在气液界面上压缩诱导聚(L-乳酸)膜的结构变化

doi:10.3866/PKU.WHXB201504013

物理化学学报 >> 2015, Vol. 31 >> Issue (6): 1162-1168.doi: 10.3866/PKU.WHXB201504013

在气液界面上压缩诱导聚(L-乳酸)膜的结构变化

王丽, 季姗, 陈启斌, 刘洪来

华东理工大学化学系, 化学工程国家重点实验室, 上海200237

收稿日期:2015-01-29 修回日期:2015-04-01 发布日期:2015-06-05
通讯作者: 陈启斌 E-mail:qibinchen@ecust.edu.cn
基金资助:
国家自然科学基金(21273074)及中央高校基本科研业务费专项资金资助项目

Structural Transition of Poly(L-lactic acid) Film Induced by Compression at Air/Water Interface

WANG Li, JI Shan, CHEN Qi-Bin, LIU Hong-Lai

State Key Laboratory of Chemical Engineering, Department of Chemistry, East China University of Science and Technology, Shanghai 200237, P. R. China

Received:2015-01-29 Revised:2015-04-01 Published:2015-06-05
Contact: CHEN Qi-Bin E-mail:qibinchen@ecust.edu.cn
Supported by:
The project was supported by the National Natural Science Foundation of China (21273074) and Fundamental Research Funds for the Central Universities of China.

摘要/Abstract

摘要：

聚乳酸(PLA)是一种环境友好及生物可降解的聚合物, 其界面性质受到了广泛关注. 本文以Langmuir-Blodgett (LB)膜天平、原子力显微镜(AFM)研究了聚(L-乳酸) (PLLA)在气液界面上的性质. 表面压-面积(π-A)等温曲线的结果表明, 在膜压缩的初始阶段, 表面压逐渐增大; 当膜压为9.0 mN·m^-1时, 曲线出现了一个平台,其重复单元的面积大约在0.11-0.17 nm²之间. 原子力显微镜的结果发现, 在压缩过程中, 膜结构发生了明显的变化: 平台刚出现时, 膜内出现了大量的纤维结构; 在平台区内, 界面上出现了多层膜结构. 特别地, 当表面压为20.0 mN·m^-1时, PLLA在界面上可形成约6.0 nm厚的薄膜. 由此可见, PLLA等温线中的平台与其膜结构的变化紧密相关. 这有别于普通双亲分子的性质, 即这类双亲分子π-A等温线中的平台通常表示它们在二维空间上发生了单分子膜的相转变.

关键词: 聚(L-乳酸), 界面, 单分子膜, 相转变, 结构特征

Abstract:

Poly(lactic acid) (PLA) has attracted considerable interest as an environmentally friendly and biodegradable polymer. The properties of poly(L-lactic acid) (PLLA) at an air/water interface were studied based on the Langmuir-Blodgett (LB) film balance and atomic force microscopy (AFM). The surface pressure-area (π-A) isotherm indicated that the surface pressure of PLLA initially increased as the interfacial film was compressed; at π=9.0 mN·m^-1, a plateau was observed in the π-A isotherm, in which the area of the repeat unit was in the approximate range 0.11-0.17 nm². The AFM results showed that there is a clear structural transition in the PLLA film during the compression: (i) at the beginning of the plateau, a number of fibrils are present at the air/water interface and (ii) multilayer structures (at least bilayer, i.e., the underlying layer and top layer consisting of fibrils) is formed in the plateau region. In particular, when π=20.0 mN·m^-1, a thin film of PLLA of thickness about 6.0 nm was fabricated. Our findings suggest that the plateau in the PLLA π-A isotherm is closely related to a change in the film structure from monolayer to multilayer at the air/water interface. This is significantly different from the behavior of conventional amphiphiles, because the plateau in amphiphiles π-A isotherm is equivalent to a phase transition of monolayers derived from amphiphiles in a two-dimensional plane.

Key words: Poly(L-lactic acid), Interface, Monomolecular film, Phase transition, Structure characteristic

点击下载补充材料PDF格式文件

王丽, 季姗, 陈启斌, 刘洪来. 在气液界面上压缩诱导聚(L-乳酸)膜的结构变化[J]. 物理化学学报, 2015, 31(6), 1162-1168. doi: 10.3866/PKU.WHXB201504013

WANG Li, JI Shan, CHEN Qi-Bin, LIU Hong-Lai. Structural Transition of Poly(L-lactic acid) Film Induced by Compression at Air/Water Interface[J]. Acta Phys. -Chim. Sin. 2015, 31(6), 1162-1168. doi: 10.3866/PKU.WHXB201504013

链接本文: https://www.whxb.pku.edu.cn/CN/10.3866/PKU.WHXB201504013

https://www.whxb.pku.edu.cn/CN/Y2015/V31/I6/1162

参考文献

(1) Langer, R.; Tirrell, D. A. Nature 2004, 428, 487. doi: 10.1038/nature02388
(2) Ha, C.; Gardella, J. A., Jr. Chem. Rev. 2005, 105, 4205. doi: 10.1021/cr040419y
(3) Lee, W.; Iwata, T.; Gardella, J. A., Jr. Langmuir 2005, 21, 11180. doi: 10.1021/la051137b
(4) Fischer, A. M.; Frey, H. Macromolecules 2010, 43, 8539. doi: 10.1021/ma101710t
(5) Kawalec, M.; Adamus, G.; Kurcok, P.; Kowalczuk, M.; Foltran, I.; Focarete, M. L.; Scandola, M. Biomacromolecules 2007, 8, 1054. doi: 10.1021/bm061155n
(6) Kulinski, Z.; Piorkowska, E. Polymer 2005, 46, 10290. doi: 10.1016/j.polymer.2005.07.101
(7) Urayama, H.; Kanamori, T.; Fukushima, K.; Kimura, Y. Polymer 2003, 44, 5635. doi: 10.1016/S0032-3861(03)00583-4
(8) Hu, J.; Sun, X.; Ma, H.; Xie, C.; Chen, Y. E.; Ma, P. X. Biomaterials 2010, 31, 7971. doi: 10.1016/j.biomaterials.2010.07.028
(9) Shao, J.; Wang, Y.; Chen, X.; Hu, X.; Du, C. Colloids Surf. B 2014, 120, 97. doi: 10.1016/j.colsurfb.2014.05.021
(10) Ni, S.; Lee, W.; Li, B.; Esker, A. R. Langmuir 2006, 22, 3672. doi: 10.1021/la060084a
(11) Fukuhira, Y.; Kitazono, E.; Hayashi, T.; Kaneko, H.; Tanaka, M.; Shimomura, M.; Sumi, Y. Biomaterials 2006, 27, 1797. doi: 10.1016/j.biomaterials.2005.10.019
(12) Petty, M. C. Langmuir-Blodgett Films: An Introduction; Cambridge University Press: Cambridge, 1996; pp 1-37.
(13) Gaines, G. L.; Roberts, G. Insoluble Monolayers at Liquid-Gas Interfaces; JohnWiley & Sons, Inc.: New York, 1966; pp 136-202.
(14) Ulman, A. An Introduction to Ultrathin Organic Films: From Langmuir-Blodgett to Self-Assembly; Academic Press: Boston, 1991; pp 101-105.
(15) Penner, T. L.; Motschmann, H. R.; Armstrong, N. J.; Ezenyilimba, M. C.; Williams, D. J. Nature 1994, 367, 49. doi: 10.1038/367049a0
(16) Allen, D.; Westerblad, H. Science 2004, 305, 1112. doi: 10.1126/science.1103078
(17) Wijekoon, W. M. K. P.; Wijaya, S. K.; Bhawalkar, J. D.; Prasad, P. N.; Penner, T. L.; Armstrong, N. J.; Ezenyilimba, M. C.; Williams, D. J. J. Am. Chem. Soc. 1996, 118, 4480. doi: 10.1021/ja953974d
(18) Pelletier, I.; Pézolet, M. Macromolecules 2004, 37, 4967. doi: 10.1021/ma035949v
(19) Bourque, H.; Laurin, I.; Pézolet, M.; Klass, J. M.; Lennox, R. B.; Brown, G. R. Langmuir 2001, 17, 5842. doi: 10.1021/la0009792
(20) Klass, J. M.; Lennox, R. B.; Brown, G. R.; Bourque, H.; Pézolet, M. Langmuir 2003, 19, 333. doi: 10.1021/la020606w
(21) Sato, G.; Nishitsuji, S.; Kumaki, J. J. Phys. Chem. B 2013, 117, 9067. doi: 10.1021/jp403195g
(22) Gurarslan, A.; Tonelli, A. E. Macromolecules 2011, 44, 3856. doi: 10.1021/ma200530w
(23) Bjørnholm, T.; Greve, D. R.; Reitzel, N.; Hassenkam, T.; Kjaer, K.; Howes, P. B.; Larsen, N. B.; Bøgelund, J.; Jayaraman, M.; Ewbank, P. C.; McCullough, R. D. J. Am. Chem. Soc. 1998, 120, 7643. doi: 10.1021/ja981077e
(24) Casillas-Ituarte, N. N.; Chen, X.; Castada, H.; Allen, H. C. J. Phys. Chem. B 2010, 114, 9485. doi: 10.1021/jp1022357
(25) Picas, L.; Suárez-Germà, C.; Teresa Montero, M.; Domènech, Ò.; Hernández-Borrell, J. Langmuir 2012, 28, 701. doi: 10.1021/la203795t
(26) Romão, R. I. S.; Ferreira, Q.; Morgado, J.; Martinho, J. M. G.; Gonçalves da Silva, A. M. P. S. Langmuir 2010, 26, 17165. doi: 10.1021/la103029d
(27) Genson, K. L.; Vaknin, D.; Villacencio, O.; McGrath, D. V.; Tsukruk, V. V. J. Phys. Chem. B 2002, 106, 11277. doi: 10.1021/jp026244i
(28) Fang, J.; Knobler, C. M.; Gingery, M.; Eiserling, F. A. J. Phys. Chem. B 1997, 101, 8692. doi: 10.1021/jp971057j
(29) Wang, M. H.; Janout, V.; Regen, S. L. Langmuir 2012, 28, 4614. doi: 10.1021/la204985d
(30) Perepichka, I. I.; Borozenko, K.; Badia, A.; Bazuin, C. G. J. Am. Chem. Soc. 2011, 133, 19702. doi: 10.1021/ja209502d
(31) De Santis, P.; Kovacs, A. J. Biopolymers 1968, 6, 299. doi: 10.1002/bip.1968.360060305
(32) Okihara, T.; Tsuji, M.; Kawaguchi, A.; Katayama, K. I.; Tsuju, H.; Hyon, S. H.; Ikada, Y. J. Macromol. Sci. Phys. B 1991, 30, 119. doi: 10.1080/00222349108245788

[1]	霍春安, 邱圣杰, 梁青满, 耿碧君, 雷志超, 王干, 邹玉玲, 田中群, 杨扬. 光镊捕获和操控尺度极限的进展[J]. 物理化学学报, 2024, 40(1): 2303037 - .
[2]	雷淦昌, 郑勇, 曹彦宁, 沈丽娟, 王世萍, 梁诗景, 詹瑛瑛, 江莉龙. 钾改性氧化铝基羰基硫水解催化剂及其失活机理[J]. 物理化学学报, 2023, 39(9): 2210038 -0 .
[3]	赵永智, 陈晨阳, 刘文燚, 胡伟飞, 刘金平. 固态锂电池界面优化策略的研究进展[J]. 物理化学学报, 2023, 39(8): 2211017 -0 .
[4]	陈瑶, 陈存, 曹雪松, 王震宇, 张楠, 刘天西. CO₂和N₂电还原中缺陷及界面工程的最新进展[J]. 物理化学学报, 2023, 39(8): 2212053 -0 .
[5]	刘元凯, 余涛, 郭少华, 周豪慎. 高性能硫化物基全固态锂电池设计：从实验室到实用化[J]. 物理化学学报, 2023, 39(8): 2301027 -0 .
[6]	刘欢, 马宇, 曹斌, 朱奇珍, 徐斌. MXenes在水系锌离子电池中的应用研究进展[J]. 物理化学学报, 2023, 39(5): 2210027 -0 .
[7]	汪茹, 刘志康, 严超, 伽龙, 黄云辉. 高安全锂离子电池复合集流体的界面强化[J]. 物理化学学报, 2023, 39(2): 2203043 -0 .
[8]	王文亮, 张灏纯, 陈义钢, 史海峰. 具有光催化与光芬顿反应协同作用的2D/2D α-Fe₂O₃/g-C₃N₄ S型异质结用于高效降解四环素[J]. 物理化学学报, 2022, 38(7): 2201008 - .
[9]	宋雨珂, 谢文富, 邵明飞. 一体化电极电催化二氧化碳还原研究进展[J]. 物理化学学报, 2022, 38(6): 2101028 - .
[10]	朱思颖, 李辉阳, 胡忠利, 张桥保, 赵金保, 张力. 锂离子电池氧化亚硅负极结构优化和界面改性研究进展[J]. 物理化学学报, 2022, 38(6): 2103052 - .
[11]	孙轲, 赵永青, 殷杰, 靳晶, 刘翰文, 席聘贤. 有机配体表面改性NiCo₂O₄纳米线用于水全分解[J]. 物理化学学报, 2022, 38(6): 2107005 - .
[12]	殷宇豪, 沈阳, 王虎, 陈肖, 邵林, 华文宇, 王娟, 崔义. TiN/Hf_xZr_1-xO₂/TiN铁电电容器的原位生长与表征[J]. 物理化学学报, 2022, 38(5): 2006016 - .
[13]	俞宏伟, 李实, 李金龙, 朱韶华, 孙成珍. 气驱油油气混相过程的界面传质特性及其分子机制[J]. 物理化学学报, 2022, 38(5): 2006061 - .
[14]	刘苗苗, 王文娟, 郝秀萍, 董晓燕. Aβ40和hIAPP在溶液和表面的成核与交叉成核聚集行为[J]. 物理化学学报, 2022, 38(3): 2002024 - .
[15]	常明凯, 胡娜, 李遥, 鲜东帆, 周万强, 王静一, 时燕琳, 刘春立. Eu(Ⅲ)在蒙脱石上的吸附及碳酸根和磷酸根对其吸附的影响[J]. 物理化学学报, 2022, 38(3): 2003031 - .

在气液界面上压缩诱导聚(L-乳酸)膜的结构变化

Structural Transition of Poly(L-lactic acid) Film Induced by Compression at Air/Water Interface

PDF

赞

可视化

摘要/Abstract

支持信息

引用本文

使用本文

参考文献

相关文章 15

Metrics

推荐阅读 0