三维配位聚合物[Sr(BDC)(H2O)]的合成、结构与热稳定性

doi:10.3866/PKU.WHXB20110908

物理化学学报 >> 2011, Vol. 27 >> Issue (10): 2269-2274.doi: 10.3866/PKU.WHXB20110908

三维配位聚合物[Sr(BDC)(H₂O)]的合成、结构与热稳定性

付颖, 李国宝, 廖复辉, 林建华

北京分子科学国家实验室, 稀土材料化学与应用国家重点实验室, 北京大学化学与分子工程学院, 北京 100871

收稿日期:2011-05-20 修回日期:2011-06-21 发布日期:2011-09-27
通讯作者: 李国宝, 林建华 E-mail:liguobao@pku.edu.cn; jhlin@pku.edu.cn
基金资助:
国家重大基础研究计划(973) (2010CB833103)资助项目

Synthesis, Structure and Thermal Property of a 3D Coordination Polymer [Sr(BDC)(H₂O)]

FU Ying, LI Guo-Bao, LIAO Fu-Hui, LIN Jian-Hua

Beijing National Laboratory for Molecular Sciences BNLMS, State Key Laboratory of Rare Earth Materials Chemistry and Applications, College of Chemistry and Molecular Engineering, Peking University, Beijing 100871, P. R. China

Received:2011-05-20 Revised:2011-06-21 Published:2011-09-27
Contact: LI Guo-Bao, LIN Jian-Hua E-mail:liguobao@pku.edu.cn; jhlin@pku.edu.cn
Supported by:
The project was supported by the National Key Basic Research Program of China (973) (2010CB833103).

摘要/Abstract

摘要： 利用溶剂热法在硝酸锶、1,4-对苯二甲酸(BDC)、N,N'-二甲基甲酰胺(DMF)和水体系中合成了一种新的配位聚合物[Sr(BDC)(H₂O)] (1), 并通过单晶X射线衍射、变温粉末X射线衍射、元素分析、红外光谱和热重-质谱联用对其进行了表征. 该化合物属正交晶系的Pbca 空间群, 晶胞参数为a=1.1854(2) nm, b=0.7122(1) nm,c=2.0031(4) nm. 该化合物具有三维网络结构, 由共面的SrO₈四方反棱柱组成的zigzag 链通过1,4-对苯二甲酸配体连接而成. 热重-质谱联用和变温粉末X射线衍射分析表明它的骨架具有较高的热稳定性.

关键词: 1,4-对苯二甲酸, 锶, 溶剂热合成, 结构, 热稳定性

Abstract: The solvothermal reactions of Sr(NO₃)₂ with 1,4-benzenedicarboxylic acid (BDC) in a mixture of H₂O/N,N'-dimethylformamide (DMF) resulted in a novel coordination polymer, [Sr(BDC) (H₂O)] (1), which was characterized by single crystal and variable temperature powder X-ray diffraction (VTPXRD), elemental analysis, infra-red (IR) spectroscopy, and thermogravimetric-mass spectrometric (TG-MS) analysis. Compound 1 crystallizes in the orthorhombic space group Pbca with a=1.1854(2) nm, b=0.7122 (1) nm, and c=2.0031(4) nm. It is a three-dimensional (3D) framework consisting of zigzag chains that are formed by face-shared SrO₈ square antiprisms and bridging BDC ligands. TG-MS and VTPXRD studies revealed that the framework of compound 1 exhibited a high thermal stability.

Key words: 1,4-Benzenedicarboxylic acid, Strontium, Solvothermal synthesis, Structure, Thermal property

付颖, 李国宝, 廖复辉, 林建华. 三维配位聚合物[Sr(BDC)(H₂O)]的合成、结构与热稳定性[J]. 物理化学学报, 2011, 27(10), 2269-2274. doi: 10.3866/PKU.WHXB20110908

FU Ying, LI Guo-Bao, LIAO Fu-Hui, LIN Jian-Hua. Synthesis, Structure and Thermal Property of a 3D Coordination Polymer [Sr(BDC)(H₂O)][J]. Acta Phys. -Chim. Sin. 2011, 27(10), 2269-2274. doi: 10.3866/PKU.WHXB20110908

链接本文: https://www.whxb.pku.edu.cn/CN/10.3866/PKU.WHXB20110908

https://www.whxb.pku.edu.cn/CN/Y2011/V27/I10/2269

参考文献

(1) Yaghi, O. M.; Li, H. L.; Davis, C.; Richardson, D.; Groy, T. L. Acc. Chem. Res. 1998, 31, 474.

(2) Kitagawa, S.; Kitaura, R.; Noro, S. Angew Chem. Int. Edit. 2004, 43, 2334.

(3) Perry IV, J. J.; Perman J. A.; Zaworotko, M. J. Chem. Soc. Rev. 2009, 38, 1400.

(4) Férey, G. Chem. Soc. Rev. 2008, 37, 191.

(5) Eddaoudi, M.; Kim, J.; Rosi, N.; Vodak, D.;Wachter, J.; O'Keeffe, M.; Yaghi, O. M. Science 2002, 295, 469.

(6) Allendorf, M. D.; Bauer, C. A.; Bhakta, R. K.; Houk, R. J. T. Chem. Soc. Rev. 2009, 38, 1330.

(7) Zhang,W.; Ye, H. Y.; Xiong, R. G. Coord. Chem. Rev. 2009, 253, 2980.

(8) Rocha, J.; Carlos, L. D.; Paz, F. A. A.; Ananias, D. Chem. Soc. Rev. 2011, 40, 926.

(9) Murray, L. J.; Dinc?, M.; Long, J. R. Chem. Soc. Rev. 2009, 38, 1294.

(10) Alkordi, M. H.; Brant, J. A.;Wojtas, L.; Kravtsov, V. C.; Cairns, A. J.; Eddaoudi, M. J. Am. Chem. Soc. 2009, 131, 17753.

(11) Zheng, B.; Dong, H.; Bai, J. F.; Li, Y. Z.; Li, S. H.; Scheer, M. J. Am. Chem. Soc. 2008, 130, 7778.

(12) Sewiegers, G. F.; Malefets, T. J. Chem. Rev. 2000, 100, 3483.

(13) Rao, C. N. R.; Natarajan, S.; Vaidhyanathan, R. Angew. Chem., Int. Edit. 2004, 43, 1466.

(14) Li, H.; Eddaoudi, M.; O?Keeffe M.; Yaghi, O.M. Nature 1999, 402, 276.

(15) Eddaoudi, M.; Moler, D. B.; Li, H. L.; Chen, B. L.; Reineke, T. M.; O'Keeffe, M.; Yaghi, O. M. Acc. Chem. Res. 2001, 34, 319.

(16) Chen, B.; Zhao, X.; Putkham, A.; Hong, K.; Lobkovsky, E. B.; Hurtado, E. J.; Fletcher A. J.; Thomas, K. M. J. Am. Chem.Soc. 2008, 130, 6411.

(17) Kitaura, R.; Seki, K.; Akiyama G.; Kitagawa, S. Angew. Chem., Int. Edit. 2003, 42, 428.

(18) Rieter,W. J.; Taylor, K. M. L.; An, H.; LinW.; Lin,W. J. Am. Chem. Soc. 2006, 128, 9024.

(19) Chen, B. L.; Yang, Y.; Zapata, F.; Qian, G. D.; Luo, Y. S.; Zhang J. H.; Lobkovsky, E. B. Inorg. Chem. 2006, 45, 8882.

(20) Serre, C.; Millange, F.; Marrot, J.; Férey, G. Chem. Mater. 2002, 14, 2409.

(21) Reneike, T. M.; Eddaoudi, M.; O'Keeffe, M.; Yaghi, O. M. Angew. Chem., Int. Edit. 1999, 38, 2590.

(22) Liang, P. C.; Liu, H. K.; Yeh, C. T.; Lin, C. H.; Zima, V. Cryst. Growth Des. 2011, 11, 699.

(23) Williams, C. A.; Blake, A. J.;Wilson, C.; Hubberstey, P.; Schroeder, M. Cryst. Growth Des. 2008, 8, 911.

(24) Davies, R. P.; Less, R. J.; Lickiss, P. D.; White, A. J. P. J. Chem. Soc., Dalton Trans. 2007, 2528.
(25) Groeneman, R. H.; Atwood, J. L. Cryst. Eng. 1999, 2, 241.

(26) Dale, S. H.; Elsegood, M. R. J. Acta Cryst. 2003, E59, m586.
(27) Xiao, D. R.;Wang, E. B.; An, H. Y.; Su, Z. M.; Li, Y. G.; Gao, L.; Sun, C. Y.; Xu, L. Chem. Eur. J. 2005, 11, 6673.

(28) Rood, J. A.; Noll, B. C.; Henderson, K.W. Main Group Chem. 2006, 5, 21.

(29) Dinc?, M.; Long, J. R. J. Am. Chem. Soc. 2005, 127, 9376.

(30) Rood, J. A.; Noll, B. C.; Henderson, K.W. Inorg. Chem. 2006, 45, 5521.

(31) Schlapbach, L.; Züttel, A. Nature 2001, 414, 353.

(32) Classen, H. G.; Nowitski, S.; Schimatschek, H. F. Magnesium Bull. 1991, 132, 39.
(33) Schmidbaur, H.; Mikulick, P.; Müller, G. Chem. Ber. 1990, 123, 1599.

(34) TEXSAN, Single Crystal Structure Analysis Software, MSC, 3200 Research Forest Drive; Molecular Structure Corporation: Woodlands, USA, 1995.
(35) Sheldrick, G. M. SHELXS97, Program for Solution of Crystal Structures, University of Göttingen: Göttingen, Germany, 1997.
(36) Sheldrick, G. M. SHELXL97, Program for Solution of Crystal Structures, University of Göttingen: Göttingen, Germany, 1997.
(37) Sun, Z. H.; Yu,W. T.; Cheng, X. F.;Wang, X. Q.; Zhang, G. H.; Yu, G.; Fan, H. L.; Xu, D. Opt. Mater. 2008, 30, 1001.

(38) He, J. H.; Zhang, Y. T.; Pan, Q. H.; Yu, J. H.; Ding, H.; Xu, R. R. Micropor. Mesopor. Mater. 2006, 90, 45.

(39) Fu, Y.;Wang, X. Y.; Li, G. B.; Liao, F. H.; Xiong, M.; Lin, J. H. Chin. J. Inorg. Chem. 2008, 24, 1224.
[付颖, 王小云, 李国宝, 廖复辉, 熊明, 林建华. 无机化学学报, 2008, 24, 1224.]
(40) Fu, Y.; Su, J.; Yang, S. H.; Li, G. B.; Liao, F. H.; Xiong, M.; Lin, J. H. Inorg. Chim. Acta 2010, 363, 645.

(41) Xie, L. H.; Lin, J. B.; Liu, X. M.; Xue,W.; Zhang,W. X.; Liu, S. X.; Zhang, J. P.; Chen, X. M. Sci. China Chem. 2010, 53, 2144.

(42) Li, P.; Lou, J. Y.; Zhou, Y. M.; Liu, X. F.; Chen, Z. X.;Weng, L. H. Dalton Trans. 2009, 4847.
(43) Yang, S. H.; Li, G. B.; Tian, S. J.; Liao, F. H.; Lin, J. H. J. Solid State Chem. 2005, 178, 3703.

[1]	张城城, 吴之怡, 沈家辉, 何乐, 孙威. 硅纳米结构阵列：光热CO₂催化的新兴平台[J]. 物理化学学报, 2024, 40(1): 2304004 - .
[2]	冀连连, 王现鹏, 张莹莹, 申学礼, 薛娣, 王璐, 王滋, 王文冲, 黄丽珍, 迟力峰. 有机-有机界面效应的原位及非原位研究[J]. 物理化学学报, 2024, 40(1): 2304002 - .
[3]	Faizan Muhammad, 赵国琪, 张天旭, 王啸宇, 贺欣, 张立军. 空位有序双钙钛矿A₂BX₆的弹性和热电性质的第一性原理研究[J]. 物理化学学报, 2024, 40(1): 2303004 - .
[4]	王宁, 李一, 崔乾, 孙晓玥, 胡悦, 罗运军, 杜然. 金属气凝胶：可控制备与应用展望[J]. 物理化学学报, 2023, 39(9): 2212014 -0 .
[5]	罗耀武, 王定胜. 单原子催化剂电子结构调控实现高效多相催化[J]. 物理化学学报, 2023, 39(9): 2212020 -0 .
[6]	高凤雨, 刘恒恒, 姚小龙, Sani Zaharaddeen, 唐晓龙, 罗宁, 易红宏, 赵顺征, 于庆君, 周远松. 球形表面富锰Mn_xCo_3−xO_4−ƞ尖晶石型催化剂选择性催化还原NO_x研究[J]. 物理化学学报, 2023, 39(9): 2212003 -0 .
[7]	陈帅, 余创, 罗启悦, 魏超超, 李莉萍, 李广社, 程时杰, 谢佳. 卤化物固态电解质研究进展[J]. 物理化学学报, 2023, 39(8): 2210032 -0 .
[8]	梁秋菊, 常银霞, 梁朝伟, 祝浩雷, 郭子宾, 刘剑刚. 结晶动力学策略在非富勒烯体系太阳能电池形貌调控领域的应用[J]. 物理化学学报, 2023, 39(7): 2212006 -0 .
[9]	周文杰, 景启航, 李家馨, 陈颖芝, 郝国栋, 王鲁宁. 有机光催化剂用于太阳能水分解：分子水平和聚集体水平改性[J]. 物理化学学报, 2023, 39(5): 2211010 -0 .
[10]	唐甜蜜, 王振旅, 管景奇. 调控单位点M-N-C电催化剂的电子结构提升二氧化碳还原性能[J]. 物理化学学报, 2023, 39(4): 2208033 -0 .
[11]	张婧雯, 马华隆, 马军, 胡梅雪, 李启浩, 陈胜, 宁添姝, 葛创新, 刘晰, 肖丽, 庄林, 张熠霄, 陈立桅. 碱性聚合物电解质膜的表面锥形阵列结构提升燃料电池性能[J]. 物理化学学报, 2023, 39(2): 2111037 -0 .
[12]	齐亚娥, 夏永姚. 电解液调控策略提升水系锌离子电池正极材料电化学性能[J]. 物理化学学报, 2023, 39(2): 2205045 -0 .
[13]	王正慜, 洪庆玲, 王晓慧, 黄昊, 陈煜, 李淑妮. 氮掺杂石墨烯气凝胶锚定RuP纳米粒子用于水合肼氧化辅助产氢[J]. 物理化学学报, 2023, 39(12): 2303028 - .
[14]	郑书逸, 吴佳, 王可, 胡梦晨, 文欢, 尹诗斌. 钴掺杂电子调控Ni-Mo-O多孔纳米棒选择性氧化5-羟甲基糠醛耦合制氢[J]. 物理化学学报, 2023, 39(12): 2301032 - .
[15]	高振飞, 宋清泉, 肖志华, 李兆龙, 李涛, 罗家俊, 王珊珊, 周万立, 李兰英, 于俊荣, 张锦. 亚微米尺寸、高结晶度石墨烯增强间位芳纶纤维力学性能[J]. 物理化学学报, 2023, 39(10): 2307046 - .

三维配位聚合物[Sr(BDC)(H₂O)]的合成、结构与热稳定性

Synthesis, Structure and Thermal Property of a 3D Coordination Polymer [Sr(BDC)(H₂O)]

PDF

赞

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

Metrics

推荐阅读 0