Interaction of Binary Pluronic Block Molecules

Zhao Jian-Xi, Chen Xiao-Dong, Jiang Lin-Qin   

  1. Department of Chemistry,Fuzhou University,Fuzhou 350002
  • Received:2000-03-27 Revised:2000-06-28 Published:2000-12-15
  • Contact: Zhao Jian-Xi E-mail:jxzhao.colloid@fzu.edu.cn

PDF

3340

赞

摘要：

用I2探针增溶分光光度法考察二元Pluronic两亲嵌段共聚物在水溶液中的胶束化行为，实验结果表明，对于分子PPO嵌段长度相近的P94/L92和F108/L92二元混合体系，这些分子在全部浓度比例范围内都发生相互作用，生成了混合胶束，由于这些分子的PEO嵌段长度不等，随着具有较短PEO嵌段的L92分子加入，P94/L92和F108/L92混合胶束外壳的EO基团数减少导致水化度降低。对于分子PPO嵌段长度不等的P94/L64二元混合体系，当溶液体当中L64的质量分数wL64<0.4时，由于P94/L64混合预胶束的形成，使P94分子在较高浓度时才生成单组分胶束，当wL64>0.4后，溶液中生成了P94/L64混合胶束，温度升高促进了胶束化行为。

关键词: Pluronic嵌段共聚物, 相互作用, 混合胶束

Abstract:

Water-soluble poly(ethylene oxide)-block-poly(propylnen oxide)-block-poly-(ethylene oxide)(PEO-PPO-PEO) copolymers are nonionic macromolecular surface-active agents,available commercially as Pluronics.Recently,the micellization of these copolymers has been focused because of a strong interest in Pluronic micelles as drug-microcarriers in therapeutic creams and ointments.However, micellization of Pluroniccopolymers is very complex compared with those conventional surfactants.Due to this reason,interaction of binary Pluronic has been hardly studied up to now.This paper reported the micellization of binary Pluronic moleculesP94/L92 and F108/L92 which have similar length in PPO blocks and different length in PEO blocks,as well as P94/L64 which have different length in PPO blocks.I2 was used as a probe to determine the criticalmicelle concentration(cmc) of the mixtures in aqueous solutions.This method has been confirmed to be very sensitive to the determination of cmcm.The results showed that P94/L92 or F108/L92 binary components interact each other to form mixed micelles over the range of all concentration ratio.With addition of L92 molecules with a shorter PEO block,hydration of P94/L92 orF108/L92 mixed micelles was weakened duo to a decrease in the number of EO groups within the shell.When the mass fraction of L64,wL64<0.4,the micellization in P94/L64 mixtures was hindered and the cmc of P94 was enhanced to a higher value due to the formation of P94/L64 mixed pre-micelles in aqueous solution.Theses mixed pre-micelles have weaker hydrophobicity compared with those pre-micelles formed with individual P94 molecules.Over the range of wL64<0.4,therefore.there was only the micelles formed with individual P94 molecules when the micellization took place.With further increasing wL64,the mixed micelles of P94/L64 started to be formed and the critical point of mixed micelle formation was determined at wL64=0.4.

Key words: Pluronic block copolymer, Interaction, Mixed micelie