ZrO2负载Pt 催化巴豆醛选择性加氢

doi:10.3866/PKU.WHXB20101216

物理化学学报 >> 2010, Vol. 26 >> Issue (12): 3273-3277.doi: 10.3866/PKU.WHXB20101216

ZrO₂负载Pt 催化巴豆醛选择性加氢

郑海影, 谢冠群, 王晓霞, 金凌云, 罗孟飞

浙江师范大学物理化学研究所, 浙江省固体表面反应化学重点实验室, 浙江金华321004

收稿日期:2010-07-16 修回日期:2010-09-19 发布日期:2010-12-01
通讯作者: 罗孟飞 E-mail:mengfeiluo@zjnu.cn
基金资助:
浙江省自然科学基金(Y4100300)资助项目

Selective Hydrogenation of Crotonaldehyde over ZrO₂-Supported Pt Catalysts

ZHENG Hai-Ying, XIE Guan-Qun, WANG Xiao-Xia, JIN Ling-Yun, LUO Meng-Fei

Zhejiang Key Laboratory for Reactive Chemistry on Solid Surfaces, Institute of Physical Chemistry, Zhejiang Normal University, Jinhua 321004, Zhejiang Province, P. R. China

Received:2010-07-16 Revised:2010-09-19 Published:2010-12-01
Contact: LUO Meng-Fei E-mail:mengfeiluo@zjnu.cn
Supported by:
The project was supported by the Zhejiang Provincial Natural Science Foundation (Y4100300).

摘要/Abstract

摘要：

以高比表面积ZrO₂为载体, 采用浸渍法制备了负载型Pt 催化剂, 应用于常压下气相巴豆醛加氢反应,考察了Pt 负载量和H₂还原温度等对巴豆醛选择性加氢性能的影响. 实验结果表明, Pt 负载量(质量分数)为3%的3Pt/ZrO₂催化剂经500 ℃还原后, 具有较高的巴豆醛选择性加氢性能: 巴豆醛转化率为27%, 巴豆醇的选择性为55%. X射线粉末衍射(XRD)分析, CO化学吸附, NH₃程序升温脱附(NH₃-TPD)表征结果表明Pt/ZrO₂催化剂上Lewis强酸中心和适宜的Pt颗粒(约为8 nm)有利于巴豆醛选择性加氢生成巴豆醇.

关键词: 加氢, Pt/ZrO₂催化剂, 高比表面积ZrO₂, 巴豆醇, Lewis酸, Pt粒子大小

Abstract:

Pt catalysts supported on high specific surface area ZrO₂ were prepared by the impregnation method and applied to the hydrogenation of crotonaldehyde in the gas phase at atmospheric pressure. The effects of Pt loading and reduction temperature on the catalytic properties of the Pt/ZrO₂ catalysts were investigated. It was found that the 3Pt/ZrO₂ catalyst with a mass fraction of 3% Pt and at a reduction temperature of 500 °C exhibited favorable catalytic performance for the selective hydrogenation of crotonaldehyde. The selectivity for crotyl alcohol reached 55% at 27% crotonaldehyde conversion. The catalysts were characterized by X-ray powder diffraction (XRD), CO chemisorption, and NH₃ temperature programmed desorption (NH₃-TPD). The results indicated that the catalytic performance depended on the strong Lewis acidic sites on the catalyst surface and a proper Pt particle size of ca 8 nm for the selective hydrogenation of crotonaldehyde to crotyl alcohol.

Key words: Hydrogenation, Pt/ZrO₂ Catalyst, High specific surface area ZrO₂, Crotyl alcohol, Lewis acid, Particle size of Pt

郑海影, 谢冠群, 王晓霞, 金凌云, 罗孟飞. ZrO₂负载Pt 催化巴豆醛选择性加氢[J]. 物理化学学报, 2010, 26(12), 3273-3277. doi: 10.3866/PKU.WHXB20101216

ZHENG Hai-Ying, XIE Guan-Qun, WANG Xiao-Xia, JIN Ling-Yun, LUO Meng-Fei. Selective Hydrogenation of Crotonaldehyde over ZrO₂-Supported Pt Catalysts[J]. Acta Phys. -Chim. Sin. 2010, 26(12), 3273-3277. doi: 10.3866/PKU.WHXB20101216

链接本文: https://www.whxb.pku.edu.cn/CN/10.3866/PKU.WHXB20101216

https://www.whxb.pku.edu.cn/CN/Y2010/V26/I12/3273

参考文献

1. Milone, C.; Ingoglia, R.; Schipilliti, L. ; Crisafulli, C.; Neri, G.; Galvagno, S. J. Catal., 2005, 236: 80
2. Mertens, P. G. N.; Vandezande, P.; Ye, X. P.; Poelman, H. Appl. Catal. A: Gen., 2009, 335: 176
3. Kliewer, C.; J. Bieri, M.; Somorjai, G. A. J. Am. Chem. Soc., 2009, 131: 9958
4. Claus, P.; Hofmeister, H. J. Phys. Chem. B, 1999, 103: 2766
5. Gebauer-Henke, E.; Grams, J.; Szubiakiewicz, E.; Farbotko, J.; Touroude, R.; Rynkowski, J. J. Catal., 2007, 250: 195
6. Ramos-Ferández, E.V.; Sepúlveda-Escribano, A.; Rodríguez-Reinoso, F. Catal. Commun., 2008, 9: 1243
7. Yang, Q. Y.; Zhu, Y., Tian, L.; Pei, Y.; Qian M. H.; Fan, K. N. Acta Phys. -Chim. Sin., 2009, 25: 1853. [杨秋芸, 朱渊, 田莉, 裴燕, 乔明华, 范康年. 物理化学学报, 2009, 25: 1853]
8. Jen. P. H.; Hsu, Y. H.; Lin, S. D. Catal. Today, 2007, 123: 133
9. Hubaut, R.; Daaqe, M.; Bonnelle, J. P. Appl. Catal. A: Gen., 1986, 22: 231
10. Noller, H., Lin,W. M. J. Catal., 1984, 85: 25
11. Okumura, M.; Akita, T.; Haruta, M. Catal. Today, 2002, 74: 265
12. Centeno, M. A. ; Hadjiivanov, K.; Venkov, T.; Kilmev, H.; Odriozola, J. A. J. Mol. Catal. A: Chem., 2006, 252: 142
13. Xie, G. Q.; Liu, X. J.; Tao, L. P.; Lu, J. Q.; Luo, M. F.; Li, X. N. Chin. J. Catal., 2009, 30: 543. [谢冠群, 刘西敬, 陶丽萍, 鲁继青,罗孟飞, 李小年. 催化学报, 2009, 30: 543]
14. Gebauer-Henke, E.; Grams, J.; Szubiakiewicz, E.; Farbotko, J.; Touroude, R.; Rynkowski, J. J. Catal., 2007, 250: 195
15. Abid, M.; Paul-Boncour, V.; Touroude, R. Appl. Catal. A: Gen., 2006, 297: 48
16. Ammari, F.; Lamotte, J.; Touroude, R. J. Catal., 2004, 221: 32
17. Campo, B.; Volpe, M.; Ivanova, S.; Touroude, R. J. Catal., 2006, 242: 162
18. Campo, B.; Petit, C.; Volpe, M. A. J. Catal., 2008, 254: 71
19. Guo, M. N.; Guo, C. X.; Jin, L. Y.;Wang, Y. J.; Lu, J. Q.; Luo, M. F. Mater. Lett., 2010, 64: 1638
20. Anderson, J. A.; Daley, R. A.; Christou, S. Y.; Efstathiou, A. M. Appl. Catal. B: Environ., 2006, 64: 89
21. Xie, G. Q.; Liu, X. J.; Lu, J. Q.; Li, X. N.; Luo, M. F. Chin. J. Rare Earth, 2009, 27: 756. [谢冠群, 刘西敬, 鲁继青, 李小年,罗孟飞. 中国稀土学报, 2009, 27: 756]
22. Grass, M. E.; Rioux, R. M.; Somorjai, G. A. Catal. Lett., 2009, 28: 1
23. Triwahyono, S.; Abdul-Jalil, A.; Musthofa, M. Appl. Catal. A: Gen., 2010, 373: 90
24. Ammari, F.; Milome, C.; Touroude, R. J. Catal., 2005, 235: 1
25. Yang, S.W.; Xu, J.; Xin, Q. Chin. J. Mol. Catal., 1998, 12: 152. [杨树武, 徐江, 辛勤. 分子催化, 1998, 12: 152]

[1]	董少明, 普颖慧, 牛一鸣, 张蕾, 王永钊, 张炳森. 间隙碳调控Ni实现1,3-丁二烯高效加氢[J]. 物理化学学报, 2023, 39(11): 2301012 - .
[2]	万宇彤, 方帆, 孙瑞雪, 张杰, 常焜. 金属氧化物半导体用于光热催化CO₂加氢反应：最新进展和展望[J]. 物理化学学报, 2023, 39(11): 2212042 - .
[3]	方洪燕, 江静静, 王定胜, 刘向文, 朱敦如, 李亚栋. 乙炔半加氢催化剂设计[J]. 物理化学学报, 2023, 39(10): 2305030 - .
[4]	曹美芳, 陈博, 阮涛, 欧阳新平, 邱学青. Pt/NbPWO双功能催化剂的制备及氢解碱木质素制备芳香单体[J]. 物理化学学报, 2022, 38(10): 2204037 - .
[5]	郝睿, 关伟翔, 刘菲, 张磊磊, 王爱琴. Lewis酸催化纤维素制乳酸机理研究[J]. 物理化学学报, 2022, 38(10): 2205027 - .
[6]	李少鹏, 杜靖, 张彬, 刘艳贞, 梅清清, 孟庆磊, 董明华, 杜鹃, 赵志娟, 郑黎荣, 韩布兴, 赵美廷, 刘会贞. 利用空间位阻和氢溢流协同作用促进5-羟甲基糠醛选择性加氢制备5-甲基糠醛[J]. 物理化学学报, 2022, 38(10): 2206019 - .
[7]	王艳秋, 钟子欣, 刘唐康, 刘国亮, 洪昕林. Cu@UiO-66衍生的Cu⁺-ZrO₂界面位点用于高效催化CO₂加氢制甲醇[J]. 物理化学学报, 2021, 37(5): 2007089 - .
[8]	华凯敏, 刘晓放, 魏百银, 张书南, 王慧, 孙予罕. 过渡金属催化CO₂/H₂参与的羰基化研究进展[J]. 物理化学学报, 2021, 37(5): 2009098 - .
[9]	李聪明, 陈阔, 王晓月, 薛楠, 杨恒权. 探究Cu/ZnO相互作用对CO₂加氢制甲醇反应性能的影响[J]. 物理化学学报, 2021, 37(5): 2009101 - .
[10]	张赛, 张铭凯, 瞿永泉. 二氧化铈表面构建固体“受阻”Lewis酸碱对用于小分子活化[J]. 物理化学学报, 2020, 36(9): 1911050 - .
[11]	张建, 王亮, 伍芷毅, 王成涛, 苏泽瑞, 肖丰收. 理性设计核-壳Rh@沸石催化材料用于二烯烃选择加氢反应[J]. 物理化学学报, 2020, 36(9): 1912001 - .
[12]	尹雅芝,胡兵,刘国亮,周晓海,洪昕林. 利用ZnO@ZIF-8核壳结构构建高选择性、高稳定性的Pd/ZnO催化剂用于CO₂加氢制甲醇[J]. 物理化学学报, 2019, 35(3): 327 -336 .
[13]	刘艳芳,胡兵,尹雅芝,刘国亮,洪昕林. 无表面活性剂条件下一锅法制备金属/氧化锌复合材料用于催化二氧化碳加氢制甲醇反应[J]. 物理化学学报, 2019, 35(2): 223 -229 .
[14]	高云楠,刘世桢,赵振清,陶亨聪,孙振宇. 二氧化碳多相催化加氢制C₂及以上烃类和醇的研究进展[J]. 物理化学学报, 2018, 34(8): 858 -872 .
[15]	宁红岩,杨其磊,杨晓,李鹰霞,宋兆钰,鲁逸人,张立红,刘源. 碳纤维负载Rh-Mn紧密接触的催化剂及其合成气制乙醇催化性能[J]. 物理化学学报, 2017, 33(9): 1865 -1874 .

ZrO₂负载Pt 催化巴豆醛选择性加氢

Selective Hydrogenation of Crotonaldehyde over ZrO₂-Supported Pt Catalysts

PDF

赞

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

Metrics

推荐阅读 0