二维/一维BiOBr0.5Cl0.5/WO3 S型异质结助力光催化CO2还原

doi:10.3866/PKU.WHXB202111008

物理化学学报 >> 2022, Vol. 38 >> Issue (7): 2111008.doi: 10.3866/PKU.WHXB202111008

所属专题：异质结光催化材料

二维/一维BiOBr_0.5Cl_0.5/WO₃ S型异质结助力光催化CO₂还原

朱弼辰¹, 洪小洋¹, 唐丽永¹^,*(), 刘芹芹¹, 唐华²^,*()

¹ 江苏大学，材料科学与工程学院，江苏镇江 212013
² 青岛大学，环境科学与工程学院，山东青岛 266071

收稿日期:2021-11-04 录用日期:2021-12-01 发布日期:2021-12-06
通讯作者: 唐丽永,唐华 E-mail:1000003184@mail.ujs.edu.cn;huatang79@163.com
作者简介:第一联系人：
^† Contributed to this work equally.
基金资助:
国家自然科学基金(21975110);国家自然科学基金(21972058);山东省泰山青年学者项目资助

Enhanced Photocatalytic CO₂ Reduction over 2D/1D BiOBr_0.5Cl_0.5/WO₃ S-Scheme Heterostructure

Bichen Zhu¹, Xiaoyang Hong¹, Liyong Tang¹^,*(), Qinqin Liu¹, Hua Tang²^,*()

¹ School of Materials Science and Engineering, Jiangsu University, Zhenjiang 212013, Jiangsu Province, China
² School of Environmental Science and Engineering, Qingdao University, Qingdao 266071, Shandong Province, China

Received:2021-11-04 Accepted:2021-12-01 Published:2021-12-06
Contact: Liyong Tang,Hua Tang E-mail:1000003184@mail.ujs.edu.cn;huatang79@163.com
About author:Email: huatang79@163.com (H.T.)
Email: 1000003184@mail.ujs.edu.cn (L.T.)
Supported by:
the National Natural Science Foundation of China(21975110);the National Natural Science Foundation of China(21972058);Prof. H. Tang gratefully acknowledges financial support from Taishan Youth Scholar Program of Shandong Province

摘要/Abstract

摘要：

S型异质结不但可以提高载流子的分离效率，还可以维持较强的氧化还原能力。因此，构建S型异质是提高光催化二氧化碳还原反应的有效途径。本研究通过静电自组装法构建了具有近红外光响应(> 780 nm)的二维BiOBr_0.5Cl_0.5纳米片和一维WO₃纳米棒S型异质结光催化剂，并用于高效还原二氧化碳。能带位置和界面电子相互作用的综合分析表明：在光催化二氧化碳还原反应过程中，BiOBr_0.5Cl_0.5/WO₃遵循S型电子转移路径；不仅提高了载流子的高效分离，还维持了两相(BiOBr_0.5Cl_0.5和WO₃)较高的氧化还原能力。此外，二维纳米片/一维纳米棒的结构使得半导体之间具备良好的界面接触，有利于载流子的分离，且暴露更多的活性位点，最终提高催化效率。结果显示，BiOBr_0.5Cl_0.5/WO₃异质结催化剂表现出较高的CO₂还原能力和CO选择性，CO的产率高达16.68 μmol∙g^-1∙h^-1，分别是BiOBr_0.5Cl_0.5的1.7倍和WO₃的9.8倍。本工作为构建S型二维/一维异质结光催化剂高效还原二氧化碳提供了新的思路。

关键词: 二维/一维异质结构, BiOBr_0.5Cl_0.5纳米片, WO₃纳米棒, 二氧化碳还原, S型异质结

Abstract:

Catalytic reduction of CO₂ to CO has been considered promising for converting the greenhouse gas into chemical intermediates. Compared to other catalytic methods, photocatalytic CO₂ reduction, which uses solar energy as the energy input, has attracted significant attention because it is a clean and inexhaustible resource. Therefore, using high-performance photocatalysts for effective CO₂ reduction under mild reaction conditions is an active research hotspot. However, several current photocatalysts suffer from low solar energy conversion efficiency due to the extensive charge recombination and few active sites, leading to low CO₂ reduction efficiency. Generally, constructing an S-scheme heterojunction can not only promote charge separation but also help maintain strong redox ability. Therefore, the S-scheme heterojunction is expected to help in achieving high conversion activity and CO₂ reduction efficiency. Here, 2D tetragonal BiOBr_0.5Cl_0.5 nanosheets and hexagonal WO₃ nanorods were prepared using a simple hydrothermal synthesis method, and the 2D/1D BiOBr_0.5Cl_0.5 nanosheets/WO₃ nanorods (BiOBr_0.5Cl_0.5/WO₃) S-scheme heterojunction with near infrared (NIR) light (> 780 nm) response were prepared via the electrostatic self-assembly method for the photocatalytic CO₂ reduction. Following characterization and analysis, including diffuse reflectance spectra (DRS), Mott-Schottky plots, transient photocurrent response, time-resolution photoluminescence spectrum (TRPL), electrochemical impedance spectroscopy (EIS), linear sweep voltammetry (LSV), and electron spin resonance (ESR) measurements, it can be demonstrated that an S-scheme carrier transfer route was formed between the 2D BiOBr_0.5Cl_0.5 nanosheets and 1D WO₃ nanorods. Driven by the internal electric field, which was formed between the two semiconductors, electron migration was boosted, thus inhibiting the recombination of photogenerated carriers, while the stronger redox ability was maintained, thus providing good reduction efficiency over BiOBr_0.5Cl_0.5/WO₃ composite in CO₂ reduction. In addition, the 2D/1D nanosheet/nanorod structure allowed for enhanced interface contact with abundant active sites, which favored charge separation and increased photocatalytic activity. Furthermore, the amount of WO₃ nanorods added during the preparation of the composites was altered, which led to the optimal amount of 5% (w, mass fraction) for the photocatalytic CO₂ reduction. As a result, the BiOBr_0.5Cl_0.5/WO₃ composite exhibited superior photocatalytic reduction performance with a CO yield of 16.68 μmol·g^-1·h^-1 in the presence of any precious metal cocatalyst or sacrificial agent, which was 1.7 and 9.8 times that of pure BiOBr_0.5Cl_0.5 and WO₃, respectively. In addition, the BiOBr_0.5Cl_0.5/WO₃ composite provided continuously increased CO yields with excellent selectivity under full-spectrum light irradiation, suggesting good photocatalytic stability. This work describes a novel idea for the construction of 2D/1D S-scheme heterojunction photocatalysts for efficient CO₂ reduction.

Key words: 2D/1D heterostructure, BiOBr_0.5Cl_0.5 nanosheets, WO₃ nanorods, CO₂ reduction, S-scheme

点击下载补充材料PDF格式文件

朱弼辰, 洪小洋, 唐丽永, 刘芹芹, 唐华. 二维/一维BiOBr_0.5Cl_0.5/WO₃ S型异质结助力光催化CO₂还原[J]. 物理化学学报, 2022, 38(7), 2111008. doi: 10.3866/PKU.WHXB202111008

Bichen Zhu, Xiaoyang Hong, Liyong Tang, Qinqin Liu, Hua Tang. Enhanced Photocatalytic CO₂ Reduction over 2D/1D BiOBr_0.5Cl_0.5/WO₃ S-Scheme Heterostructure[J]. Acta Phys. -Chim. Sin. 2022, 38(7), 2111008. doi: 10.3866/PKU.WHXB202111008

链接本文: https://www.whxb.pku.edu.cn/CN/10.3866/PKU.WHXB202111008

https://www.whxb.pku.edu.cn/CN/Y2022/V38/I7/2111008

图/表 9

Fig 1

Fig 2

Fig 3

Fig 4

Fig 5

Fig 6

Fig 7

Fig 8

参考文献 71

1	Li Y. F. ; Zhang M. ; Zhou L. ; Yang S. J. ; Wu Z. S. ; Ma Y. H. Acta Phys. -Chim. Sin 2021, 37, 2009030.
	李云锋; 张敏; 周亮; 杨思佳; 武占省; 马玉花; 物理化学学报, 2021, 37, 2009030. doi: 10.3866/PKU.WHXB202009030
2	Fei X. G. ; Tan H. Y. ; Cheng B. ; Zhu B. C. ; Zhang L. Y. Acta Phys. -Chim. Sin. 2021, 37, 2010027.
	费新刚; 谭海燕; 程蓓; 朱必成; 张留洋; 物理化学学报, 2021, 37, 2010027. doi: 10.3866/PKU.WHXB202010027
3	Wageh S. ; Al-Ghamdi A. A. ; Liu L. J. Acta Phys. -Chim. Sin 2021, 37, 2010024.
	WagehS.; Al-GhamdiA. A.; 刘丽君; 物理化学学报, 2021, 37, 2010024. doi: 10.3866/PKU.WHXB202010024
4	Wang Z. J. ; Hong J. J. ; Ng S.-F. ; Liu W. ; Huang J. J. ; Chen P. F. ; Ong W.-J. Acta Phys. -Chim. Sin 2021, 37, 2011033.
	王则鉴; 洪佳佳; NgS.-F.; 刘雯; 黄俊杰; 陈鹏飞; OngW.-J.; 物理化学学报, 2021, 37, 2011033. doi: 10.3866/PKU.WHXB202011033
5	Liu Q. Q. ; He X. D. ; Peng J. J. ; Yu X. H. ; Tang H. ; Zhang J. Chin. J. Catal. 2021, 42, 1478. doi: 10.1016/s1872-2067(20)63753-6
6	Wang Z. L. ; Chen Y. F. ; Zhang L. Y. ; Cheng B. ; Yu J. G. ; Fan J. J. J. Mater. Sci. Technol. 2020, 56, 143. doi: 10.1016/j.jmst.2020.02.062
7	Li K. Y. ; Chen J. ; Ao Y. H. ; Wang P. F. Sep. Purif. Technol. 2021, 259, 118177. doi: 10.1016/j.seppur.2020.118177v
8	Mu R. H. ; Ao Y. H. ; Wu T. F. ; Wang C. ; Wang P. F. J. Alloys Compd 2020, 812, 151990. doi: 10.1016/j.jallcom.2019.151990
9	Zhang Y. ; Qin H. N. ; Li B. L. ; Wu B. Chin. J. Struc. Chem. 2021, 40, 595. doi: 10.14102/j.cnki.0254-5861.2011-2989
10	Che H. N. ; Gao X. ; Chen J. ; Hou J. ; Ao Y. H. ; Wang P. F. Angew. Chem. Int. Ed. 2021, 60, 2. doi: 10.1002/anie.202111769
11	Liu X. T. ; Gu S. N. ; Zhao Y. J. ; Zhou G. W. ; Li W. J. J. Mater. Sci. Technol 2020, 56, 45. doi: 10.1016/j.jmst.2020.04.023
12	Zhang J. Y. ; Liao H. G. ; Sun S. G. Chin. J. Struc. Chem 2020, 39, 1019. doi: 10.14102/j.cnki.0254-5861.2011-2553
13	Han S. T. ; Li W. Y. ; Xi H. L. ; Yuan R. S. ; Long J. L. ; Xu C. J. Hazard. Mater. 2021, 423, 127012. doi: 10.1016/j.jhazmat.2021.127012v
14	Li D. S. ; Huang Y. ; Li S. M. ; Wang C. H. ; Li Y. Y. ; Zhang X. T. ; Liu Y. C. Chin. J. Catal. 2021, 41, 154. doi: 10.1016/s1872-2067(19)63475-3
15	Lu Y. ; Fan D. Q. ; Wang Y. D. ; Xu H. L. ; Lu C. H. ; Yang X. F. ACS Nano 2021, 15, 10366. doi: 10.1021/acsnano.1c02578
16	Sayed M. ; Zhu B. C. ; Kuang P. Y. ; Liu X. Y. ; Cheng B. ; Ghamdi A. A. A. ; Wageh S. ; Zhang L. Y. ; Yu J. G. Adv. Sust. Syst. 2021, 2100264. doi: 10.1002/adsu.202100264
17	Wang L. B. ; Cheng B. ; Zhang L. Y. ; Yu J. G. Small 2021, 17, 2103447. doi: 10.1002/smll.202103447
18	Lin H. ; Ma Z. Y. ; Zhao J. W. ; Liu Y. ; Chen J. Q. ; Wang J. H. ; Wu K. F. ; Jia H. P. ; Zhang X. M. ; Cao X. H. ; et al Angew. Chem. Int. Ed. 2021, 60, 1235. doi: 10.1002/anie.202009267
19	Zhang L. ; Xiao W. P. ; Zhang Y. ; Han F. Y. ; Yang X. F. Compos. Commun. 2021, 26, 100792. doi: 10.1016/j.coco.2021.100792
20	Wang J. F. ; Chen J. ; Wang P. F. ; Hou J. ; Wang C. ; Ao Y. H. Appl. Catal. B Environ. 2018, 239, 578. doi: 10.1016/j.apcatb.2018.08.048
21	Zhou S. Q. ; Wang Y. ; Zhou K. ; Ba D. Y. ; Ao Y. H. ; Wang P. F. Chin. Chem. Lett. 2021, 32, 2179. doi: 10.1016/j.cclet.2020.12.002
22	Wageh S. ; Al-Ghamdi A. A. ; Rashida J. ; Li X. ; Zhang P. Chin. J. Catal. 2021, 42, 667. doi: 10.1016/S1872-2067(20)63705-6
23	Fan D. Q. ; Lu Y. ; Zhang H. ; Xu H. L. ; Lu C. H. ; Tang Y. C. ; Yang X. F. Appl. Catal. B Environ. 2021, 295, 120285. doi: 10.1016/j.apcatb.2021.120285
24	Liu L. Z. ; Hu T. P. ; Dai K. ; Zhang J. F. ; Liang C. H. Chin. J. Catal. 2021, 42, 46. doi: 10.1016/s1872-2067(20)63560-4
25	Wang R. ; Shen J. ; Sun K. H. ; Tang H. ; Liu Q. Q. Appl. Surf. Sci. 2019, 493, 1142. doi: 10.1016/j.apsusc.2019.07.121
26	Lu Y. ; Zhang H. ; Fan D. Q. ; Chen Z. P. ; Yang X. F. J. Hazard. Mater. 2021, 423, 127128. doi: 10.1016/j.jhazmat.2021.127128
27	Liu X. ; Zhao Y. X. ; Yang X. F. ; Liu Q. Q. ; Yu X. H. ; Li Y. Y. ; Tang H. ; Zhang T. R. Appl. Catal. B Environ. 2020, 275, 119144. doi: 10.1016/j.apcatb.2020.119144
28	Yan S. W. ; Song H. J. ; Li Y. ; Yang J. ; Jia X. H. ; Wang S. Z. ; Yang X. F. Appl. Catal. B Environ. 2022, 301, 120820. doi: 10.1016/j.apcatb.2021.120820
29	Xie Q. ; He W. N. ; Liu S. W. ; Li C. H. ; Zhang J. F. ; Wong P. K. Chin. J. Catal. 2020, 41, 140. doi: 10.1016/s1872-2067(19)63481-9
30	Wang L. ; Zhu C. L. ; Yin L. S. ; Huang W. Acta Phys. -Chim. Sin. 2020, 36, 1907001.
	王梁; 朱澄鹭; 殷丽莎; 黄维; 物理化学学报, 2020, 36, 1907001. doi: 10.3866/PKU.WHXB201907001
31	Sayed M. ; Xu F. Y. ; Kuang P. Y. ; Low J. X. ; Wang S. Y. ; Zhang L. Y. ; Yu J. G. Nat. Commun. 2021, 12, 4936. doi: 10.1038/s41467-021-26467-6
32	Prasad C. ; Tang H. ; Liu Q. Q. ; Bahadur I. ; Karlapudi S. ; Jiang Y. J. Int. J. Hydrog. Energy 2020, 45, 337. doi: 10.1016/j.ijhydene.2019.07.070
33	Kuang P. Y. ; Wang Y. R. ; Zhu B. C. ; Xia F. J. ; Tung C. W. ; Wu J. S. ; Chen H. M. ; Yu J. G. Adv. Mater. 2021, 33, 2008599. doi: 10.1002/adma.202008599
34	Bie C. B. ; Yu H. G. ; Cheng B. ; Ho W. K. ; Fan J. J. ; Yu J. G. Adv. Mater. 2021, 33, 2003521. doi: 10.1002/adma.202003521
35	Tao J. N. ; Yu X. H. ; Liu Q. Q. ; Liu G. W. ; Tang H. J. Colloid Interface Sci. 2021, 585, 470. doi: 10.1016/j.jcis.2020.10.028
36	Wang R. ; Shen J. ; Zhang W. J. ; Liu Q. Q. ; Zhang M. Y. ; Zulfiqar; ; Tang H. Ceram. Int. 2020, 46, 23. doi: 10.1016/j.ceramint.2019.08.226
37	Wu J. ; Xie Y. ; Ling Y. ; Si J. C. ; Li X. ; Wang J. L. ; Ye H. ; Zhao J. S. ; Li S. Q. ; Zhao Q. D. ; et al Chem. Eng. J. 2020, 400, 125944. doi: 10.1016/j.cej.2020.125944
38	Zhang Z. Y. ; Chi M. F. ; Veith G. M. ; Zhang P. F. ; Lutterman D. A. ; Rosenthal J. ; Overbury S. T. ; Dai S. ; Zhu H. Y. ACS Catal. 2016, 6, 6255. doi: 10.1021/acscatal.6b01297
39	Han L. L. ; Song S. J. ; Liu M. J. ; Yao S. Y. ; Liang Z. X. ; Cheng H. ; Ren Z. H. ; Liu W. ; Lin R. Q. ; Qi G. C. ; et al J. Am. Chem. Soc. 2020, 142, 12563. doi: 10.1021/jacs.9b12111
40	Jia X. M. ; Han Q. F. ; Wang X. ; Zhu J. W. Photochem. Photobiol. 2018, 94, 942. doi: 10.1111/php.12943
41	Wilczewska P. ; Bielicka-Giełdoń A. ; Borzyszkowska A. F. ; Ryl J. ; Klimczuk T. ; Siedlecka E. M. J. Photochem. Photobiol. A Chem. 2019, 382, 111932. doi: 10.1016/j.jphotochem.2019.111932
42	Liu Y. Y. ; Son W. J. ; Lu J. B. ; Huang B. B. ; Dai Y. ; Whangbo M. H. Chem. Eur. J. 2011, 17, 9342. doi: 10.1002/chem.201100952
43	Bao Y. P. ; Lee W. J. ; Guan C. T. ; Liang Y. N. ; Lim T. T. ; Hu X. J. Mater. Chem. B 2021, 9, 3079. doi: 10.1016/j.seppur.2021.119203
44	Sanaa S. K. ; Vladimir U. ; Yulia K. ; Ella M. ; Inna P. ; Yoel S. Catal. Commun. 2011, 12, 1136. doi: 10.1016/j.catcom.2011.03.014
45	Zhang B. ; Ji G. B. ; Liu Y. S. ; Gondal M. A. ; Chang X. F. Catal. Commun. 2013, 36, 25. doi: 10.1016/j.catcom.2013.02.021
46	Li Y. ; Zheng X. N. ; Yang J. ; Zhao Z. H. ; Cui S. H. J. Taiwan Inst. Chem. E 2021, 119, 213. doi: 10.1016/j.jtice.2021.02.014
47	Zhang M. ; Cheng J. ; Xuan X. X. ; Zhou J. H. ; Cen K. F. Chem. Eur. J. 2017, 322, 22. doi: 10.1016/j.cej.2017.03.126
48	Pan Y. X. ; You Y. ; Xin S. ; Li Y. T. ; Fu G. T. ; Cui Z. M. ; Men Y. L. ; Cao F. F. ; Yu S. H. ; Goodenough J. B. J. Am. Chem. Soc. 2017, 139, 4123. doi: 10.1021/jacs.7b00266
49	Gu S. S. ; Marianov A. N. ; Xu H. M. ; Jiang Y. J. J. Mater. Sci. Technol. 2021, 80, 20. doi: 10.1016/j.jmst.2020.09.053
50	Tang H. ; Xia Z. H. ; Chen R. ; Liu Q. Q. ; Zhou T. H. Chem. Asian J. 2020, 15, 3456. doi: 10.1002/asia.202000912
51	Hong X. Y. ; Yu X. H. ; Wang L. L. ; Liu Q. Q. ; Sun J. F. ; Tang H. Inorg. Chem. 2021, 60, 12506. doi: 10.1021/acs.inorgchem.1c01716
52	Tahir M. ; Tahir B. J. Mater. Sci. Technol. 2022, 106, 195. doi: 10.1016/j.jmst.2021.08.019
53	Liu D. N. ; Chen D. Y. ; Li N. J. ; Xu Q. F. ; Li H. ; He J. H. ; Lu M. J. Angew. Chem. Int. Ed. 2021, 133, 1521. doi: 10.1002/ange.201914949
54	Dehkordi A. B. ; Ziarati A. ; Ghasemi J. B. ; Badiei A. Sol. Energy 2020, 205, 465. doi: 10.1016/j.solener.2020.05.071
55	Xu Q. L. ; Zhang L. Y. ; Cheng B. ; Fan J. J. ; Yu J. G. Chem 2020, 6, 1543. doi: 10.1016/j.chempr.2020.06.010
56	Liu Q. Q. ; He X. D. ; Tao J. N. ; Tang H. ; Liu Z. Q. ChemNanoMat. 2021, 7, 44. doi: 10.1002/cnma.202000536
57	Peng J. J. ; Shen J. ; Yu X. H. ; Tang H. ; Zulfiqar ; Liu Q. Q. Chin. J. Catal. 2021, 42, 87. doi: 10.1016/S1872-2067(20)63595-1
58	Xu F. Y. ; Meng K. ; Cheng B. ; Wang S. Y. ; Xu J. S. ; Yu J. G. Nat. Commun. 2020, 11, 4613. doi: 10.1038/s41467-020-18350-7
59	Girish K. S. ; Koteswara R. K. S. R. Appl. Surf. Sci. 2015, 355, 939. doi: 10.1016/j.apsusc.2015.07.003
60	Wang L. L. ; Tang G. G. ; Liu S. ; Dong H. L. ; Liu Q. Q. ; Sun J. F. ; Tang H. Chem. Eng. J. 2022, 428, 131338. doi: 10.1016/j.cej.2021.131338
61	Xia Y. ; Tian Z. H. ; Heil T. ; Meng A. ; Cheng B. ; Cao S. W. ; Yu J. G. ; Antonietti M. Joule 2019, 3, 2792. doi: 10.1016/j.joule.2019.08.011
62	Ye L. ; Wen Z. H. Int. J. Hydrog. Energy 2019, 44, 3751. doi: 10.1016/j.ijhydene.2018.12.093
63	Gao M. C. ; Yang J. X. ; Sun T. ; Zhang Z. Z. ; Zhang D. F. ; Huang H. J. ; Lin H. X. ; Fang Y. ; Wang X. X. Appl. Catal. B Environ. 2019, 243, 734. doi: 10.1016/j.apcatb.2018.11.020
64	Tang M. L. ; Ao Y. H. ; Wang P. F. ; Wang C. J. Hazard. Mater. 2020, 387, 121713. doi: 10.1016/j.jhazmat.2019.121713
65	Wang S. L. ; Zhu Y. ; Luo X. ; Huang Y. ; Chai J. W. ; Wong T. I. ; Xu G. Q. Adv. Funct. Mater. 2018, 28, 1705357. doi: 10.1002/adfm.201705357
66	Fu J. W. ; Xu Q. L. ; Low J. X. ; Jiang C. J. ; Yu J. G. Appl. Catal. B Environ. 2019, 243, 556. doi: 10.1016/j.apcatb.2018.11.011
67	Liu Q. Q. ; Huang J. X. ; Tang H. ; Yu X. H. ; Shen J. J. Mater. Sci. Technol. 2020, 56, 196. doi: 10.1016/j.jmst.2020.04.026
68	Manthiram K. ; Alivisatos A. P. J. Am. Chem. Soc. 2012, 134, 3995. doi: 10.1021/ja211363w
69	An Z. ; Zhou T. H. Chin. J. Struc. Chem 2019, 38, 644. doi: 10.14102/j.cnki.0254-5861.2011-2112
70	Ma B. R. ; Xin S. S. ; Xin Y. J. ; Ma X. M. ; Zhang C. L. ; Gao M. C. ; Ma F. ; Ma Y. M. Sep. Purif. Technol. 2021, 268, 1383. doi: 10.1016/j.seppur.2021.118699
71	Sun H. G. ; Tian Z. X. ; Zhou G. L. ; Zhang J. M. ; Li P. Appl. Surf. Sci. 2019, 469, 125. doi: 10.1016/j.apsusc.2018.11.006

[1]	陈轼逸, 付家龙, 裘建平, 常国菊, 郝仕油. 废弃医用口罩衍生的碳量子点增强BiOBr/g-C₃N₄ S型异质结光催化降解聚对苯二甲酸乙二醇酯(PET)[J]. 物理化学学报, 2026, 42(1): 100135 - .
[2]	葛成艳, 胡佳伟, 刘星雨, 宋玉玺, 刘超, 邹志刚. 自集成黑色NiO团簇与ZnIn₂S₄微球实现S型电子转移机制下光热辅助制氢[J]. 物理化学学报, 2026, 42(1): 100154 - .
[3]	洪佳楠, 许辰宇, 刘烟, 黎昌棋, 王梦琳, 张彦威. 通过边缘活性位点调控解析光热催化中析氢与二氧化碳还原的界面竞争[J]. 物理化学学报, 2025, 41(9): 100099 - .
[4]	韦梦兰, 欧晓霞, 王艺濛, 张梦圆, 滕飞, 王凯旋. S型异质结g-C₃N₄/Bi₂WO₆高效降解左氧氟沙星：性能、机理及降解路径[J]. 物理化学学报, 2025, 41(9): 100105 - .
[5]	王文龙, 郝文韬, 何浪, 乔佳, 李宁, 陈朝秋, 覃勇. 碳量子点/TiO₂ S型异质结的能带和吸附工程促进光催化CO₂甲烷化[J]. 物理化学学报, 2025, 41(9): 100116 - .
[6]	蔡家杰, 程畅, 刘博文, 张建军, 姜传佳, 程蓓. CdS/DBTSO-BDTO S型异质结光催化制氢及其电荷转移动力学[J]. 物理化学学报, 2025, 41(8): 100084 - .
[7]	孟凡鹏, 赵飞, 林靖恺, 赵金生, 张华阳, 王少彬. 优化氮化碳纳米片/球形共轭聚合物S型异质结界面电场以促进析氢反应[J]. 物理化学学报, 2025, 41(8): 100095 - .
[8]	王伟康, 吴亚栋, 张建军, 孟凯, 李金河, 王乐乐, 刘芹芹. 三聚氰胺泡沫支撑的S型硫铟锌镉/硫掺杂氮化碳异质结的绿色H₂O₂合成：协同界面电荷转移调控与局域光热效应[J]. 物理化学学报, 2025, 41(8): 100093 - .
[9]	苗鑫宇, 杨浩, 何杰, 王晶, 靳治良. 调整Keggin型多金属氧酸盐电子结构构建S型异质结用于光催化析氢[J]. 物理化学学报, 2025, 41(6): 100051 - .
[10]	杨祎, 周欣, 谷苗莉, 程蓓, 吴珍, 张建军. S型ZnO/CdIn₂S₄光催化剂制备H₂O₂偶联苄胺氧化的超快电子转移飞秒吸收光谱研究[J]. 物理化学学报, 2025, 41(6): 100064 - .
[11]	李朋, 崔元映, 王中辽, DawsonGraham, 邵春风, 代凯. CeO₂/Bi₁₉Br₃S₂₇ S型异质结的高效界面电荷转移用于增强光催化CO₂还原[J]. 物理化学学报, 2025, 41(6): 100065 - .
[12]	吴金往, 谢琦靖, 张成亮, 史海峰. 自旋极化增强ZnFe_1.2Co_0.8O₄/BiVO₄ S型异质结光催化性能降解四环素[J]. 物理化学学报, 2025, 41(5): 100050 - .
[13]	陈润华, 吴琼, 罗婧宸, 祖小龙, 朱姗, 孙永福. 缺陷态二维超薄材料用于光/电催化CO₂还原的基础与展望[J]. 物理化学学报, 2025, 41(3): 100019 - .
[14]	马德运, 梁凤兰, 薛清泉, 刘艳萍, 庄春强, 李世杰. 界面工程与氧空位协同策略促进Cd_0.5Zn_0.5S/BiOBr S型异质结高效光催化去除抗生素[J]. 物理化学学报, 2025, 41(12): 100190 - .
[15]	雷嘉莉, 王娟, 张文慧, 王国宏, 梁子辉, 李金懋. TiO₂/CdIn₂S₄ S型异质结光催化剂促进光催化产氢耦合香兰醇氧化[J]. 物理化学学报, 2025, 41(12): 100174 - .

二维/一维BiOBr_0.5Cl_0.5/WO₃ S型异质结助力光催化CO₂还原

Enhanced Photocatalytic CO₂ Reduction over 2D/1D BiOBr_0.5Cl_0.5/WO₃ S-Scheme Heterostructure

RichHTML

PDF

赞

可视化

摘要/Abstract

支持信息

引用本文

使用本文

图/表 9

参考文献 71

相关文章 15

Metrics

推荐阅读 0