Phase Separation and Acid Etching of Sodium Borosilicate Glasses Studied by NMr

Ren Hai-Lan,Yue Yong,Ye Chao-Hui,Tan Guo-Hua,Yuan qi-Hua   

  1. Laboratory of Nuclear Magnetic Resonance and Atomic and Molecular Physics,Wuhan Institute of Physics,Academia simica,Wuhan 430071|Advanced Materials Institute,Wuhan University of Technology,Wuhan 430070
  • Received:1996-10-07 Revised:1997-01-13 Published:1997-06-15
  • Contact:

PDF

3139

Like

Abstract:

Multinuclear solid-state NMR, including (29)Si、(23)Na、(11)B MAS and （29）Si CP/MAS NMR was employed to study the structure change of Na2O-B2O3-SiO2 glasses after 24 hour heat-treatment of phase separation at different temperatures. Then the glasses were etched with acid. The results show that there is a turning point temperature. Being confined by dynamical factors, phase separation did not reach equilibrium below this temperature. The degree of phase separation was reduced when the temperature was decreased. When the temperature was above this turning temperature, the phase separation could reach equilibrium. Being controlled by thermodynamics, the degree of mtiscibility was enhanced when the temperature was increased. The phase separation was the best when the heat-treatment of phase separation was proceeded at this turning temperature. The NMR results obtained from different resonant nuclei were consistent with one another.

Key words: Sodium borosilicate, Phase separation, Etching, NMR