: 10.1021/jacs.6b11263
57	Zhao J. ; Nan J. ; Zhao Z. ; Li N. ; Liu J. ; Cui F. Appl. Catal. B 2017, 202, 509. doi: 10.1016/j.apcatb.2016.09.065
58	Yu L. M. ; Mo Z. ; Zhu X. L. ; Deng J. J. ; Xu F. ; Song Y. H. ; She Y. B. ; Li H. M. ; Xu H. Green Energy Environ. 2021, 6, 538. doi: 10.1016/j.gee.2020.05.011
59	Guo J. R. ; Wang L. P. ; Wei X. ; Alothman Z. A. ; Albaqami M. D. ; Malgras V. ; Yamauchi Y. ; Kang Y. Q. ; Wang M. Q. ; Guan W. S. ; et al J. Hazard. Mater. 2020, 415, 125591. doi: 10.1016/j.jhazmat.2021.125591
60	Wen X. J. ; Lu Q. ; Lv X. X. ; Sun J. ; Guo J. ; Fei Z. H. ; Niu Z. G. J. Hazard. Mater. 2020, 385, 121508. doi: 10.1016/j.jhazmat.2019.121508
61	Chen Y. ; Xu L. ; Yang M. Y. ; Jia Y. F. ; Yan Y. T. ; Qian J. C. ; Chen F. ; Li H. N. Sens. Actuators B 2022, 353, 131187. doi: 10.1016/j.snb.2021.131187
62	Li L. L. ; Zheng X. Y. ; Chi Y. H. ; Wang Y. ; Sun X. ; Yue Q. Y. ; Gao B. Y. ; Xu S. P. J. Hazard. Mater. 2020, 383, 121211. doi: 10.1016/j.jhazmat.2019.121211
63	Sarkhosh M. ; Sadani M. ; Abtahi M. ; Mohseni S. M. ; Sheikhmohammadi A. ; Azarpira H. ; Najafpoor A. A. ; Atafar Z. ; Rezaei S. ; Alli R. ; et al J. Hazard. Mater. 2019, 377, 418. doi: 10.1016/j.jhazmat.2019.05.090
64	Liu C. ; Mao S. ; Shi M. X. ; Wang F.Y. ; Xia M. Z. ; Chen Q. ; Ju X. H. J. Hazard. Mater. 2021, 420, 126613. doi: 10.1016/j.jhazmat.2021.126613
65	Yi X. H. ; Ji H. D. ; Wang C. C. ; Li Y. ; Li Y. H. ; Zhao C. ; Wang A. ; Fu H. F. ; Wang P. ; Zhao X. ; et al Appl. Catal. B 2021, 293, 120229. doi: 10.1016/j.apcatb.2021.120229
66	Wang F. ; Liu S. S. ; Feng Z. Y. ; Fu H. F. ; Wang M. Y. ; Wang P. ; Liu W. ; Wang C. C. J. Hazard. Mater. 2022, 440, 129723. doi: 10.1016/j.jhazmat.2022.129723
67	Li J. ; Ye Y. H. ; Ye L. Q. ; Su S. Y. ; Ma Z. Y. ; Huang J. D. ; Xie H. Q. ; Doronkin D. E. ; Zimina A. ; Grunwaldt J. D. ; et al J. Mater. Chem. A 2019, 7, 2821. doi: 10.1039/C8TA10922B
68	Liang J. L. ; Zhang W. ; Liu Z. Y. ; Song Q. Q. ; Zhu Z. H. ; Guan Z. Q. ; Wang H. Y. ; Zhang P. J. ; Li J. ; Zhou M. ; et al ACS Catal. 2022, 12, 12217. doi: 10.1021/acscatal.2c03970
69	Li H. ; Li F. ; Yu J. G. ; Cao S. W. Acta Phys. -Chim. Sin. 2021, 37, 2010073.
	李瀚; 李芳; 余家国; 曹少文; 物理化学学报, 2021, 37, 2010073. doi: 10.3866/PKU.WHXB202010073

Photocatalyst	CIP (mg∙L⁻¹)	Removal rate (%)	References
biochar@ZnFe₂O₄/BiOBr	15	60.0% at 60 min	36
BiOAc/BiOBr	10	75% at 120 min	37
Vo-BiOBr/Bi₂Sn₂O₇	10	77.4% at 120 min	38
Bi₂S₃/BiOCl	10	70.0% at 180 min	39
BiOCl@Bi₂WO₆	10	65.0% at 300 min	40
NGQDs-BiOI/MnNb₂O₆	20	57.4% at 120 min	41
BOI-CBBMO-3	20	75.0% at 60 min	42
MnO₂/BiOBr	20	77.3% at 60 min	This work

[1]	陈轼逸, 付家龙, 裘建平, 常国菊, 郝仕油. 废弃医用口罩衍生的碳量子点增强BiOBr/g-C₃N₄ S型异质结光催化降解聚对苯二甲酸乙二醇酯(PET)[J]. 物理化学学报, 2026, 42(1): 100135 - .
[2]	黄火帅, 韦之栋, 严嘉玮, 池家晟, 苏千翔, 陈铭夏, 江治, 孙洋洲, 上官文峰. 揭示Zn_xCd_1−xS固溶体光催化析氢中的直接-间接带隙跃迁机制[J]. 物理化学学报, 2026, 42(1): 100141 - .
[3]	赵呈孝, 李昭霖, 吴东方, 杨小飞. SBA-15模板化共价三嗪框架增强光催化产氢[J]. 物理化学学报, 2026, 42(1): 100149 - .
[4]	陈芸, 邓代洁, 徐丽, 朱兴旺, 李赫楠, 孙成明. 共价键调控电荷转移以实现自供能电化学传感平台对重金属离子的灵敏分析[J]. 物理化学学报, 2026, 42(1): 100144 - .
[5]	洪佳楠, 许辰宇, 刘烟, 黎昌棋, 王梦琳, 张彦威. 通过边缘活性位点调控解析光热催化中析氢与二氧化碳还原的界面竞争[J]. 物理化学学报, 2025, 41(9): 100099 - .
[6]	韦梦兰, 欧晓霞, 王艺濛, 张梦圆, 滕飞, 王凯旋. S型异质结g-C₃N₄/Bi₂WO₆高效降解左氧氟沙星：性能、机理及降解路径[J]. 物理化学学报, 2025, 41(9): 100105 - .
[7]	李静萍, 严素定, 吴佳曦, 程强, 王楷. LiFePO₄改善无机/有机S型光催化剂的过氧化氢光合作用[J]. 物理化学学报, 2025, 41(9): 100104 - .
[8]	吴琦, 王长华, 李莹莹, 张昕彤. 增强g-C₃N₄@BN范德华异质结界面上的三重态电子转移增强光催化合成H₂O₂[J]. 物理化学学报, 2025, 41(9): 100107 - .
[9]	张凤英, 梅杨林, 蒋毓蔓, 郑申申, 郑凯波, 周莹. 瞬态吸收光谱在太阳能转化利用中的研究进展[J]. 物理化学学报, 2025, 41(9): 100118 - .
[10]	王文龙, 郝文韬, 何浪, 乔佳, 李宁, 陈朝秋, 覃勇. 碳量子点/TiO₂ S型异质结的能带和吸附工程促进光催化CO₂甲烷化[J]. 物理化学学报, 2025, 41(9): 100116 - .
[11]	蔡家杰, 程畅, 刘博文, 张建军, 姜传佳, 程蓓. CdS/DBTSO-BDTO S型异质结光催化制氢及其电荷转移动力学[J]. 物理化学学报, 2025, 41(8): 100084 - .
[12]	袁乐汪, 彭垚垚, 管宗杰, 方煜. 二维共价有机框架作为光催化剂在有机合成中的研究进展[J]. 物理化学学报, 2025, 41(8): 100086 - .
[13]	王玉, 石海洋, 陈子涵, 陈峰, 王苹, 王雪飞. 具有富电子Pt^δ−壳层的空心AgPt@Pt核壳催化剂：提升光催化H₂O₂生成选择性与活性[J]. 物理化学学报, 2025, 41(7): 100081 - .
[14]	刘方璇, 刘子妍, 周国伟, 高婷婷, 刘文宇, 孙彬. 中空结构光催化剂[J]. 物理化学学报, 2025, 41(7): 100071 - .
[15]	罗雅丹, 郑浩, 李鑫, 李锋民, 唐华, 佘希林. 调节O, S共掺杂C₃N₄中的活性氧生成以促进光催化降解微塑料[J]. 物理化学学报, 2025, 41(6): 100052 - .

构筑Z型MnO₂/BiOBr异质结用于光催化环丙沙星去除和CO₂还原

Construction of Z-Scheme MnO₂/BiOBr Heterojunction for Photocatalytic Ciprofloxacin Removal and CO₂ Reduction

RichHTML

PDF

赞

可视化

摘要/Abstract

引用本文

使用本文

图/表 12

参考文献 69

相关文章 15

Metrics

推荐阅读 0