Preparation of Functional Polymer Nanomaterial and Its Catalytic Property

SHE Shi-Xiong; SU Bi-Tao; YANG Yan; MIN Shi-Xiong; LEI Zi-Qiang   

  1. Key Laboratory of Eco-Environment-Related Polymer Materials of the Ministry of Education, Key Laboratory of Gansu Polymer Materials, College of Chemistry and Chemical Engineering, Northwest Normal University, Lanzhou 730070, P. R. China; College of Science, Shenyang Agriculture Uuniversity, Shenyang 110161, P. R. China

  • Received:2006-11-13 Revised:2007-01-29 Published:2007-06-04
  • Contact: SU Bi-Tao E-mail:subt0608@sina.com

PDF

4509

Like

Abstract:

After properly heat-activating the polymers poly(furancarbinol-co-phenol) (PFP-0) and polyparaphenylene (PPP-0), two new functional polymer nanomaterials, PFP and PPP were obtained. Their properties as catalysts in water pollution treatment were studied. The samples were determined by means of DTA-TG, TEM, FT-IR, and UV-Vis. The results showed that under natural light and air conditions, dye methylene blue (MB) could be almost fully degraded and largely mineralized on them within a few minutes; the variation of the conjugation structure had great influence on their stabilities; compared with each other, the existence of polar groups was found to be decisive factor to the catalytic properties.

Key words: Functional polymer, Nanomaterial, Preparation, Catalytic property